Effects of Annealing Process on Crystallization and Low Temperature Resistance Properties of PP-R Composites
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2018年第4期
论文作者：麻玉龙 WANG Xiaomeng LIU Wei 龚维 何力
文章页码：855 - 862
摘 要：The effects of the annealing process on the mechanical properties and crystallization behaviors of polypropylene random copolymer（PP-R） composites were investigated using differential scanning calorimetry（DSC）, wide-angle X-ray diffraction（WAXD）, and dynamic mechanical analysis（DMA）, and scanning electron microscopy（SEM）. The experimental results indicated that the annealing process significantly influenced the comprehensive properties of PP-R composites. At temperatures below 23 ℃, the impact strength of the PP-R composites annealed at 120 ℃ for 6 h was relatively high at 74.73 k J/m2, which was 16.8% higher than that of the samples annealed at 80 ℃ for 6 h. At low temperatures（-30-0 ℃）, the impact strength ranged from approximately 13.31 k J/m2 to 54.4 k J/m2. In addition, the annealing process conducted at 120 ℃ for 6 h improved the crystalline structure and low-temperature toughness of the PP-R composites and induced α-form to β-form crystal transformation. The work provides a possible method to reinforce and toughen the semicrystalline polymer at low temperatures（-30-0 ℃） by annealing.
麻玉龙1,2，WANG Xiaomeng1，LIU Wei1，龚维1,3，何力3
1. College of Materials and Architectural Engineering, Guizhou Normal University2. Guizhou Institute of Metallurgy and Chemical Engineering3. National Engineering Research Center for Compounding and Modification of Polymeric Materials
摘 要：The effects of the annealing process on the mechanical properties and crystallization behaviors of polypropylene random copolymer（PP-R） composites were investigated using differential scanning calorimetry（DSC）, wide-angle X-ray diffraction（WAXD）, and dynamic mechanical analysis（DMA）, and scanning electron microscopy（SEM）. The experimental results indicated that the annealing process significantly influenced the comprehensive properties of PP-R composites. At temperatures below 23 ℃, the impact strength of the PP-R composites annealed at 120 ℃ for 6 h was relatively high at 74.73 k J/m2, which was 16.8% higher than that of the samples annealed at 80 ℃ for 6 h. At low temperatures（-30-0 ℃）, the impact strength ranged from approximately 13.31 k J/m2 to 54.4 k J/m2. In addition, the annealing process conducted at 120 ℃ for 6 h improved the crystalline structure and low-temperature toughness of the PP-R composites and induced α-form to β-form crystal transformation. The work provides a possible method to reinforce and toughen the semicrystalline polymer at low temperatures（-30-0 ℃） by annealing.