In-situ Synthesis of SnO2 Quantum Dots/ZnS Nanosheets Heterojunction as a Visible-light-driven Photocatalyst for Degradation of Rhodamine B,Potassium Dichromate and Tetracycline
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2020年第4期
论文作者：张琛旭 吴湘锋 JIA Yunning CHANG Tianlong LIU Zhifeng FU Yunxuan LIU Xutao 王惠 SHI Yimai ZUO Yuqian
文章页码：719 - 725
摘 要：The SnO2 quantum dots （SnO2QDs）/ZnS nanosheets （ZnSNs） heterojunction was fabricated via an in-situ synthetic method at room temperature.Rhodamine B,potassium dichromate,and tetracycline were used to discuss the photocatalytic activities of the as-prepared samples under the visible light illumination.The photocatalytic mechanism of the as-prepared samples was also proposed.The experimental results indicate that the degradation efficiency of the as-prepared SnO2QDs/ZnSNs heterojunction first increases and then decreases with increasing the usage of ZnSNs.When the mass ratio of SnO2QDs to ZnSNs is 1:2 in 180 min,the as-prepared samples have the highest degradation efficiency of 89.1% for rhodamine B,97.7% for potassium dichromate,and 83.8% for tetracycline,which are much higher than 51.7%,26.8%,and 0.9% of pure SnO2QDs as well as 37.9%,87.1%,and 19.1% of pure ZnSNs,respectively.After it is repeatedly degraded for 3 times,it possesses the degradation efficiency of 62.5% for rhodamine B,which increases by 200.5% in comparison with 20.8% of the pure SnO2QDs.Moreover,the enhanced photocatalytic performances of the as-prepared hybrids are attributed to the formation of heterojunction between the SnO2QDs and ZnSNs.In addition,hydroxyl radicals and superoxide anion radicals play major roles during the photocatalytic degradation process,while holes play a minor role.
张琛旭1，吴湘锋1，JIA Yunning1，CHANG Tianlong1，LIU Zhifeng2，FU Yunxuan1，LIU Xutao1，王惠1，SHI Yimai1，ZUO Yuqian1
1. School of Materials Science and Engineering, Hebei Provincial Key Laboratory of Traffic Engineering Materials, Shijiazhuang Tiedao University2. Tianjin Key Laboratory of Building Green Functional Materials, Tianjin Chengjian University
摘 要：The SnO2 quantum dots （SnO2QDs）/ZnS nanosheets （ZnSNs） heterojunction was fabricated via an in-situ synthetic method at room temperature.Rhodamine B,potassium dichromate,and tetracycline were used to discuss the photocatalytic activities of the as-prepared samples under the visible light illumination.The photocatalytic mechanism of the as-prepared samples was also proposed.The experimental results indicate that the degradation efficiency of the as-prepared SnO2QDs/ZnSNs heterojunction first increases and then decreases with increasing the usage of ZnSNs.When the mass ratio of SnO2QDs to ZnSNs is 1:2 in 180 min,the as-prepared samples have the highest degradation efficiency of 89.1% for rhodamine B,97.7% for potassium dichromate,and 83.8% for tetracycline,which are much higher than 51.7%,26.8%,and 0.9% of pure SnO2QDs as well as 37.9%,87.1%,and 19.1% of pure ZnSNs,respectively.After it is repeatedly degraded for 3 times,it possesses the degradation efficiency of 62.5% for rhodamine B,which increases by 200.5% in comparison with 20.8% of the pure SnO2QDs.Moreover,the enhanced photocatalytic performances of the as-prepared hybrids are attributed to the formation of heterojunction between the SnO2QDs and ZnSNs.In addition,hydroxyl radicals and superoxide anion radicals play major roles during the photocatalytic degradation process,while holes play a minor role.
关键词：