Effect of Solidification Condition and Carbon Content on the Morphology of MC Carbide in Directionally Solidified Nickel-base Superalloys
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2014年第12期
论文作者：X.W.Li L.Wang J.S.Dong L.H.Lou
文章页码：1296 - 1300
摘 要：Evolution of the morphology of MC carbides with the change of cooling rate and carbon content in two kinds of nickel-base superalloys, K417 G and DD33, has been investigated. The morphology of MC carbides evolves from faceted to script-like with increasing cooling rate. Varying the carbon content from 40X10-6 to 320X10-6, the morphology of carbides changes from blocky, rod-like into script-like. Scanning electron microscopy observation of deep-etched samples indicates that these carbides evolve from octahedral to dendritic and then into welldeveloped dendrites accordingly in a three-dimensional manner. The morphology evolution is discussed from the viewpoint of the preferential growth orientation of fcc crystals and the carbide growth rate during directional solidification.
X.W.Li，L.Wang，J.S.Dong，L.H.Lou
Superalloys Division, Institute of Metal Research, Chinese Academy of Sciences
摘 要：Evolution of the morphology of MC carbides with the change of cooling rate and carbon content in two kinds of nickel-base superalloys, K417 G and DD33, has been investigated. The morphology of MC carbides evolves from faceted to script-like with increasing cooling rate. Varying the carbon content from 40X10-6 to 320X10-6, the morphology of carbides changes from blocky, rod-like into script-like. Scanning electron microscopy observation of deep-etched samples indicates that these carbides evolve from octahedral to dendritic and then into welldeveloped dendrites accordingly in a three-dimensional manner. The morphology evolution is discussed from the viewpoint of the preferential growth orientation of fcc crystals and the carbide growth rate during directional solidification.
关键词：