Trans. Nonferrous Met. Soc. China 25(2015) 3139-3145
Kinetics of titanium leaching with citric acid in sulfuric acid from red mud
Xiao-bo ZHU1,2, Wang LI1,2, Xue-mao GUAN1,2
1. School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo 454000, China;
2. Henan Key Discipline Open Laboratory of Mining Engineering Materials, Henan Polytechnic University, Jiaozuo 454000, China
Received 13 October 2014; accepted 28 December 2014
Abstract:
The recovery of titanium with citric acid in sulfuric acid from red mud was put forward to strengthen acid leaching efficiency. The main factors on the recovery of titanium such as citric acid addition, sulfuric acid concentration, leaching temperature, time and liquid-to-solid ratio were studied. The kinetics analysis of titanium leaching from red mud was deeply investigated. The results show that the citric acid could increase the recovery of titanium and decrease the consumption of sulfuric acid. The recovery of titanium was increased from 65% to 82% and the consumption of sulfuric acid was decreased by about 30% with using 5% citric acid. The dissolution of perovskite, brookite, and hematite in red mud could easily be dissolved using citric acid. The acid leaching process was controlled by internal diffusion of shrinking core model (SCM) and the correlation coefficient was above 0.98. The apparent rate constant was increased from 0.0012 to 0.0019 with 5% citric acid at 90 °C. The apparent activation energy of titanium leaching decreased from 39.77 kJ/mol to 34.61 kJ/mol with 5% citric acid.
Key words:
red mud; titanium; kinetics; citric acid; acid leaching;
1 Introduction
Red mud is a kind of alkaline solid waste from the tailings during alumina production of bauxite [1-3]. About 0.8-1.5 t red muds are generated per ton of alumina and it is estimated that over 70 million tons of the waste are impounded annually in the world [4,5]. Meanwhile, the rising tendency of red mud output is increasing year by year. The disposal of damming up process on red mud is expensive and can cause environmental problems [6-8].
Red mud usually contains many kinds of metals such as Ti, Al, Ca, Na, V and Sc [9-11]. Titanium is a valuable metal which can be extracted from many kinds of minerals using direct acid leaching, alkaline leaching and activation roasting-acid leaching [12-14]. The recovery of titanium from Bayer process red mud was investigated with concentrated sulfuric acid [15]. The sulfuric acid concentration above 6 mol/L was needed and the recovery of titanium was lower than 70% [16]. For example, the extraction of titanium from red mud with sulfuric acid leaching under the condition of atmospheric pressure and without pretreatment was proposed by AGATZINILEONARDOU et al [17]. The recovery of titanium was 64.5% under the condition of sulfuric acid concentration of 6 mol/L, temperature of 60 °C and liquid-to-solid mass ratio of 20:1. Therefore, a lot of strong acid leaching solution was obtained due to the high sulfuric acid concentration and liquid-to-solid ratio [18,19]. However, there are few reports on the new effective agent and kinetics of titanium leaching from red mud.
In order to enhance leaching efficiency and decrease sulfuric acid consumption, the present research work was to investigate the recovery of titanium with citric acid from red mud. Furthermore, the process was scientifically explained using leaching kinetics to confirm titanium recovery from red mud.
2 Experimental
2.1 Materials
The red mud was collected from Henan Province, China. Its particle size distribution is shown in Fig. 1.
Fig. 1 Particle size distribution of red mud
It is found that 50% of the red mud was smaller than 5 μm, whereas 100% of the sample was smaller than 33 μm. The sample was very fine and did not need to be crushed for acid leaching. The sample was assayed using inductively coupled plasma atomic emission spectroscopy (ICP-AES), and the result is given in Table 1.
Table 1 Main chemical composition of red mud (mass fraction, %)
It is shown that the composition of this red mud complex contained many metallic oxides such titanium, aluminum, ferrum, calcium and vanadium oxides. The XRD pattern of the red mud sample is depicted in Fig. 2.
It is indicated that the main minerals in the red mud were perovskite, brookite, hematite, calcite, cancrinite, quartz and muscovite.
The analytical purity chemical reagent including citric acid and sulfuric acid from Dengke Chemical Reagent Technology Co., Ltd., was used. The water used in this work was distilled water.
