J. Cent. South Univ. (2013) 20: 1151-1155

DOI: 10.1007/s11771-013-1597-5

Preparation and effects of W-doping on electrochemical properties of spinel Li₄Ti₅O₁₂ as anode material for lithium ion battery

ZHANG Xin-long(张新龙), HU Guo-rong(胡国荣), PENG Zhong-dong(彭忠东)

School of Metallurgical Science and Engineering, Central South University, Changsha 410083, China

Central South University Press and Springer-Verlag Berlin Heidelberg 2013

Abstract:

W-doped Li₄Ti₅O₁₂ in the form of Li₄Ti_4.95W_0.05O₁₂ was firstly synthesized via solid state reaction. X-ray diffraction (XRD) and scanning electron microscope (SEM) were employed to characterize the structure and morphology of Li₄Ti_4.95W_0.05O₁₂. W-doping does not change the phase composition and particle morphology, while remarkably improves its cycling stability at high charge/discharge rate. Li₄Ti_4.95W_0.05O₁₂ exhibits an excellent rate capability with a reversible capacity of 131.2 mA·h/g at 10C and even 118.6 mA·h/g at 20C. The substitution of W for Ti site can enhance the electronic conductivity of Li₄Ti₅O₁₂ via the generation of mixing Ti⁴⁺/Ti³⁺, which indicates that Li₄Ti_4.95W_0.05O₁₂ is promising as a high rate anode for the lithium-ion batteries.

Key words:

lithium-ion battery; lithium titanate; anode material; doping；

1 Introduction

The ever-growing demand for portable batteries with high energy density is exerting pressure for the development of advanced lithium-ion batteries. For large-scale applications such as electric and hybrid vehicle systems, the vital issue is the availability of advanced materials. In recent years, there has been considerable effort devoted to developing high energy density, safe and reliable new materials to use as the anodes in lithium-ion batteries [1]. The spinel Li₄Ti₅O₁₂ has been found to be an attractive anode material for lithium ion battery [2-3]. In the lithium titanate spinel- type structure of Li₄Ti₅O₁₂, the formal valence of titanium is +4, which is the highest achievable oxidation state possible for titanium. This Li₄Ti₅O₁₂ material has been found to intercalate lithium ions without strain or shrinkage to the lattice. It has a flat Li insertion potential at about 1.55 V (versus Li⁺/Li), above the reduction potential of common electrolyte solvents, mitigating the formation of solid-electrolyte interface (SEI) and avoiding formation of lithium dendrites making the battery safer. However, several disadvantages exist compared to graphite. These include the poor electric conductivity that limits its full capacity at high charge/ discharge rates.

In the literature, effort has been expended to improve the conductivity. Several methods were proposed: 1) doping Li₄Ti₅O₁₂ by other metal cations or non-metal ions in Li, Ti or O sites [4-9]; 2) incorporating a second phase with high electronic conductivity such as carbon and metal powder [10-15]; 3) making a nitridation to form oxynitride species on its surface [16]. However, to our best knowledge, there are less investigations on the electrochemical characteristics of W-doped Li₄Ti₅O₁₂ as an anode material. In this work, we proposed to partially substitute Ti⁴⁺ with W⁶⁺, which will cause a transition of a certain amount of Ti⁴⁺ to Ti³⁺ as charge compensation. The transition from Ti⁴⁺ to Ti³⁺ in Li₄Ti₅O₁₂ will lead to an increase in the electronic conductivity and thus improve the rate performance.

2 Experimental

2.1 Materials preparation

Li₄Ti₅O₁₂ samples were prepared using a solid-state method from TiO₂ (anatase structure) and LiOH·H₂O. The W doped Li₄Ti₅O₁₂ was also prepared using a solid-state method with TiO₂ (anatase structure), LiOH·H₂O and WO₃. In both cases, 2% (mass fraction) excessive LiOH·H₂O was used to compensate for lithium volatilization during the high temperature heating. A 1% W doping level was selected, which yields the composition of Li₄Ti_4.95W_0.05O₁₂ assuming that W sits on a Ti site. This is probably a good assumption that the ionic radius of W⁶⁺ was 0.060 nm, similar with the ionic radius of Ti⁴⁺ (0.061 nm) and much smaller than the ionic radius of Li⁺ (0.076 nm). Powders of the precursor materials were mixed in a mortar and pestle with enough methanol to form slurry. The undoped mixed reactant mixture was heated at 800 °C for 5 h in air (oxidizing) and the W-doped mixed reactant mixture was heated at 800 °C for 5 h in 3% (volume fraction) H₂/Ar (reducing) to obtain the final powders.

