Effect of Rapid Quenching on Electrochemical Properties of AB5 and AB3.5-Type Hydrogen Storage Alloys
来源期刊：Journal of Rare Earths2007年第S2期
论文作者：李平 郑雪萍 安富强 Islam S.Humail 曲选辉
文章页码：135 - 138
摘 要：Effect of rapid quenching on the electrochemical properties of AB5 and AB3.5-type hydrogen storage alloys was studied. The results indicated that the discharge capacities of the rapid quenching MmNi3.55Co0.75Mn0.4Al0.3 alloys decrease under 25 and -35 ℃ with the increase of the quenching rate. Comparatively, the decrease extent of the quenching alloys at -35 ℃ is lower than that at 25 ℃. The result on the study of the cycle life indicated that the quenching process was favorable to improve the cycle stabilities of the MmNi3.55Co0.75-Mn0.4Al0.3 alloys under 25 and -35 ℃. Whereas, the effect of the quenching process on the La0.7Mg0.3（Ni0.85Co0.15）3.5 alloy was different at 25 ℃ from at -35 ℃. Under 25 ℃, the cycle life of the alloy was obviously improved by the quenching process, however, the quenching process did not improve but decreased slightly the cycle life at -35 ℃.
李平，郑雪萍，安富强，Islam S.Humail，曲选辉
摘 要：Effect of rapid quenching on the electrochemical properties of AB5 and AB3.5-type hydrogen storage alloys was studied. The results indicated that the discharge capacities of the rapid quenching MmNi3.55Co0.75Mn0.4Al0.3 alloys decrease under 25 and -35 ℃ with the increase of the quenching rate. Comparatively, the decrease extent of the quenching alloys at -35 ℃ is lower than that at 25 ℃. The result on the study of the cycle life indicated that the quenching process was favorable to improve the cycle stabilities of the MmNi3.55Co0.75-Mn0.4Al0.3 alloys under 25 and -35 ℃. Whereas, the effect of the quenching process on the La0.7Mg0.3（Ni0.85Co0.15）3.5 alloy was different at 25 ℃ from at -35 ℃. Under 25 ℃, the cycle life of the alloy was obviously improved by the quenching process, however, the quenching process did not improve but decreased slightly the cycle life at -35 ℃.
关键词：