Effect of Monolithic LaB6 on the Ablation Resistance of ZrC/SiC Coating Prepared by Supersonic Plasma Spraying for C/C Composites
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2016年第10期
论文作者：Yujun Jia Hejun Li Lu Li Qiangang Fu Kezhi Li
文章页码：996 - 1002
摘 要：Ablation resistance of monolithic LaB6-doped ZrC coating for SiC-coated carbon/carbon composites by supersonic atmospheric plasma spray was investigated under an oxyacetylene torch with a heat flux of 4.18 MW/m2. Result shows that ZrC coating with 10 vol.% LaB6 has a good ablation resistance compared with pure ZrC, ZrC with 20 vol.% LaB6 and SiC-doped ZrC coating. After ablation for 15 s, the weight is increased by 1.12 mg/s. The good ablation resistance is ascribed to the formation of a stabilized scale which consists of protective La2Zr2O7-containing molten phase and ZrO2 particles keeping the integrity of the coating.
Yujun Jia，Hejun Li，Lu Li，Qiangang Fu，Kezhi Li
State Key Laboratory of Solidification Processing, Northwestern Polytechnical University
摘 要：Ablation resistance of monolithic LaB6-doped ZrC coating for SiC-coated carbon/carbon composites by supersonic atmospheric plasma spray was investigated under an oxyacetylene torch with a heat flux of 4.18 MW/m2. Result shows that ZrC coating with 10 vol.% LaB6 has a good ablation resistance compared with pure ZrC, ZrC with 20 vol.% LaB6 and SiC-doped ZrC coating. After ablation for 15 s, the weight is increased by 1.12 mg/s. The good ablation resistance is ascribed to the formation of a stabilized scale which consists of protective La2Zr2O7-containing molten phase and ZrO2 particles keeping the integrity of the coating.