Characterization and in-situ formation mechanism of tungsten carbide reinforced Fe-based alloy coating by plasma cladding
来源期刊：International Journal of Minerals Metallurgy and Materials2018年第4期
论文作者：Mi-qi Wang Ze-hua Zhou Lin-tao Wu Ying Ding Ze-hua Wang
文章页码：439 - 443
摘 要：The precursor carbonization method was first applied to prepare W–C compound powder to perform the in-situ synthesis of the WC phase in a Fe-based alloy coating. The in-situ formation mechanism during the cladding process is discussed in detail. The results reveal that fine and obtuse WC particles were successfully generated and distributed in Fe-based alloy coating via Fe/W–C compound powders. The WC particles were either surrounded by or were semi-enclosed in blocky M7C3 carbides. Moreover, net-like structures were confirmed as mixtures of M23C6 and α-Fe; these structures were transformed from M7C3. The coarse herringbone M6C carbides did not only derive from the decomposition of M7C3 but also partly originated from the chemical reaction at the α-Fe/M23C6 interface. During the cladding process, the phase evolution of the precipitated carbides was WC → M7C3 → M23C6 + M6C.
Mi-qi Wang，Ze-hua Zhou，Lin-tao Wu，Ying Ding，Ze-hua Wang
College of mechanics and materials, Hohai University
摘 要：The precursor carbonization method was first applied to prepare W–C compound powder to perform the in-situ synthesis of the WC phase in a Fe-based alloy coating. The in-situ formation mechanism during the cladding process is discussed in detail. The results reveal that fine and obtuse WC particles were successfully generated and distributed in Fe-based alloy coating via Fe/W–C compound powders. The WC particles were either surrounded by or were semi-enclosed in blocky M7C3 carbides. Moreover, net-like structures were confirmed as mixtures of M23C6 and α-Fe; these structures were transformed from M7C3. The coarse herringbone M6C carbides did not only derive from the decomposition of M7C3 but also partly originated from the chemical reaction at the α-Fe/M23C6 interface. During the cladding process, the phase evolution of the precipitated carbides was WC → M7C3 → M23C6 + M6C.
关键词：