Trans. Nonferrous Met. Soc. China 24(2014) 2695-2703
Noisy-power dissipation and efficiency in NiO/Fe2O3 wet grinding by planetary ball mill
Yun YAO1, Gang XIE1,2, Yan-qing HOU1, Rong-xing LI1, Wei-hong LUO1, Ru-zhen PENG1, Zhan-liang YU2
1. Faculty of Metallurgical and Energy Engineering, Kunming University of Science and Technology, Kunming 650093, China;
2. Kunming Metallurgy Research Institution, Kunming 650031, China
Received 20 May 2013; accepted 14 April 2014
Abstract:
The relationship between the efficiency of NiO/Fe2O3 wet grinding and noisy-power dissipation was studied. The optimal grinding parameters were found as: a slurry water content of 64.10%-85.47%, ball number ratio of 360/20, revolution speed of 300.9 r/min, powder-filling ratio of 10.88%, ball-filling ratio of 20.53%-23.88%, and grinding time of approximately 6 h. The discrete element method (DEM) was employed to analyze relationship between the noisy-power dissipation and the grinding efficiency, and equations describing the relationship were derived. The mean particle size of the ground powder decreased with a decrease in the degree of noisy-power dissipation, while the grinding efficiency and the amount of specific impact power used decreased with an increase in the degree of noisy-power dissipation.
Key words:
noisy-power dissipation; NiO/Fe2O3 powder; planetary ball mill; mean particle size;
1 Introduction
Interest in alloy and cermet materials for fabricating inert anodes for use in industrial aluminum electrolysis has increased in recent years because of their significant advantages in terms of energy, cost, productivity, and environmental benefits [1-8]. NiFe2O4-based cermet is one of the most promising materials studied in recent years, due to its high electrical conductivity and corrosion resistance [6,9]. However, the performance of the inert anode fabricated from NiFe2O4-based cermet could not satisfy the requirements for aluminum electrolysis because of unsuitable mechanical properties and insufficient corrosion resistance and electrical conductivity.
Generally, ball milling and sintering techniques have been used to produce NiFe2O4-based cermet. However, well-blended, fine granular NiO/Fe2O3, which is the precursor of NiFe2O4, must be prepared first. The planetary ball mill is one of the most popular equipments for grinding NiO/Fe2O3 because of its moderate cost and simple setup and handling [7,10,11]. Researchers identified that the grinding efficiency of planetary ball mill depends on several factors, such as pot diameter, pot depth, ball diameter, ball-filling ratio, revolution radius, material-filling ratio, and rotational speed [12,13]. Further, the impact energy between balls and powders, frequency of impacts, and abrasion are major factors that influence the working of planetary ball mills, and these factors are related to the ball–ball, ball-container, ball–powder, and powder–powder impact energy and collision frequency [14,15]. The specific impact energy is a useful parameter for analyzing the grinding mechanism and granular media performance [12-14,16]. However, few systematic experimental investigations conducted to date have focused on technical parameters, noisy-power dissipation, and efficiency in NiO/Fe2O3 grinding because observing the motion of the balls within the mills and evaluating the performance of the mills are difficult. In fact, studies on NiO/Fe2O3 grinding and their noisy-power dissipation are seldom reported nowadays.
In recent years, the discrete element method (DEM) [10,14,15,17-19], particle element method (PEM) [20], and modified version of the distinct element method (MDEM) [21] have been utilized to investigate specific impact energy dissipation in the case of materials such as gibbsite [13,14,22], limestone [22], and talc [16]. In particular, the DEM is one of the most powerful techniques for investigating the granular-media grinding mechanism and performance.
Therefore, in this study, the DEM is employed to analyze the water-filling ratio, number ratio of balls with diameters of 10 mm and 20 mm, revolution speed, powder-filling ratio, ball-filling ratio, grinding time, and the relationship between grinding efficiency and noisy-power dissipation in the grinding of NiO/Fe2O3. Three major mechanical energy dissipation modes were found during planetary ball milling operation: efficient energy absorption by the ground powder, noisy-power dissipation, and thermal energy generation as a result of heating of the granular media, pots, and gas during grinding. The efficient energy absorbed by ground powder and noisy-power dissipation should not be omitted in the balls motion, but thermal energy of heating granular media grinding, pots and gas is very small because the temperature is homogeneous during the grinding.