2.2 Characterization

The crystal structure of the powders was characterized by X-ray diffraction (XRD, Rigaka DMax- RB) using Cu K_α radiation (10°≤2θ≤90°). Scanning electron microscope (SEM, KYKY2800) was used to study the morphology of the materials.

2.3 Electrochemical tests

The electrochemical cycling performances of the Li₄Ti₅O₁₂ powders were evaluated at room temperature (20 °C) with laboratory-scale Li/Li₄Ti₅O₁₂ button cells including a lithium metal foil as counter electrode, and a composite of 80% (mass fraction) Li₄Ti₅O₁₂, 10% acetylene black (AB), and 10% polytetrofluornethelene (PTFE) binder as a cathode. A micro-porous polypropylene film (Celgard 2400) was used as a separator and 1 mol/L LiPF6 solution with the 1:1 volumetric ratio of ethylene carbonate-dimethyl carbonate (EC-DMC) was used as the electrolyte. All cells were assembled inside a glove box filled with ultra-pure argon. Charge/discharge characteristics of the cells were recorded in the potential range of 1.0-3.0 V using a LAND batteries test system (CT2001A, Jinnuo Electronics Co., Ltd., Wuhan, China) and specific capacities were calculated based on the mass of Li₄Ti₅O₁₂. Electrochemical impedance spectroscopy (EIS) was also measured using a potentiostat/galvanostat EG&G 273A coupled to a frequency response analyzer (FRA) EG&G 1025. The impedance data were obtained between 1 MHz and 10 mHz at 5 mV as the applied sinusoidal perturbation. Electrical resistance measurement of the sintered and polished pellets of Li₄Ti₅O₁₂ was also performed at electrochemical workstation above.

3 Results and discussion

The color of the synthesized Li₄Ti₅O₁₂ powder is white. The X-ray diffraction patterns of the Li₄Ti₅O₁₂ and Li₄Ti_4.95W_0.05O₁₂ are shown in Fig. 1(a). All the sharp diffraction peaks can be attributed to the cubic spinel structure of Li₄Ti₅O₁₂ without obvious impurity phase, which indicates that W⁶⁺ has successfully entered the lattice of the spinel and does not change its structural characteristics. The XRD pattern reveals that the (111) peak of the Li₄Ti_4.95W_0.05O₁₂ shifts to smaller angels.For a clear observation, the peak position variation of (111) plane is magnified and shown in Fig. 1(b). The XRD refinement according to the Rietveld method indicates that the lattice parameter of the Li₄Ti_4.95W_0.05O₁₂ is 8.366 ? and the lattice parameter of the Li₄Ti₅O₁₂ is 8.361 ?. The doping of W will cause the lattice constant of the parameter become larger. This may be due to the fact that the substitution of W⁶⁺ for Ti⁴⁺ site will cause the transition of a certain amount of Ti⁴⁺ to Ti³⁺ as charge compensation [8], which will cause the increase of the lattice constant of the Li₄Ti₅O₁₂ because Ti³⁺ (0.067 nm) is larger than Ti⁴⁺ (0.061 nm).

Fig. 1 XRD patterns of Li₄Ti₅O₁₂ and Li₄Ti_4.95W_0.05O₁₂ (a) and magnified (111) peaks of Li₄Ti₅O₁₂ and Li₄Ti_4.95W_0.05O₁₂ (b)

Figure 2 shows the SEM images of the undoped Li₄Ti₅O₁₂ powder and the W-doped powder. The grains of pure Li₄Ti₅O₁₂ are small with the size generally distributed in the range of 200-300 nm. Small particles will enlarge the contact areas between particles and electrolyte, and thus improve the specific capacity of the electrode. In Fig. 2(b), the particle size of the W-doped powder is larger than that of the pure one, but is also several hundred nanometers.

The acquisition of these homogeneous, nano-sized Li₄Ti₅O₁₂ powders could be attributed to the precursor material, nano-sized anatase structure TiO₂, which could be mixed more sufficiently with the other materials compared to the usually used micro-sized rutile structure TiO₂. The sintering time in this work is much shorter than the ordinarily reported 10-15 h. Short sintering time is also critical to prevent the grains from excessive growth.