Fig. 2 XRD pattern of red mud sample
2.2 Methods
The sample was firstly dried at 95 °C for 12 h in a TE-DO130 drying oven (China), which was taken out of the drying oven and then cooled further to room temperature. Then 20 g dried sample was mixed citric acid with the sulfuric acid solution of different concentrations. Then, the ore slurry was stirred using a KX79-1 magnetic heating mixer (China) at the speed of 300 r/min under different conditions of time, temperature and liquid-to-solid ratio. The acid leaching solution was collected by filtration with a SHB-IIIA vacuum suction filter (China). The solid residue was dissolved in hydrofluoric acid solution and then the content of titanium was determined by ICP-AES. The recovery of titanium was calculated by the following equation.
(1)
where α is the recovery of titanium, q is the titanium quantity of sample and p is the titanium quantity of final residue.
3 Results and discussion
3.1 Effect of citric acid
The effect of citric acid addition on the recovery of titanium is shown in Fig. 3 under the condition of sulfuric acid concentration of 5 mol/L, liquid-to-solid ratio of 5:1, temperature of 90 °C and reaction time of 60 min.
It can be observed that the recovery of titanium increased with increasing the citric acid addition. The increasing rate was sharp in low citric acid addition range, and became mild in citric acid addition ratio range. The recovery of titanium could reach 82% with adding 5% citric acid.
3.2 Effect of sulfuric acid concentration
The effects of sulfuric acid concentration without and with 5% citric acid on recovery of titanium are illustrated in Fig. 4 under the condition of liquid-to-solid ratio of 5:1, temperature of 90 °C and reaction time of 60 min.
Fig. 3 Effect of citric acid addition on recovery of titanium
Fig. 4 Effect of sulfuric acid concentration on recovery of titanium
It can be seen from Fig. 4 that the 82% of titanium recovery could be obtained with 7 mol/L sulfuric acid, but only 5 mol/L sulfuric acid was needed with adding 5% citric acid. The recovery of titanium was increased and the increase tendency was symmetrical with increasing sulfuric acid concentration. Furthermore, the sulfuric acid consumption was decreased by 30% with adding 5% citric acid.
3.3 Effect of liquid-to-solid ratio
The effects of liquid-to-solid ratio on recovery of titanium at different leaching time without and with 5% citric acid are shown in Fig. 5 and Fig. 6, respectively under the condition of sulfuric acid concentration of 5 mol/L and temperature of 90 °C.
It is indicated that the recovery of titanium increased with increasing the liquid-to-solid ratio in Fig. 5 and Fig. 6. The increase tendency was sharp at low liquid-to-solid ratio and leaching time range. The recovery of titanium could increase from 45% to 60% with increasing liquid-to-solid ratio from 3:1 to 5:1 at leaching time of 60 min without citric acid. The recovery of titanium was 79% with liquid-to-solid ratio of 9:1 at leaching time of 60 min. The increase tendency of titanium recovery with 5% citric acid was similar to that without citric acid. The recovery of titanium was 82% at liquid-to-solid ratio of 7:1 with adding 5% citric acid. Therefore, the citric acid could not only decrease the sulfuric acid concentration, but also reduce the liquid-to- solid ratio in the acid leaching process.
3.4 Effect of leaching temperature
The effects of leaching temperature on recovery of titanium at different leaching time without and with 5% citric acid are given in Fig. 7 and Fig. 8, respectively under the condition of sulfuric acid concentration of 5 mol/L and liquid-to-solid ratio of 5:1.
Fig. 5 Effect of liquid-to-solid ratio on recovery of titanium without citric acid
Fig. 6 Effect of liquid-to-solid ratio on recovery of titanium with 5% citric acid
Fig. 7 Effect of leaching temperature on recovery of titanium without citric acid
Fig. 8 Effect of leaching temperature on recovery of titanium with 5% citric acid
It can be observed that the recovery of titanium increased sharply with increasing temperature from 30 °C to 90 °C. The titanium recovery increased from 20% to 65% with increasing temperature from 30 °C to 90 °C at leaching time of 60 min, whereas the values were 30% and 82% at leaching temperature of 30 °C and 90 °C with adding 5% citric acid in Fig. 7 and Fig. 8. It can be also explained that the reaction rate of acid leaching with citric acid was quicker. Furthermore, the increasing rate of the recovery of titanium was rapid first and then became mild.