2 Experimental
2.1 Equipment and chemical reagents
The grinding mill used in this study was a planetary ball mill (XQM-4L, China). The mill consisted of four pots made of stainless steel (density, ρ=8.2×103 kg/m3) placed on a revolving disk. The volume, inner diameter, and height of the pots were 1l, 118, and 92 mm, respectively. The grinding media were dual-sized balls (diameters of 10 mm, 20 mm) made of stainless steel. The rotational speed, r, which was determined by the rotation-to-revolution speed ratio of the planetary ball mill, was set to be 1.00 for the study (r=NP/Nr, where NP is the rotation speed of the pots and Nr is the revolution speed of the disk). The revolution speed of the disk could be varied from 50 to 400 r/min, and the rotation speed of the disk could be varied from 100 to 800 r/min. The planetary ball mill was set to alternately rotate and revolve in the clockwise and anticlockwise directions at intervals of 5 min. The pot was set to rotate counter to the direction of revolution of the disk.
The acoustic test instrument employed in the study was an AR824 digital sound level meter (Smart Sensor, China) and was used to test the level of noisy-power dissipation in the planetary ball mill. During the working of the ball mill, the output of the digital meter increased with an increase in the amount of power dissipated. Thus, the digital sound level meter could evaluate the efficiency of grinding indirectly.
The sizes of the particles of the samples to be ground were measured using the sedimentation method. Ethanol (CH3CH2OH; minimum concentration of 99.8%) was employed as the liquid for the measurements. The sedimentation method for determining the particle size is based on the fact that particles were smaller in size when displace in larger volume of suspension (Vs) of ethanol absolute at any point of time. The specific surface areas of the ground powers were characterized by a Nova Win surface area analyzer (Quantachrome Instruments, USA).
The test samples to be ground were a ferric oxide (Fe2O3) powder (minimum concentration of 95.76%; Liuzhou Yuejin Chemical Industry Limited Company, China) and a nickel protoxide (NiO) powder (minimum concentration of 99%, Chengdu Nickel Powder Materials LLC, China). The initial diameters of the Fe2O3 and NiO powder particles were 47 and 75 μm, respectively. The two powders were mixed in a Fe2O3/NiO mass ratio of 57.9/42.1. The Fe2O3/NiO mixture was then dispersed in water in different concentrations, and the resulting slurries were used as the starting samples. These samples were placed in each pot of the planetary ball mill and ground. The blended slurries were dried in an oven at 100 °C for 24 h. The blended powders obtained after drying the slurries were dispersed using an agate mortar. As mentioned previously, the particle sizes of the blended powders were measured using the sedimentation method, and their specific surface areas were measured using a surface area analyzer.
2.2 Single-factor experiments
2.2.1 Effect of water content of slurry
200 small balls (diameter of 10 mm) and 40 big balls (diameter of 20 mm) were placed in each stainless steel pot along with 234 g of the powder mixture to be ground. The grinding time and rotation speed were set to be 4 h and 299.5 r/min, respectively. The amount of water added to each pot ranged from 50 g to 450 g. That is to say, the water content of the NiO/Fe2O3 slurries was 21.4%-192.3%.
2.2.2 Effect of number ratio of big to small balls
The small (diameter of 10 mm) and big (diameter of 20 mm) steel balls were placed at different number ratios in the stainless steel pots. However, the total volume of the balls was kept constant at ~272.3 cm3. The numbers of small and big balls used are listed in Table 1. At every stage of the experiment, each pot contained the same number of balls. 234 g of the dry powder was placed in each pot. The grinding time and rotation speed were set to be 4 h and 299.5 r/min, respectively. The amount of water added to each pot was 150 g. That is to say, the water content of the NiO/Fe2O3 slurry in each pot was 64.1%.
Table 1 Number ratio of balls with diameters of 10 mm and 20 mm
2.2.3 Effect of rotation speed
360 small balls and 20 big ones were placed in each pot. 234 g of the dry powder mixture was also placed in each pot. The grinding time was set to be 4 h. The amount of water added to each pot was 150 g. That is to say, the water content of the NiO/Fe2O3 slurry in each pot was 64.1%. The rotation speed was varied from 260.6 to 460.8 r/min.
