Organic Light Emitting Diodes with p-Si Anodes and Semitransparent Ce/Au Cathodes
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2011年第2期
论文作者：孙志国 姜广智
文章页码：208 - 211
摘 要：The Ce （x nm）/Au （15 nm） stacked layers were used as semitransparent cathodes in the top-emission organic light emitting devices （TOLEDs） fabricated on a p-type silicon anodes and substrate,where x varies from 4 to 16.The consequence of the Ce layer thickness on transmittance and the device performance were studied when the organic layers NPB （60 nm）/ALQ （60 nm） were kept unchanged,where NPB was N,N’-bis-（1-naphthl）-diphenyl-1,1’-biphenyl-4,4’-diamine,and AlQ is tris-（8-hydroxyquinoline） aluminum.The cathode of Ce （11 nm）/Au （15 nm） has a transparency of 46%,and the TOLED with it achieves the highest luminescence efficiencies:a current efficiency of 0.91 cd/A at 13.7 V and a peak power efficiency of 0.28 lm/W at 9 V.The turn-on voltage is 3.0 V.The Ce/Au cathode is both chemically and electrically stable.
孙志国1，姜广智2
1. Department of Medical Technology,Henan Medical College for Staff and Workers2. Department of Physics,Zhengzhou Normal University
摘 要：The Ce （x nm）/Au （15 nm） stacked layers were used as semitransparent cathodes in the top-emission organic light emitting devices （TOLEDs） fabricated on a p-type silicon anodes and substrate,where x varies from 4 to 16.The consequence of the Ce layer thickness on transmittance and the device performance were studied when the organic layers NPB （60 nm）/ALQ （60 nm） were kept unchanged,where NPB was N,N’-bis-（1-naphthl）-diphenyl-1,1’-biphenyl-4,4’-diamine,and AlQ is tris-（8-hydroxyquinoline） aluminum.The cathode of Ce （11 nm）/Au （15 nm） has a transparency of 46%,and the TOLED with it achieves the highest luminescence efficiencies:a current efficiency of 0.91 cd/A at 13.7 V and a peak power efficiency of 0.28 lm/W at 9 V.The turn-on voltage is 3.0 V.The Ce/Au cathode is both chemically and electrically stable.
关键词：