Fig. 2 SEM images of Li₄Ti₅O₁₂ (a) and Li₄Ti_4.95W_0.05O₁₂ (b)

The electrochemical properties of the powders are determined by charge/discharge test at constant current density. Figure 3 shows the first and second charge-discharge curves of the undoped and W-doped Li₄Ti₅O₁₂ powder at 0.5C rate in potential window between 3.0 and 1.0 V. The cycling behavior is typical of LTO with a flat plateau at an average potential of 1.55 V which is attributed to a two-phase phenomenon pertaining to Li₄Ti₅O₁₂ and Li₇Ti₅O₁₂ phases. The voltage platform is the result of an adjustment of the above intercalation and deintercalation processes. The sharp and linear increases of the voltage at the end of the charge and the start of the discharge curves are results of electrode polarization. The cation distribution in Li₄Ti₅O₁₂ and Li₇Ti₅O₁₂ phases during electrochemical charge/discharge processes can be written as follows:

[Li]_8a[Li_1/3Ti_5/3]_16d[O₄]_32e+Li⁺+e^-=

[Li₂]_16c[Li_1/3Ti_5/3]_16d[O₄]_32e                   (1)

During the first discharge, undoped Li₄Ti₅O₁₂ takes about 2.79 Li atoms corresponding to a capacity of 162.4 mA·h/g that matches well with the expected theoretical capacity for Li₄Ti₅O₁₂. However, the W-doped Li₄Ti₅O₁₂ takes about 2.66 Li atoms corresponding to a capacity of 154.5 mA·h/g less than that of the undoped one. A small electrode polarization of about 0.02 V is observed between charge-discharge curves, indicating the existence of good interparticle electrical contacts and better ion transport. In Li₄Ti₅O₁₂ structure, 75% Li⁺ ions locate at tetrahedral 8a sites, 25% Li⁺ and Ti⁴⁺ are randomly distributed at octahedral 16d sites, O^2- ions occupy the 32e sites, and the 8b, 48f and 16c sites are empty [2]. During lithiation process, 3 Li-ions can be accommodated by Li₄Ti₅O₁₂, which will make spinel Li₄Ti₅O₁₂ transform to rock-salt Li₇Ti₅O₁₂. In this process, all Li-ions, including that in 8a site and the newly inserted, will move and occupy the 16c site, and then all octahedral sites are filled. W-doping may impede the transportation of Li-ions from 8a to 16c sites, and thus influence the insertion of outside Li-ions into Li₄Ti₅O₁₂ structure. As a result, the capacity of W-doped Li₄Ti₅O₁₂ is decreased.

Fig. 3 Initial discharge-charge curves of Li₄Ti₅O₁₂ and Li₄Ti_4.95W_0.05O₁₂ at 0.5C rate

High rate performance is one of the most important electrochemical characteristics of lithium ion batteries for HEV application. The charge/discharge capacity of pure Li₄Ti₅O₁₂ and W-doped Li₄Ti₅O₁₂ electrodes at different current rates from 0.5C to 20C are shown in Fig. 4. It can be seen that, the rate performance of Li₄Ti₅O₁₂ can be improved by the doping of W. The charge and discharge capacities decrease with the current rate increasing. The Li₄Ti_4.95W_0.05O₁₂ exhibits an excellent rate capability compared with the Li₄Ti₅O₁₂, although Li₄Ti₅O₁₂ shows much more initial capacity than Li₄Ti_4.95W_0.05O₁₂. At 0.5C, the Li₄Ti_4.95W_0.05O₁₂ presents a discharge capacity of 154.5 mA·h/g, while the Li₄Ti₅O₁₂ exhibits a discharge capacity of 162.4 mA·h/g. At 20C, the discharge capacity of the Li₄Ti_4.95W_0.05O₁₂ still remains 118.6 mA·h/g, while the capacity of the undoped Li₄Ti₅O₁₂ is only 69.2 mA·h/g. We propose to partially substitute Ti⁴⁺ with W⁶⁺, which will cause a transition of a certain amount of Ti⁴⁺ to Ti³⁺ as charge compensation. The transition from Ti⁴⁺ to Ti³⁺ in Li₄Ti₅O₁₂ will lead to an increase in the electronic conductivity and thus improve the rate performance.

The cycling performances of the W-doped and undoped Li₄Ti₅O₁₂ samples at the rate of 1C are exhibited in Fig. 5. As is seen Fig. 5, more than 10.7% of the capacity loss occurs in the undoped Li₄Ti₅O₁₂ at 1C after 100 cycles, while the W-doped Li₄Ti₅O₁₂ loses only 2.5% after 100 cycles. The 100th discharge capacity of the W-doped Li₄Ti₅O₁₂ electrode is 150.4 mA·h/g, but the corresponding value of the Li₄Ti₅O₁₂ electrode is decreased to 144.6 mA·h/g. This indicates that the introduction of W ions can increase the cycle stability. This suggests that the electrode polarization is probably decreased by W-doping.