3.5 Kinetics analysis of titanium leaching
It is important to establish a quantitative measurement of the leaching kinetics and mechanism to confirm the leaching process. The XRD pattern of leaching residue of red mud is shown in Fig. 9.
Fig. 9 XRD patterns of leaching residues
It can be seen that perovskite, brookite and hematite have been dissolved and quartz was nearly not dissolved in red mud with sulfuric acid, where some anhydrites existed due to the dissolution of perovskite and brookite. However, in the leaching process with citric acid, the recovery of titanium was increased by accelerating the dissolution of perovskite and brookite, where the phase of anhydrite was enhanced with 5% citric acid. Furthermore, the residue existed after the leaching process. Therefore, the experimental data can be analyzed using the SCM [20].
According to the SCM, assuming that the leaching process is controlled by the internal diffusion, the following expression of leaching kinetics can be used:
Kat=[1-2α/3-(1-α)2/3] (2)
However, assuming that the leaching process is controlled by the chemical reaction, the following expression can be applied for the leaching kinetics:
Kbt=[1-(1-α)1/3] (3)
where t is reaction time, α is titanium recovery, Ka is rate constant of internal diffusion, Kb is rate constant of chemical reaction.
Two controlling steps of the SCM were investigated under different liquid-to-solid ratios without citric acid. The results are shown in Fig. 10.
According to Figs. 10(a) and (b), the control of internal diffusion fitted the leaching data well at different liquid-to-solid ratios. As the leaching process was controlled by internal diffusion, the main factor was the internal diffusion rate of sulfuric acid into particles interior. The internal diffusion rate increased with increasing sulfuric acid and leaching temperature.
Fig. 10 Plots of 1-2α/3-(1-α)2/3 (a) and 1-(1-α)1/3 (b) versus time at different liquid-to-solid ratios without citric acid
Two controlling steps of the SCM were investigated under different liquid-to-solid ratios with adding 5% citric acid. The results are indicated in Fig. 11.
Fig. 11 Plots of 1-2/3α-(1-α)1/2 (a) and 1-(1-α)1/3 (b) versus time at different liquid-to-solid ratios with 5% citric acid
According to Figs. 11(a) and (b), the control of internal diffusion still fitted the leaching data well at different liquid-to-solid ratios with adding citric acid. Therefore, the apparent activation energy and reaction rate constant of titanium leaching were needed to investigate to illustrate the effect of citric acid on titanium extraction from red mud.
3.6 Reaction rate constant and apparent activation energy of titanium leaching
The internal diffusion controlling steps of the SCM were investigated under different temperatures without and with adding 5% citric acid. The results are shown in Fig. 12.
It can be seen that the control of internal diffusion also fitted the leaching data well and the correlation coefficient (R2) was larger than 0.98 at different temperatures. The apparent rate constants of acid leaching process were 0.0001, 0.0002, 0.0008 and 0.0012 at 30, 50, 70 and 90 °C, respectively. However, those were 0.0002, 0.0005, 0.0011 and 0.0019, respectively with adding 5% citric acid. The apparent rate constant increased with increasing the leaching temperature, and the apparent rate constant of acid leaching with citric acid was higher than that without citric acid.
Fig. 12 Plots of 1-2α/3-(1-α)2/3 versus time at different temperatures without (a) and with 5% citric acid (b)
According to the speed constants at different temperatures without and with citric, the plots of ln Ka versus temperature were investigated. The results are indicated in Figs. 13 and 14, respectively.
Fig. 13 Plots of ln Ka versus temperature of titanium leaching without citric acid
Fig. 14 Plots of ln Ka versus temperature of titanium leaching with 5% citric acid
It can be observed that the correlation coefficient (R2) was above 0.98 at different temperatures. The apparent activation energies (Ea) of titanium leaching without and with citric acid were 39.77 kJ/mol and 34.61 kJ/mol by the calculation. The decrease of apparent activation energy can effectively enhance the leaching process based on the theory of kinetics.
