Preparation of Cordierite Ceramic Using Mixtures of Ce4+-Modified Amorphous Powder and Oxide Powders

来源期刊:Journal of Rare Earths2006年第S1期

论文作者:史志铭

文章页码:263 - 265

摘    要:<正>The cordierite ceramic with a high strength and a low thermal expansion coefficient was prepared by using mixtures of Ce4 +-modified cordierite amorphous powder and oxide powders of MgO, Al2O3 and SiO2 as starting materials. The transformation procedure of the powders was analyzed by XRD method and the surface morphology of ceramics was examined by SEM method. The flexural strength was measured in a mechanical property testing machine using the Three-Point-Bending sample. Experimental results show that the ceramic added with 10%(mass fraction) of Ce4+-modified amorphous powder is composed ofα-cordierite and small amount of CeO2 particles, and has a porosity of 15% (volume fraction) and a flexural strength of 32.6 MPa when sintered at 1350℃for 3 h. It is suggested that this low-cost process is suitable for preparing the components such as supports of vehicle exhaust converters and diesel particulate trappers.

详情信息展示

Preparation of Cordierite Ceramic Using Mixtures of Ce4+-Modified Amorphous Powder and Oxide Powders

史志铭

摘 要:<正>The cordierite ceramic with a high strength and a low thermal expansion coefficient was prepared by using mixtures of Ce4 +-modified cordierite amorphous powder and oxide powders of MgO, Al2O3 and SiO2 as starting materials. The transformation procedure of the powders was analyzed by XRD method and the surface morphology of ceramics was examined by SEM method. The flexural strength was measured in a mechanical property testing machine using the Three-Point-Bending sample. Experimental results show that the ceramic added with 10%(mass fraction) of Ce4+-modified amorphous powder is composed ofα-cordierite and small amount of CeO2 particles, and has a porosity of 15% (volume fraction) and a flexural strength of 32.6 MPa when sintered at 1350℃for 3 h. It is suggested that this low-cost process is suitable for preparing the components such as supports of vehicle exhaust converters and diesel particulate trappers.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号