Fig. 4 Initial discharge-charge curves of Li₄Ti₅O₁₂ (a) and Li₄Ti_4.95W_0.05O₁₂ (b) at different rates (0.5C, 1C, 5C, 10C, 20C)

Fig. 5 Cycling performance of Li₄Ti₅O₁₂ and Li₄Ti_4.95W_0.05O₁₂ samples (current rate, 1C)

Electrochemical impedance spectroscopy (EIS) may be considered as one of the most sensitive tools for studying the changes in the electrode behavior due to surface modification. EIS results of the coin cells with the Li₄Ti₅O₁₂ and W-doped Li₄Ti₅O₁₂ cathodes are shown in Fig. 6. The measurement is carried out after the cells have been discharged to the depth of 50% followed by three cycles. The impedance spectra are composed of one semicircle at higher frequencies followed by linear part at lower frequency end. The semicircle in the high region represents the migration of the lithium ions at the electrode/electrolyte interface. The low frequency region of the straight line is attributed to the diffusion of the lithium ions into the bulk of the electrode material, the so-called Warburg diffusion [8].

Fig. 6 EIS of Li₄Ti₅O₁₂ and Li₄Ti_4.95W_0.05O₁₂ samples

The relationship between the imaginary impedance and the low frequencies is governed by Eq. (2). The diffusion coefficient values of the lithium ions in the bulk electrode materials are calculated by Eq. (3). The Warburg impedance coefficient can be obtained from the straight lines [7]. The relation is governed by Eq. (4). These calculated results are recorded in Table 1.

Z″=-σ_wω^-1/2                                 (2)

D=0.5²                                      (3)

Z_re=R_e+R_ct+σ_wω^-1/2                       (4)

where Z″ is the imaginary impedance, ω is the angular frequency in the low frequency region, R_ct is the charge-transfer resistance, R_e is the electrolyte resistance, D is the diffusion coefficient.

The obtained diffusion coefficients show that W-doped Li₄Ti₅O₁₂ sample has higher mobility for Li⁺ diffusion than the undoped Li₄Ti₅O₁₂ sample. This is attributed to the concentration of electrons caused by the transition of a certain amount of Ti⁴⁺ to Ti³⁺ as charge compensation. The transition from Ti⁴⁺ to Ti³⁺ in Li₄Ti₅O₁₂ will lead to an increase in the electronic conductivity and thus improve the rate performance.

Table 1 Impedance parameters of undoped Li₄Ti₅O₁₂ and Li₄Ti_4.95W_0.05O₁₂ samples

4 Conclusions

1) Li₄Ti_4.95W_0.05O₁₂ powders have been successfully synthesized by a simple solid state reaction. XRD patterns show that the Li₄Ti_4.95W_0.05O₁₂ has good crystallinity and high phase purity. The Li₄Ti_4.95W_0.05O₁₂ electrode presents better cycling performance than the Li₄Ti₅O₁₂ electrode prepared by the similar process. W-doping does not change the phase composition and particle morphology, while remarkably improves its cycling stability at high charge/discharge rate.

2) The substitution of W for Ti site can enhance the electronic conductivity of Li₄Ti₅O₁₂ via the generation of mixing Ti⁴⁺/Ti³⁺. At 20C, the discharge capacity of the Li₄Ti_4.95W_0.05O₁₂ still remains 118.6 mA·h/g, while the capacity of the undoped Li₄Ti₅O₁₂ is only 69.2 mA·h/g. More than 10.7% of the capacity loss occurs in the undoped Li₄Ti₅O₁₂ at 1C after 100 cycles, while the W-doped Li₄Ti₅O₁₂ loses only 2.5% after 100 cycles. The 100th discharge capacity of the W-doped Li₄Ti₅O₁₂ electrode is 150.4 mA·h/g, but the corresponding value of the Li₄Ti₅O₁₂ electrode is decreased to 144.6 mA·h/g.

References

[1] TARASCON J M, ARMAND M. Issues and challenges facing rechargeable lithium batteries [J].Nature, 2001, 414(15): 359-367.

[2] OHZUKU T, UEDA A, YAMAMOTO N. Zero-strain insertion material of Li[Li_1/3Ti_5/3Ti_5/3]O₄ for rechargeable lithium cells [J]. Journal of the Electrochemical Society, 1995, 142(5): 1431-1435.