4 Conclusions
1) The recovery of titanium reached 82% under the conditions of citric acid of 5%, sulfuric acid concentration of 5 mol/L, temperature of 90 °C, liquid- to-solid ratio of 5:1 and time of 60 min. The XRD patterns of red mud and leaching residue showed that the citric acid could enhance the dissolution of perovskite and brookite.
2) The acid leaching process was controlled by internal diffusion and the correlation coefficient was above 0.98 using SCM. The speed constant and Ea of titanium leaching were 0.0019 and 34.61 kJ/mol with 5% citric acid at 90 °C, which resulted in the increase of titanium recovery.
References
[1] YU Zhang-long, SHI Zhi-xia, CHEN Yong-mei, NIU Yin-jian, WANG Yong-xia, WAN Ping-yu. Red-mud treatment using oxalic acid by UV irradiation assistance [J]. Transactions of Nonferrous Metals Society of China, 2012, 22(2): 456-460.
[2] JIANG Yi-jiao, NING Ping. An overview of comprehensive utilization of red mud from aluminum production [J]. Environment Science and Technology, 2003, 26: 40-42. (in Chinese)
[3] LI Xiao-bin, XIAO Wei, LIU Wei, LIU Gui-hua, PENG Zhi-hong, ZHOU Qiu-sheng, QI Tian-gui. Recovery of alumina and ferric oxide from Bayer red mud rich in iron by reduction sintering [J]. Transaction of Nonferrous Metals Society of China, 2009, 19(5): 1342-1347.
[4] LAI Lan-ping, ZHOU Li-pu, HAN Gang, LUO Xing-ping. The red mud reclaims synthetically and makes use of current situation and progress [J]. Sichuang Nonferrous Metals, 2008, 1: 43-48. (in Chinese)
[5] LIU Wang-chao, SUN Shou-yi, ZHANG Ling, JAHANSHAHI S, YANG Jia-kuan. Experimental and simulative study on phase transformation in Bayer red mud soda-lime roasting system and recovery of Al, Na and Fe [J]. Minerals Engineering, 2012, 39: 213-215.
[6] ZHU Qiang, QI Bo. Development and status of red mud comprehencesive utilization technology in China [J]. Light Metals, 2009, 8: 8-10. (in Chinese)
[7] LUO Dao-cheng, LIU Jun-feng, YI Ping-gui, CHENG An-guo. New process of utilizing red mud from alumina treating plant to produce high quality direct-reduction iron [J]. China Mining Magazine, 2002, 5: 50-53. (in Chinese)
[8] YANG Shao-wen, CAO Yao-hua, LI Qing. The current situation and progress: Multipurpose utilization of red mud from alumina production [J]. Conservation and Utilization of Mineral Resources, 1999, 6: 46-49. (in Chinese)
[9] ZENG De-qi. Comprehensive utilization of associated component from bauxite in pingguo [J]. Light Metals, 2000, 8: 7-10. (in Chinese)
[10] INDRANI G, SAUMYEN G, BALASUBRAMANIAM R, RAMESH K A V. Leaching of metals from fresh and sintered red mud [J]. Journal of Hazardous Materials, 2011, 185: 662-668.
[11] SMIRNOV D I, MOLCHANOVA T V. The investigation of sulfuricacid sorption recovery of scandium and uranium from the red mud of alumina production [J]. Hydrometallurgy, 1997, 45: 249-259.
[12] LIU Shui-shi, GUO Yu-feng, QIU Guan-zhou, JIANG Tao, CHENG Feng. Solid-state reduction kinetics and mechanism of pre-oxidized vanadium-titanium magnetite concentrate [J]. Transactions of Nonferrous Metals Society of China, 2014, 24(10): 3372-3377.
[13] LIU Shui-shi, GUO Yu-feng, QIU Guan-zhou, JIANG Tao, CHENG Feng. Preparation of Ti-rich material from titanium slag by activation roasting followed by acid leaching [J]. Transactions of Nonferrous Metals Society of China, 2013, 23(4): 1174-1178.
[14] SUI Li-li, ZHANG Yu-chun. Reaction kinetics of roasting high-titanium slag with concentrated sulfuric acid [J]. Transactions of Nonferrous Metals Society of China, 2014, 24(3): 848-853.
