High Velocity Electric Arc Sprayed Fe-Al-Nb-B Composite Coating and Its Wear Behavior
来源期刊：Acta Metallurgica Sinica2013年第3期
论文作者：Yongxiong CHEN Xiubing LIANG Jinyuan BAI Binshi XU
文章页码：313 - 320
摘 要：A type of Fe-Al-Nb-B cored wire was designed and the coating was prepared using a robot-based electric wire arc spraying process. The Fe-Al binary cored wire and coating were also prepared as comparison. The phase composition and structure of the coatings were investigated using X-ray diffraction （XRD）, scanning electron microscopy （SEM） coupled with energy dispersive X-ray spectroscopy （EDS） and transmission electron microscopy （TEM）. The coating tribological properties were evaluated with the micromotion wear tester under different conditions. The results show that, although typical lamellar structure was performed for both the arc sprayed Fe-Al-Nb-B coating and Fe-Al coating, the structure composition, mechanical and wear properties of the former are quite different from those of latter. The Fe-Al-Nb-B coating is a typical composite coating, which is distributed inhomogeneously with α-Fe crystalline, FeAl and Fe 3 Al intermetallics, amorphous and nanocrystallines as well as locally existed oxide phases. As a result, the mircrohardness and wear resistance of the Fe-Al-Nb-B composite coating increased significantly. Finally the mechanism of the coating wear resistant behavior was discussed based on the experimental results such as friction coefficient, two dimensional and three dimensional worn surface profiles.
Yongxiong CHEN1，Xiubing LIANG1，Jinyuan BAI2，Binshi XU2
1. National Engineering Research Center for Mechanical Product Remanufacturing, Academy of Armored Forces Engineering2. National Key Laboratory for Remanufacturing, Academy of Armored Forces Engineering
摘 要：A type of Fe-Al-Nb-B cored wire was designed and the coating was prepared using a robot-based electric wire arc spraying process. The Fe-Al binary cored wire and coating were also prepared as comparison. The phase composition and structure of the coatings were investigated using X-ray diffraction （XRD）, scanning electron microscopy （SEM） coupled with energy dispersive X-ray spectroscopy （EDS） and transmission electron microscopy （TEM）. The coating tribological properties were evaluated with the micromotion wear tester under different conditions. The results show that, although typical lamellar structure was performed for both the arc sprayed Fe-Al-Nb-B coating and Fe-Al coating, the structure composition, mechanical and wear properties of the former are quite different from those of latter. The Fe-Al-Nb-B coating is a typical composite coating, which is distributed inhomogeneously with α-Fe crystalline, FeAl and Fe 3 Al intermetallics, amorphous and nanocrystallines as well as locally existed oxide phases. As a result, the mircrohardness and wear resistance of the Fe-Al-Nb-B composite coating increased significantly. Finally the mechanism of the coating wear resistant behavior was discussed based on the experimental results such as friction coefficient, two dimensional and three dimensional worn surface profiles.