2.2.4 Effect of powder-filling ratio
360 small balls and 20 big balls were placed in each pot. The total mass of all the balls was 2151.33 g. The amounts of dry powder added to each pot were 116.79, 234.00, 351.00, 468.00, and 585.30 g for ball/powder mass ratios of 5.44%, 10.88%, 16.32%, 21.75%, and 27.21%, respectively. The grinding time and rotation speed were set to be 4 h and 300.9 r/min, respectively. The amount of water added to each pot was 150 g. That is to say, the water content of the NiO/Fe2O3 slurry in each pot was 64.1%.
2.2.5 Effect of ball-filling ratio
Balls were placed in the pots in different ball-filling ratios, J. The ball-filling ratios used are listed in Table 2. The amount of dry powder added to each pot was 234.2 g. The grinding time and rotation speed were set to be 4 h and 300.9 r/min, respectively. The amount of water added to each pot was 150 g. That is to say, the water content of the NiO/Fe2O3 slurry in each pot was 64.1%.
2.2.6 Effect of grinding time
360 small balls and 20 big ones (the ball-filling ratio was 27.23%) were placed in each pot. The amount of dry powder added to each pot was 234 g. The grinding time, t, was varied from 2 h to 12 h with the mean grinding time being 2 h. The rotation speed was set to be 300.9 r/min. The amount of water added to each pot was 150 g. That is to say, the water content of the NiO/Fe2O3 slurry in each pot was 64.1%.
Table 2 Conditions corresponding to different ball-filling ratios
3 Results and discussion
During planetary ball milling operations, mechanical energy is dissipated through three major paths. These are the absorption of energy by the powder to be ground, noisy-power dissipation, and the thermal energy released by the heating of the granular media being ground and the pots and gas used in the grinding process. On the basis of the results of this study, the mechanical energy dissipated could be represented by Eq. (1). In this equation, the last term on the right-hand side is usually very small, as the temperature during the grinding process remains constant.
PW=PW,m+PW,n+PW,h (1)
where PW is the specific impact energy of the planetary ball mill; PW,m is the energy absorbed by the granular media to be ground; PW,n is the energy dissipated owing to noisy-power dissipation; PW,h is the thermal energy released by the heating of the granular media to be ground and the pots and gas used.
3.1 Analysis of Vs and PW,n for different slurry water contents
Figure 1 shows the effects of the slurry water content on Vs and PW,n for the parameters listed in Table 3. It can be seen that Vs and PW,n increase initially with an increase in the slurry water content. The value of Vs peaks at 27 mL when the content is 85.5%; the corresponding value of PW,n is 0.0026 J/s. The value of PW,n reaches the maximum (0.0044 J/s) when the content is 42.7%; the corresponding Vs is 18 mL. Further, both Vs and PW,n decease with further increase in the water content.
The above-described phenomena were analyzed using the DEM. Using the DEM, MORI et al [16] had found that the motion of the balls during wet milling is affected by the drag force, FD, and the buoyancy of the mill balls.
Fig. 1 Relationship among slurry water content, Vs, and PW,n
Table 3 Parameters for single-factor experiments
The value of FD can be calculated using Eq. (2). It should be noted that Cd in Eq. (2) is calculated using Eq. (3) and it is a function of the Reynolds number, Re, which is given by Eq. (4).
(2)
(3)
(4)
where Cd is the drag coefficient; A is the projection area of a mall ball; ρs is the density of the slurry; uR is the relative velocity of an individual ball and the slurry; dB is the diameter of an individual ball; α is the viscosity of the slurry.
According to Eqs. (2)-(4), the phenomenon of grinding shown in Fig. 1 is related to ρs, A, uR, α, and dB. dB is assumed to be constant for this experiment. When the water content of the slurry is very small (i.e., the powder mixture in the mill pots is dry), uR remains constant and Re increases with an increase in water content. It should be noted that Re is very small since the viscosity of the slurry is high when it is dry, that is, its water content is very low. Therefore, the last term on the right-hand side of Eq. (3) cannot be neglected. Hence, Cd decreases with an increase in Re. In addition, FD decreases with a decrease in Cd, as suggested by Eq. (2). The buoyancy of the balls is also very low when the slurry water content is low. The energy dissipated by the powder is very large because FD and buoyancy are very small. The first term on the right-hand side of Eq. (1), which results from the force acting on the powder, is very large. Therefore, the value of PW is determined primarily by the PW,m term, which increases with an increase in Vs.