[15] CENGELOGLU Y, KIR E, ERSOZ M, BUYUKERKEK T, GEZGIN S. Recovery and concentration of metals from red mud by Donnan dialysis [J]. Colloids and Surfaces, 2003, 223: 95-101. (in Chinese)
[16] OCHSEKUHN P M, LYBEROPULU T, PARISSAKIS G. Recovery of lanthanides and yttrium from red mud by selective leaching [J]. Analytica Chmica Acta, 1996, 319: 249-254.
[17] AGATZINILEONARDOU S, OUSTADAKI P, TSAKIRIDIS P E, MARKOPOULOS C. Titanium leaching from red mud by diluted sulfuric acid at atmospheric pressure [J]. Journal of Hazardous Materials, 2008, 157: 579-586.
[18] ZHU Zhao-wu, ZHANG Wen-sheng, CHENG Chu-yong. A literature review of titanium solvent extraction in chloride media [J]. Hydrometallurgy, 2011, 105: 304-313.
[19] SONG Qiang, WANG Jia-wei, XU Ben-jun. Leaching of Ti-enriched slag from red mud with sulfuric acid [J]. Nonferrous Metals, 2012, 5: 27-29. (in Chinese)
[20] ZHU Xiao-bo, ZHANG Yi-min, HUANG Jing, LIU Tao, WANG Yi. A kinetics study of multi-stage counter-current circulation acid leaching of vanadium from stone coal [J]. International Journal of Mineral Processing, 2012, 114-117: 1-6.
柠檬酸助浸提取赤泥中钛的动力学
朱晓波1,2，李 望1,2，管学茂1,2
1. 河南理工大学 材料科学与工程学院，焦作454000；
2. 河南理工大学 河南省高等学校矿业工程材料重点学科开放实验室，焦作454000
摘 要：在硫酸体系中，采用柠檬酸助浸提取赤泥中的钛，以提高钛的浸出效率。考察柠檬酸用量、硫酸浓度、浸出温度、反应时间和液固比等因素对钛浸出率的影响。研究赤泥浸出提钛过程的动力学理论。结果表明：在赤泥浸出过程中添加柠檬酸可显著提高钛的回收率和降低硫酸消耗。通过添加5%的柠檬酸，钛的浸出率从65%提高至82%，硫酸消耗降低30%，赤泥中的钙钛矿、板钛矿和赤铁矿更容易溶解溶出。动力学研究表明：赤泥助浸酸浸提钛过程受未反应收缩核模型的扩散步骤控制，线性相关系数大于0.98。通过添加5%的柠檬酸，可使赤泥酸浸提钛表观速率常数从0.0012提高至0.0019，表观活化能由39.77 kJ/mol 降至 34.61 kJ/mol。
关键词：赤泥；钛；动力学；柠檬酸；酸浸
(Edited by Yun-bin HE)
Foundation item: Project (B2014-012) supported by the Doctoral Foundation from Henan Polytechnic University, China
Corresponding author: Xiao-bo ZHU; Tel: +86-391-3986937; E-mail: zhuxiaobo0119@126.com
DOI: 10.1016/S1003-6326(15)63944-9
Abstract: The recovery of titanium with citric acid in sulfuric acid from red mud was put forward to strengthen acid leaching efficiency. The main factors on the recovery of titanium such as citric acid addition, sulfuric acid concentration, leaching temperature, time and liquid-to-solid ratio were studied. The kinetics analysis of titanium leaching from red mud was deeply investigated. The results show that the citric acid could increase the recovery of titanium and decrease the consumption of sulfuric acid. The recovery of titanium was increased from 65% to 82% and the consumption of sulfuric acid was decreased by about 30% with using 5% citric acid. The dissolution of perovskite, brookite, and hematite in red mud could easily be dissolved using citric acid. The acid leaching process was controlled by internal diffusion of shrinking core model (SCM) and the correlation coefficient was above 0.98. The apparent rate constant was increased from 0.0012 to 0.0019 with 5% citric acid at 90 °C. The apparent activation energy of titanium leaching decreased from 39.77 kJ/mol to 34.61 kJ/mol with 5% citric acid.