Influence of Microstructural Evolution on the Hot Deformation Behavior of an Fe–Mn–Al Duplex Lightweight Steel
来源期刊：Acta Metallurgica Sinica2018年第4期
论文作者：Li-Xiong Xu Hui-Bin Wu Xin-Tian Wang
文章页码：389 - 400
摘 要：The hot deformation behavior of Fe–26 Mn–6.2 Al–0.05 C steel was studied by experimental hot compression tests in the temperature range of 800–1050 °C and strain rate range of 0.01–30 s21 on a Gleeble-3500 thermal simulation machine. The microstructural evolution during the corresponding thermal process was observed in situ by confocal laser scanning microscopy. Electron backscattered diffraction and transmission electron microscopy analyses were carried out to observe the microstructural morphology before and after the hot deformation. Furthermore, interrupted compression tests were conducted to correlate the microstructural characteristics and softening mechanisms at different deformation stages.The results showed that hot compression tests of this steel were all carried out on a duplex matrix composed of austenite and d-ferrite. As the deformation temperature increased from 800 to 1050 °C, the volume fraction of austenite decreased from 70.9% to 44.0%, while that of d-ferrite increased from 29.1% to 56.0%. Due to the different stress exponents（n） and apparent activation energies（Q）, the generated strain was mostly accommodated by d-ferrite at the commencement of deformation, and then both dynamic recovery and dynamic recrystallization occurred earlier in d-ferrite than in austenite.This interaction of strain partitioning and unsynchronized softening behavior caused an abnormal hot deformation behavior profile in the Fe–Mn–Al duplex steel, such as yield-like behavior, peculiar work-hardening behavior, and dynamic softening behavior, which are influenced by not only temperature and strain rate but also by microstructural evolution.
Li-Xiong Xu1，Hui-Bin Wu1,2，Xin-Tian Wang1
1. Collaborative Innovation Center of Steel Technology,University of Science and Technology Beijing2. National Engineering Research Center of Advanced Rolling,University of Science and Technology Beijing
摘 要：The hot deformation behavior of Fe–26 Mn–6.2 Al–0.05 C steel was studied by experimental hot compression tests in the temperature range of 800–1050 °C and strain rate range of 0.01–30 s21 on a Gleeble-3500 thermal simulation machine. The microstructural evolution during the corresponding thermal process was observed in situ by confocal laser scanning microscopy. Electron backscattered diffraction and transmission electron microscopy analyses were carried out to observe the microstructural morphology before and after the hot deformation. Furthermore, interrupted compression tests were conducted to correlate the microstructural characteristics and softening mechanisms at different deformation stages.The results showed that hot compression tests of this steel were all carried out on a duplex matrix composed of austenite and d-ferrite. As the deformation temperature increased from 800 to 1050 °C, the volume fraction of austenite decreased from 70.9% to 44.0%, while that of d-ferrite increased from 29.1% to 56.0%. Due to the different stress exponents（n） and apparent activation energies（Q）, the generated strain was mostly accommodated by d-ferrite at the commencement of deformation, and then both dynamic recovery and dynamic recrystallization occurred earlier in d-ferrite than in austenite.This interaction of strain partitioning and unsynchronized softening behavior caused an abnormal hot deformation behavior profile in the Fe–Mn–Al duplex steel, such as yield-like behavior, peculiar work-hardening behavior, and dynamic softening behavior, which are influenced by not only temperature and strain rate but also by microstructural evolution.
关键词：