Secondly, Cd, ρs, A, and α decrease and uR increases with an increase in the slurry water content, that is, as the dry powder becomes a slurry (or as the ground material starts to cover the grinding balls). The grinding process corresponds to a transition state that is affected by both FD and the buoyancy together. The energy dissipated by the powder is the maximum in this transition state. Therefore, PW is determined by PW,m. Further, Vs is the maximum in this transition state.
In the end, the NiO/Fe2O3 powder does not cover the balls completely as the buoyancy of the balls is at the highest value. The value of Re is very large, and thus the last term on the right-hand side in Eq. (3) can be neglected. Further, ρs, A, uR, α, dB, and Cd are constant. Hence, FD does not vary with an increase in the slurry water content when the water content is very large. Therefore, Vs remains almost constant, and PW is mostly determined by the PW,n term.
According to Eqs. (2)-(4), Vs decreases (i.e., the particle size is large) when FD increases. Similarly, Vs increases (i.e., the particle size is small) when FD decreases. From Fig. 1, it can be seen that Vs reaches the maximum value of 27 mL when PW,n and the water content are 0.003-0.0026 J/s and 64.10%-85.47%, respectively. In this case, the grinding process is the most efficient, and PW,n has the smallest value. Hence, the slurry water content should be controlled to be 64.10%-85.47%. Further, an interesting phenomenon can be seen in Fig. 1, in which the grinding efficiency of the planetary ball mill decreases as the energy dissipated in the form of noisy power increases.
3.2 Analysis of Vs and PW,n for different ball number ratios
Figure 2 shows that Vs and PW,n vary with the number ratio of the balls with diameters of 10 mm and 20 mm as the other parameters listed in Table 3, remain constant. It can be seen from the figure that Vs increases to 40 mL (i.e., the particle size decreases as Vs increases) with an increase in the number ratio; the corresponding PW,n is 0.0023 J/s. Further, Vs decreases with the number ratio of the balls. However, PW,n increases with an increase in the number ratio.
Fig. 2 Relationship among number ratio of balls with diameters of 10 mm and 20 mm, Vs, and PW,n
On the basis of the DEM, ROSENKRANZ et al [10] and MIO et al [12] found that the motion of the mill balls is effective in grinding powders when the motion shifts from cascading-type to cataracting-type during grinding; further, they also noted that the rolling motion of the mill balls was ineffective for grinding. This phenomenon can be interpreted using the Newton’s Second Law. For simplicity, considering that a single-mill ball spirals upwards, as shown in Fig. 3. According to the Newton’s Second Law, this type of cascading motion can be described by Eq. (5).
(5)
where μ is the friction coefficient; R is the rotation-to-revolution speed ratio; ω is the angular velocity; θ is the angle between the horizontal and vertical directions; g is standard gravity.
Fig. 3 Force analysis of in pots dspiral motion of a mill ball
In Fig. 2 and Eq. (5), R and the rotation and revolution speeds are constants. μ and θ increase with an increase in the number ratio of the balls with diameters of 10 mm and 20 mm. Cascading-type motion takes place when the term on the left-hand side of Eq. (5) is greater than the term on the right-hand side. At this point, the motion shifts from cascading type to cataracting type. The specific impact energy increases when the motion is of the cascading type, suggesting that a greater amount of PW is absorbed by the NiO/Fe2O3 powder, resulting in finer particles. Hence, Vs reaches a high value of 40 mL when the motion is of the cascading type. Subsequently, the motion shifts from the cataracting type to the rolling type when the number ratio is increased further. Rolling-type motion is ineffective for grinding because the rate of collision of the balls decreases considerably and the balls start colliding against the mill walls. Hence, Vs decreases slowly when rolling-type motion occurs.
As can be seen from Fig. 2, PW,n decreases when Vs and the number ratio increase with PW,n exhibiting the lowest value at Vs of 40 mL and number ratio of 360/20. The grinding process is the most efficient when PW,n is the lowest.
3.3 Analysis of Vs and PW,n for different rotation-to- revolution speeds
Figure 4 plots Vs and PW,n as functions of the rotation-to-revolution speed, v; the rest of the parameters were the ones listed in Table 3. Both Vs and PW,n increase with an increase in v. The value of Vs peaks at 40 mL when the rotation-to-revolution speed is 300.9 r/min and PW,n is 2.9 mJ/s. Further, PW,n reaches its maximum value of 7.5 mJ/s when the rotation-to-revolution speed is 420.4 r/min and Vs is 30 mL. Subsequently, both Vs and PW,n decrease for further increases in the rotation-to- revolution speed.
