Effect of yttrium oxide addition on absorption and emission properties of bismuth-doped silicate glasses
来源期刊:Journal of Rare Earths2012年第5期
论文作者:戴能利 王岩山 杨旅云 栾怀训 李进延
文章页码:418 - 421
摘 要:Y/Bi co-doped silicate glasses were prepared,and the effects of Y 2 O 3 on the absorption and emission properties were investigated by spectrum measurement.It was found that the absorption intensity in visible region decreases with increase of Y 3+ concentration in(70-x)SiO 2 xY 2 O 3-30CaO-1.5Bi 2 O 3(x=0 mol.%,1 mol.%,3 mol.%,5 mol.%,7 mol.%) glasses.The emissions centered at 410,630,1200 and 1290 nm were observed under 280,470,514 and 808 nm excitation,respectively.The emission intensity had the similar change tendency in the visible and near infrared region.We also discussed the actual role of Y 3+ ions playing in the visible and near infrared emissions of the silicate glasses.
戴能利1,王岩山1,杨旅云1,栾怀训1,李进延1
1. Wuhan National Laboratory for Optoelectronics,School of Optoelectronics Science and Engineering,Huazhong University of Science and Technology
摘 要:Y/Bi co-doped silicate glasses were prepared,and the effects of Y 2 O 3 on the absorption and emission properties were investigated by spectrum measurement.It was found that the absorption intensity in visible region decreases with increase of Y 3+ concentration in(70-x)SiO 2 xY 2 O 3-30CaO-1.5Bi 2 O 3(x=0 mol.%,1 mol.%,3 mol.%,5 mol.%,7 mol.%) glasses.The emissions centered at 410,630,1200 and 1290 nm were observed under 280,470,514 and 808 nm excitation,respectively.The emission intensity had the similar change tendency in the visible and near infrared region.We also discussed the actual role of Y 3+ ions playing in the visible and near infrared emissions of the silicate glasses.
关键词: