Friction and Wear Behavior of Modified Layer Prepared on Ti-13Nb-13Zr Alloy by Magnetron Sputtering and Plasma Nitriding
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2017年第4期
论文作者：田伟红 GUO Yangyang LI Xuanpeng TANG Bin 范爱兰
文章页码：951 - 957
摘 要：Two kinds nitride modified layers were obtained on Ti-13Nb-13 Zr surface to improve the wear property via magnetron sputtering and plasma nitriding techniques, respectively. The structures of the modified layer and the worn surface after sliding test were characterized using X-ray diffraction（XRD） and scanning electron microscopy（SEM）. The friction and wear behavior of the modified layer against alumina ball was investigated in the absence of lubricant under different loads（1 N and 2 N）. The X-ray diffraction analysis reveals that nitride layer is mainly composed of TiN and Ti2N, while coating film consists of Ti N phase. Friction and wear test indicates that both modified layers can improve the wear resistance compared to untreated Ti-13Nb-13 Zr. Ti N thin film produces very hard surface, but may be easy to cause coating fracture and delamination under high normal load. However, nitride layer exhibits better wear performance. This is attributed to hard compound layer maintained its integrity with the hardened nitrogen diffusion zone during friction and wear process.
田伟红，GUO Yangyang，LI Xuanpeng，TANG Bin，范爱兰
Research Institute of Surface Engineering, Taiyuan University of Technology
摘 要：Two kinds nitride modified layers were obtained on Ti-13Nb-13 Zr surface to improve the wear property via magnetron sputtering and plasma nitriding techniques, respectively. The structures of the modified layer and the worn surface after sliding test were characterized using X-ray diffraction（XRD） and scanning electron microscopy（SEM）. The friction and wear behavior of the modified layer against alumina ball was investigated in the absence of lubricant under different loads（1 N and 2 N）. The X-ray diffraction analysis reveals that nitride layer is mainly composed of TiN and Ti2N, while coating film consists of Ti N phase. Friction and wear test indicates that both modified layers can improve the wear resistance compared to untreated Ti-13Nb-13 Zr. Ti N thin film produces very hard surface, but may be easy to cause coating fracture and delamination under high normal load. However, nitride layer exhibits better wear performance. This is attributed to hard compound layer maintained its integrity with the hardened nitrogen diffusion zone during friction and wear process.
关键词：