The changes in Vs and PW,n with v can be interpreted on the basis of the value of PW during milling. Based on the DEM, KANO et al [20], MORI et al [16], and MIO et al [12,13] found that PW can be calculated using Eq. (6). In this equation, vj is the relative velocity corresponding to the collisions between two balls and/or of a ball against the mill wall. Equation (1) can be expressed as Eq. (8) on the basis of Eq. (6).
(6)
(7)
(8)
where W is the mass of the sample placed in the mill; n is the number of collisions of the balls per second in the mill; m is the mass of a small ball; M is the reduced mass of balls with diameter of 10 mm and 20 mm; t is the grinding time.
In this experiment, M and W were assumed to be constant. The values of PW and n were affected only by vj. Vs increases with PW,m in Eq. (8). Cascading-type motion does not occur when v is very small, owing to the centrifugal force caused by the rotation of the pot being small. In this case, vj and PW are very small, and hence, the value of Vs is also very small. Cascading-type motion does occur when v reaches a critical value, as can be seen from Eq. (8), owing to there being equilibrium between the centrifugal forces acting on the balls because of the rotation of the pot and the revolution of the disk. The motion changes from the cascading type to the cataracting type as v increases further. Vs peaks at 39.5 mL, indicating that most of the PW is absorbed by the NiO/Fe2O3 powder and that the particle size is smaller when cascading-type motion occurs and eventually changes into cataracting-type motion. Eventually, the motion shifts from the cataracting type into the rolling type when v increases beyond the critical value. As mentioned previously, rolling-type motion is ineffective for grinding, as it results in a lower number of collisions of the individual balls and leads to collisions against the mill wall. The value of vj decreases as the rolling speed increases, and PW is mostly determined by PW,n. Further, Vs also decreases with an increase in the rolling speed.
It can be seen from Fig. 4 that PW,n increases with an increase in v, reaching a peak value of 7.5 mJ/s. Subsequently, its value falls. Cascading-type motion does not occur when v<300.9 r/min. As both vj and PW are very small, so is the value of PW,n. However, cascading-type motion takes place when v ≥ 300.9 r/min in Eq. (8). More of PW is absorbed by the NiO/Fe2O3 powder, and the particle size is smaller when cascading-type motion occurs. Hence, PW,n increases slightly. Then, the motion shifts from the cataracting type to the rolling type when v>> 300.9 r/min. The value of vj decreases as the extent of rolling increases, and PW is determined mostly by PW,n. Hence, the value of PW,n is extremely large. It is interesting to note that the value of Vs peaks at 39.5 mL when PW,n reaches a low point, and Vs reaches the lowest value when PW,n reaches its peak, which is 7.5 mJ/s. The above-described phenomena suggest that the grinding efficiency increases with a decrease in the degree of noisy-power dissipation.
Fig. 4 Relationship among rotation-to-revolution speed, Vs, and PW,s
3.4 Analysis of Vs and PW,n for different powder-filling ratios
Figure 5 reveals that both Vs and PW,n decrease with an increase in the powder-filling ratio when the other parameters listed in Table 3 remain unchanged. This phenomenon can be explained by Eqs. (6) and (8). With an increase in the powder-filling ratio (i.e., with an increase in W in Eqs. (6) and (8)), the powders completely cover the container walls and the milling balls. This leads to a decrease in the collision frequency (n) and vj. Thus, PW and PW,n decrease in Eqs. (6) and (8). Cascading-type motion does not occur as the powder-filling ratio is increased. On the other hand, it does occur when the powder-filling ratio is decreased. Figure 5 shows that the volume of the suspension is the highest when the powder-filling ratio is 5.44%; however, it is suggested that the powder-filling ratio is set to be ~10.88% in order to reduce the friction and wear.
Fig. 5 Relationship among powder-filling ratio, Vs, and PW,n
Figure 6 shows the volume of the suspension for different number ratios of the balls with diameters of 10 and 20 mm; the power-filling ratio remains the same. The number ratios are 5 and 18, respectively, for curves 1 and 2 in Fig. 6. Figure 6 also shows that Vs increases with an increase in the number ratio and that Vs decreases with an increase in the powder-filling ratio. When the powder-filling ratio is increased (i.e., W in Eqs. (6) and (8) is increased), the powder completely covers the container walls and the balls, leading to a lower collision frequency (n) and vj. As a result, PW in Eqs. (6) and (8) decreases. Figure 6 also suggests that Vs increases with an increase in the number ratio. Both n and vj increase with an increase in the ball number ratio in Eqs. (6) and (8). This causes PW,m to increase. Further, Vs increases with the increase in PW,m. Finally, Fig. 5 also shows that the volume of the suspension is the maximum when the powder-filling ratio is 5.44%; however, as noted previously, it is suggested that the powder-filling ratio is set to be ~10.88% in order to reduce the friction and wear.
Fig. 6 Relationship between powder-filling ratio and Vs
3.5 Analysis of Vs and PW,n for different ball-filling ratios
Figure 7 shows the plots of the experimental values of Vs and PW,n as functions of the ball-filling ratio while the other parameters listed in Table 3 were kept constant. It can be seen from the figure that Vs reaches a maximum value of 44 mL when the ball-filling ratio is 20.53%-23.88%, at which PW,n is 0.4-0.7 mJ/s. Subsequently, the value of Vs decreases. The value of PW,n increases slowly when the ball-filling ratio is smaller than 20.53%. However, it increases significantly when the ball-filling ratio is greater than 23.88%.
Fig. 7 Relationship among ball-filling ratio, Vs, and PW,n
This phenomenon can be explained by Eqs. (5), (6), and (8). It was assumed that W remained constant in this experiment. Initially, the excess NiO/Fe2O3 slurry that covered the container walls and the milling balls leads to lowering of the collision frequency (n) and vj in Eqs. (6) and (8). The μ in Eq. (5) is also very large, while v is very small, owing to the centrifugal force being small. Hence, Vs increases with an increase in the ball-filling ratio. Further, PW,n increases slowly with an increase in Vs. Therefore, the collision frequency (n) and vj in Eqs. (6) and (8) increase with an increase in the ball- filling ratio (i.e., M increases in Eqs. (6) and (8)), because the extent to which the NiO/Fe2O3 slurry covers the container walls and the balls decreases. As result, μ, R, and ω also decrease in Eq. (5). Cascading-type motion occurs and shifts to the cataracting type with an increase in the ball-filling ratio when the term on the left-hand side in Eq. (5) is smaller than the term on the right-hand size. Thus, the value of PW,m increases in Eqs. (6) and (8), and Vs increases with an increase in PW,m. However, cascading-type motion does not occur when the ball-filling ratio is increased further. This is owing to the fact that the container walls and the balls are no longer covered by the NiO/Fe2O3 slurry and because when the number of balls is high, it leads to lowering of the collision frequency (n) and vj in Eqs. (6) and (8), while the volume of the mill pot remains constant. The value of mg in Eq. (5) is also very large.
It can be seen from Fig. 7 that PW,n increases sharply when the ball-filling ratio ≥ 23.88%. The dashed line is the nonlinear fitting line that represents the relationship between PW,n and the ball-filling ratio, J, in Fig. 7. The relationship between PW,n and J can be described empirically by Eq. (9), where the values of the empirical constants, P0W,n, A, and K are 5.59×10-5, 3.48×10-6 and -4.23, respectively, within the experimental range. These values were obtained using the least squares method. By analyzing the experimental results, the constants P0W,n, A, and K could be explained as follows: noisy-power dissipation during planetary balling mill operation without loading, per-exponential factors, ball grinding media factors which depend on the material, respectively. The R and R2 values for Eq. (9) were 99.4% and 98.1%, respectively.
(9)
where K is the ball grinding media factor which depends on the material.
On the basis of the above-described results, it can be surmised that the volume of the suspension increases with a decrease in the extent of noisy-power dissipation. Thus, it can be assumed that the efficiency of planetary ball milling would decrease when the extent of noisy-power dissipation exceeds a specific value, which is determined by Eq. (9). Therefore, Eq. (9) is useful for determining the efficiency of planetary ball milling.
3.6 Analysis of Vs and PW,n for different grinding time
Figure 8 shows that PW,n,t, which is the product of PW,n and the grinding time, increases with the grinding time as the other milling parameters, listed in Table 3, remain constant. However, Vs reaches a maximum value of 30 mL and subsequently decreases with an increase in the grinding time, as shown in Fig. 8. This is because the powder grain size is large for grinding time less than 6 h, and the finer powder particles agglomerate when the grinding time is more than 6 h. Thus, the NiO/Fe2O3 powder should be ground for ~6 h.