[3] ARIYOSHI K, YAMATO R, OHZUKU T.Zero-strain insertion mechanism of Li[Li_1/3Ti_5/3]O₄ for advanced lithium-ion (shuttlecock) batteries [J]. Electrochim Acta, 2005, 51(6): 1125-1129.

[4] MARTLN P, LOPEZ M L, PICO C, VEIGA M L. Li_(4-x)/3Ti_(5-2x)/3Cr_xO₄ (0≤x≤0.9) spinels: New negatives for lithium batteries [J]. Solid State Sci, 2007, 9(6): 521-526.

[5] HAO Y J, LAI Q Y, LU J Z, JI X Y. Effects of dopant on the electrochemical properties of Li₄Ti₅O₁₂ anode materials [J]. Ionics, 2007, 13(5): 369-373.

[6] HUANG S, WEN Z, ZHU X, LIN Z. Effects of dopant on the electrochemical performance of Li₄Ti₅O₁₂ as electrode material for lithium ion batteries [J]. J Power Sources, 2007, 165(1): 408-412.

[7] LI X, QU M, YU Z. Structural and electrochemical performances of Li₄Ti_5-xZr_xO₁₂ as anode material for lithium-ion batteries [J]. J Alloys Compd, 2009, 487(1/2): L12-L17.

[8] ZHONG Z. Synthesis of Mo⁴⁺ substituted spinel Li₄Ti_5-xMo_xO₁₂ [J]. Electrochem Solid-State Lett, 2007, 10(12): A267-A269.

[9] ALLEN J L, JOW T R, WOLFENSTINE J. Low temperature performance of nanophase Li₄Ti₅O₁₂ [J]. J Power Sources, 2006, 159(2): 1340-1345.

[10] HUANG S, WEN Z, ZHANG J, GU Z, XU X. Preparation and electrochemical performance of Ag doped Li₄Ti₅O₁₂ [J]. Solid State Ionics, 2006, 177(15): 851-855.

[11] GAO J, YING J, JIANG C, WAN C. Preparation and characteristic of carbon-coated Li₄Ti₅O₁₂ anode material [J]. J Power Sources, 2007, 166(2): 255-259.

[12] YANG L, GAO L. High-density spherical Li₄Ti₅O₁₂/C anode material with good rate capability for lithium ion batteries [J]. J Alloys Compd, 2009, 485(3): 93-97.

[13] CHENG L, YAN J, ZHU G N, LUO J Y, WANG C X, XIA Y Y. General synthesis of carbon-coated nanostructure Li₄Ti₅O₁₂ as a high rate electrode material for Li-ion intercalation [J]. J Mater Chem, 2010, 20(3): 595-602.

[14] WANG Y, LIU H, WANG K, EIJI H, WANG Y, ZHOU H. Synthesis and electrochemical performance of nano-sized Li₄Ti₅O₁₂ with double surface modification of Ti(III) and carbon [J]. J Mater Chem, 2009, 19(37): 6789-6785.

[15] KAVAN L, DUNSCH L, KATAURA H. Electrochemical tuning of electronic structure of carbon nanotubes and fullerene peapods [J]. Carbon, 2004, 42(5): 1011-1019.

[16] PARK K S, BENAYAR A, KANG D J, DOO S G. Nitridation-driven conductive Li₄Ti₅O₁₂for lithium ion batteries [J]. J Am Chem Soc, 2008, 130(45): 14930-14931.

(Edited by HE Yun-bin)

Received date: 2012-10-26; Accepted date: 2013-03-08

Corresponding author: HU Guo-rong, PhD; Tel: +86-13908482734; E-mail: hgrhsj@263.net

Abstract: W-doped Li₄Ti₅O₁₂ in the form of Li₄Ti_4.95W_0.05O₁₂ was firstly synthesized via solid state reaction. X-ray diffraction (XRD) and scanning electron microscope (SEM) were employed to characterize the structure and morphology of Li₄Ti_4.95W_0.05O₁₂. W-doping does not change the phase composition and particle morphology, while remarkably improves its cycling stability at high charge/discharge rate. Li₄Ti_4.95W_0.05O₁₂ exhibits an excellent rate capability with a reversible capacity of 131.2 mA·h/g at 10C and even 118.6 mA·h/g at 20C. The substitution of W for Ti site can enhance the electronic conductivity of Li₄Ti₅O₁₂ via the generation of mixing Ti⁴⁺/Ti³⁺, which indicates that Li₄Ti_4.95W_0.05O₁₂ is promising as a high rate anode for the lithium-ion batteries.