Modification of NiCoCrAlY with Pt: Part Ⅰ. Effect of Pt depositing location and cyclic oxidation performance
来源期刊:JOURNAL OF MATERIALS SCIENCE TECHNOLOG2019年第3期
论文作者:Yingfei Yang Hongrui Yao Zebin Bao Pan Ren Wei Li
文章页码:341 - 349
摘 要:Pt layers of 5 μm in thickness were electroplated before or after depositing NiCoCrAlY coating by arc ion plating(AIP) aiming for identifying the effect of Pt enriching position on microstructure and cyclic oxidation behavior of Pt modified NiCoCrAlY coatings. Al-rich zones formed at the same position of Ptrich zones for both modified coatings due to uphill diffusion of Al driven by Pt. Cyclic oxidation tests at 1000 and 1100?C indicated that oxidation resistance of NiCoCrAlY was improved by Pt modification via different mechanisms: at surface, Pt-rich zone promoted selective oxidation of Al to form α-Al2O3,whilst at coating/substrate interface Pt-rich zone acted as effective diffusion barrier for titanium. Roles of Pt played in enhancing the oxidation performance of various Pt-modified NiCoCrAlY coating were investigated.
Yingfei Yang1,2,Hongrui Yao1,Zebin Bao2,Pan Ren1,Wei Li1
1. Institute of Advanced Wear & Corrosion Resistant and Functional Material, Jinan University2. Corrosion and Protection Division, Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences
摘 要:Pt layers of 5 μm in thickness were electroplated before or after depositing NiCoCrAlY coating by arc ion plating(AIP) aiming for identifying the effect of Pt enriching position on microstructure and cyclic oxidation behavior of Pt modified NiCoCrAlY coatings. Al-rich zones formed at the same position of Ptrich zones for both modified coatings due to uphill diffusion of Al driven by Pt. Cyclic oxidation tests at 1000 and 1100?C indicated that oxidation resistance of NiCoCrAlY was improved by Pt modification via different mechanisms: at surface, Pt-rich zone promoted selective oxidation of Al to form α-Al2O3,whilst at coating/substrate interface Pt-rich zone acted as effective diffusion barrier for titanium. Roles of Pt played in enhancing the oxidation performance of various Pt-modified NiCoCrAlY coating were investigated.