Fig. 8 Relationship among grinding time, Vs, and PW,n
3.7 Analysis of specific surface area of ground powder
Table 4 lists the specific surface area distribution corresponding to milling conditions A to E, that is, for the optimum rotation-to-revolution speed (A), slurry water content (B), ball-filling ratio (C), powder-filling ratio (D), and grinding time (E). It can be seen from the table that the specific surface area of the NiO/Fe2O3 powder increases as the milling conditions are improved, resulting in a smaller mean particle size.
Table 4 Distribution of specific surface area of powder and corresponding mean particle size
4 Conclusions
1) The effects of various grinding parameters on the characteristics of a NiO/Fe2O3 powder were studied using a planetary ball mill. The relationship between the noisy-power dissipation and the grinding parameters was also investigated. The DEM was employed to explain the obtained results. It was found that the optimum grinding parameters were as follows: a slurry water content of 64.1%-85.47%; a number ratio of balls with diameters of 10 and 20 mm of 360/20; a rotation-to-revolution speed ratio of 300.9 r/min; a powder-filling ratio of approximately 10.88%; a ball-filling ratio of 20.53%- 23.88%; and a grinding time of approximately 6 h.
2) It was found that the mean particle size of the ground powder increased with an increase in the extent of noisy-power dissipation owing to collisions, while the milling efficiency and the degree of utilization of the specific impact energy decreased. The relationship between the extent of noisy-power dissipation and the ball-filling ratio was determined using the nonlinear fitting method.
3) The findings of this study should help to improve the efficiency of ball mill grinding of various materials.
Acknowledgements
This work was supported by the Inert Anode Material Production and Application in Electrolytic Production of Aluminium program of the Yunnan Aluminium Yonxin Aluminium Co. Ltd.
References
[1] KENIRY J. The economics of inert anodes and wettable cathodes for aluminum reduction cells [J]. JOM, 2001, 53(5): 37-43.
[2] de NORA V. Aluminium electrowinning—The future [J]. Aluminium, 2000, 76(12): 998-999.
[3] KVANDEK H. Inert electrodes in aluminium electrolysis cells [C]// ECKERT C E. Light Metals. California: TMS, 1999: 369-376.
[4] HRYN J N, SADOWAY D R. Cell testing of metal anodes for the aluminium electrolysis [C]//DAS S K. Light Metals. Colorado: TMS, 1993: 475-483.
[5] YANG Jian-hong, LIU Ye-xiang, WANG Hua-zhang. The behaviour and improvement of SnO2-based inert anodes in aluminium electrolysis [C]//DASSK. Light Metals. Colorado: TMS, 1993: 493-495.
[6] OLSEN E, NICKEL J. Nickel ferrite as inert anodes in aluminium electrolysis: Part I. Material fabrication and preliminary testing [J]. Journal of Applied Electrochemistry, 1999, 29: 293-299.
[7] LAI Yan-qing, HUANG Li-feng, TIAN Zhong-liang, WANG Jia-wei, ZHANG Gang, ZHANG Yong. Effect of CaO doping on corrosion resistance of Cu/(NiFe2O4-10NiO) cermet inert anode for aluminum electrolysis [J]. Journal of Central South University of Technology, 2008, 15(6): 743-747.
[8] DU Jin-jing , LIU Yi-han, YAO Guang-chun, ZHANG Zhi-gang. Effect of MnO2 addition on sintering properties of 18NiO-NiFe2O4 composite ceramics: Preliminary results [J]. Journal of Materials Engineering and Performance, 2012, 21(9): 1998-2001.
[9] LAI Yan-qing, TIAN Zhong-liang, QIN Qing-wei, ZHANG Gang, LI Jie. Solubility of complex oxide ceramic in Na3AlF6-Al2O3 melt [J]. Journal of Central South University: Nature Science, 2003, 34(3): 245-248. (in Chinese)
[10] ROSENKRANZ S, BREITUNG-FAES S, KWADE A. Experimental investigations and modelling of the ball motion in planetary ball mills [J]. Powder Technology, 2011, 212(1): 224-230.
[11] LAI Yan-qing, LI Jie, TIAN Zhong-liang, ZHANG Gang, LIU Ye-xiang. An improved pyroconductivity test of spinel-containing cermet inert anodes in aluminum electrolysis cells [C]//Light Metals. Charlotte, North Carolina: TMS (The Minerals, Metals & Materials Society), 2004: 339-344.
[12] MIO H, KANO J, SAITO F, KANEKO K. Optimum revolution and rotational directions and their speeds in planetary ball milling [J]. International Journal of Mineral Processing, 2004, 74: S85-S92.
[13] MIO H, KANO J, SAITO F. Scale-up method of planetary ball mill [J]. Chemical Engineering Science, 2004, 59(24): 5909-5916.
[14] ASHRAFIAFIZADEH H, ASHRAFIAFIZADEH M. Influence of processing parameters on grinding mechanism in planetary mill by employing discrete element method [J]. Advanced Powder Technology, 2012, 23(6): 708-716.
[15] SATO A, KANO J, SAITO F. Analysis of abrasion mechanism of grinding media in a planetary mill with DEM simulation [J]. Advanced Powder Technology, 2010, 21(2): 212-216.
[16] MORI H, MIO H, KANO J, SAITO F. Ball mill simulation in wet grinding using a tumbling mill and its correlation to grinding rate [J]. Powder Technology, 2004, 143-144: 230-239.
[17] ODA M, IWASHITA K. Study on couple stress and shear band development in granular media based on numerical simulation analyses original research article [J]. International Journal of Engineering Science, 2000, 38: 1713-1740.
[18] CHOI W S, CHUNG H Y, YOON B R, KIM S S. Applications of grinding kinetics analysis to fine grinding characteristics of some inorganic materials using a composite grinding media by planetary ball mill [J]. Powder Technology, 2001, 115: 209-214.
[19] JIANG M J, YU H S, HARRIS D. A novel discrete model for granular material incorporating rolling resistance [J]. Computers and Geotechnics, 2005, 32(5): 340-357.
[20] KANO J, MIYAZAKI M, SAITO F. Ball mill simulation and powder characteristics of ground talc in various types of mill [J]. Advanced Powder Technology, 2000, 11(3): 333-342.
[21] IWASHITA K, ODA M. Micro-deformation mechanism of shear banding process based on modified distinct element method [J]. Powder Technology, 2000, 109: 192-205.
[22] GUDIN D, KANO J, SAITO F. Effect of the friction coefficient in the discrete element method simulation on media motion in a wet bead mill [J]. Advanced Powder Technology, 2007, 18(5) : 555-565.
NiO/Fe2O3湿式行星球磨中的噪声能消耗与效率
姚 云1，谢 刚1,2，侯彦青1，李荣兴1，罗伟红1，彭如振1，于站良2
1. 昆明理工大学 冶金与能源学院，昆明 650093；2. 昆明冶金研究院，昆明 650031
摘 要：研究NiO/Fe2O3湿式混合与球磨过程中的噪声能消耗、球磨效率及二者之间的关系。结果表明，球磨工艺的最佳工艺参数为：填水率64.10%~85.47%，小/大球个数比360/20，球磨机转速300.9 r/min，填粉率约10.88%，填球率20.53%~23.88%，球磨时间6 h。引入离散元法(DEM)分析球磨过程中噪声能消耗与球磨效率之间的关系，得到噪声能消耗与填球率关系的经验方程。研究表明粉体的平均粒度随着噪声能的消耗而减小，而球磨效率和球碰撞能的利用率则随着噪声能消耗的增加而减小。
关键词：噪声能消耗；NiO/Fe2O3粉体；行星式球磨；平均粒度
(Edited by Xiang-qun LI)
Corresponding author: Yun YAO; Tel: +86-13529373085; E-mail: yyaoun1982@aliyun.com
DOI: 10.1016/S1003-6326(14)63400-2
Abstract: The relationship between the efficiency of NiO/Fe2O3 wet grinding and noisy-power dissipation was studied. The optimal grinding parameters were found as: a slurry water content of 64.10%-85.47%, ball number ratio of 360/20, revolution speed of 300.9 r/min, powder-filling ratio of 10.88%, ball-filling ratio of 20.53%-23.88%, and grinding time of approximately 6 h. The discrete element method (DEM) was employed to analyze relationship between the noisy-power dissipation and the grinding efficiency, and equations describing the relationship were derived. The mean particle size of the ground powder decreased with a decrease in the degree of noisy-power dissipation, while the grinding efficiency and the amount of specific impact power used decreased with an increase in the degree of noisy-power dissipation.