共搜索到60条信息,每页显示10条信息,共6页。用时:0小时0分0秒249毫秒
AB INITIO CALCULATION OF THE ELASTIC AND OPTICAL PROPERTIES OF AL3SC COMPOUND D.H. Xiao1,M. Song1 (1.State Key Laboratory of Powder Metallurgy, Central South University,Changsha 410083, China... of the Al3Sc compound. The optical property calculations show that a strong absorptivepeak exists from 0-15eV and a relative small absorptive peak exists around 30eV. The form iscaused by the optical......
, China) Abstract:Minor addition of Sc to aluminum results in the rapid precipitation of homogeneously distributed Al3Sc dispersoids. The presence of Al3Sc dispersoids is more effective recrystallization inhibitors. Our work established the precipitation of homogeneously distributed Al3Sc dispersoids, which are coherent with the matrix, have the L12 structure. It was also established......
微量Sc在Al-Mg合金中的作用 潘青林1,邹景霞1,张传福1,尹志民1,陈显明1 (1.中南大学材料科学与工程系,长沙,410083) 摘要:研究了微量Sc对Al-Mg合金显微组织与拉伸性能的影响.结果表明,微量Sc在Al-Mg合金中主要以初生Al3Sc和次生Al3Sc两种形式存在.初生Al3Sc是合金在凝固过程中形成的,可成为有效的非均质晶核,大大细化合金的铸态晶粒.次生Al3Sc是合金铸锭在工艺加热过程中析出的,有效地钉扎位错和亚晶界,稳定亚结构并强烈抑制合金的再结晶,具有亚结构强化和直接析出强化作用.因此,加入Sc后的Al-Mg合金的强度大大提高,并且表现出良好的强塑性配合. 关键词:Al-Mg-Sc合金; Al3Sc; 显微组织; 力学性能; [全文内容正在添加中] ......
Al-Mg-Sc合金的原子键强与力学性能 吴伟明1,刘慧1,高英俊1,班冬梅1,黄创高1 (1.广西大学物理科学与工程技术学院,广西,南宁,530004;2.中国科学院国际材料物理中心,辽宁,沈阳,110016) 摘要:运用固体经验电子理论(EET), 对掺微量Sc的Al-Mg合金的价电子结构进行计算. 结果表明: 在合金熔体中Sc与Al原子存在强的结合倾向, 易形成粗大的Al3Sc颗粒, 起非匀质形核细化晶粒作用; 在合金凝固过程中, 形成Al-Sc偏聚区, 析出细小弥散的Al3Sc颗粒, 增强了合金基体和晶界的共价键络, 使合金的硬度,强度和晶粒热稳定性都得到提高. 关键词:Al-Mg合金; Al3Sc; 共价键; 晶粒细化; 力学性能; [全文内容正在添加中] ......
Al3Sc的FFC法制备和第一性原理计算研究邹祥宇1,廖先杰2,卫学玲1,夏鹏举1,徐峰1,罗清威11. 陕西理工学院材料科学与工程学院2. 攀枝花学院材料学院摘 要:采用熔盐电脱氧法(FFC)制备Al3Sc,并应用以密度泛函理论为基础的平面波赝势方法,利用第一性原理的CASTEP软件包计算了Al3Sc的晶体结构和电子结构.结果表明:物质的量比为3∶1的Al2O3和Sc2O3混合阴极片,在700℃,3.2 V电解电压下,经20 h电解后完全形成Al3Sc.计算了Al3Sc的晶格常数a=0.411 nm,与XRD检测结果符合.关键词:熔盐电脱氧法;Al3Sc;第一性原理;晶体结构;电子结构;......
:recrystallization; Al3Sc; Al-Sc alloy; electro magnetics; rare earths; [全文内容正在添加中] ......
Recrystallization and Morphology of Microstructure in Al-Sc Alloys张军,张宗华摘 要:Minor addition of Sc to aluminum results in the rapid precipitation of homogeneously distributed Al3Sc dispersoids. The presence of Al3Sc dispersoids is more effective recrystallization inhibitors. Our work established the precipitation of homogeneously distributed Al3Sc......
微量Sc对Al-Cu-Li-Zr合金的微观组织和拉伸性能的影响 朱朝明1,潘青林1,何运斌1,刘元斐1,尹志民1,梁文杰1 (1.中南大学,湖南,长沙,410083) 摘要:研究了微量Sc对Al-Cu-Li-Zr合金微观组织和拉伸性能的影响.结果表明:添加0.1%Sc(质量分数,下同)能消除铸态合金的枝晶组织,细化合金的晶粒.合金铸锭在随后的均匀化和热加工加热过程中,析出细小,弥散的次生Al3Sc质点,这种质点强烈地钉扎合金中的位错和亚晶界,从而有效地抑制合金的再结晶,具有亚结构强化和直接析出强化作用.加入微量Sc后,Al-Cu-Li-Zr合金的强度大大提高,并且合金的塑性也得到明显改善. 关键词:含Sc的Al-Cu-Li-Zr合金; 显微组织; Al3Sc; 拉伸性能; [全文内容正在添加中] ......
二元Al-Sc合金的屈服强度与微观组织演变孙莹莹,宋旼,贺跃辉中南大学粉末冶金国家重点实验室摘 要:采用力学性能测试和透射电镜显微组织分析研究退火工艺对Al-0.1%Sc(质量分数)合金屈服强度与显微组织演变的影响.研究表明,在退火过程中从过饱和固溶体内析出的均匀细小的可抑制Al-Sc合金再结晶和阻碍位错运动的Al3Sc颗粒的尺度与退火时间的立方根呈线性关系,服从Lifshitz-Slyozov-Wagner(LSW)模型.但随着退火温度的升高,Al3Sc颗粒的尺寸下降,与早期的研究结果相反.由于温度降低,Sc的过饱和度升高,Al3Sc的形核驱动力增大,在一定的退火时间下降低退火温度可导致Al3Sc颗粒的体积分数和Al-Sc合金的屈服强度增加.关键词:Al-Sc合金;屈服强度;显微组织;......
Sc和Zr复合微合金化在Al-Mg合金中的存在形式与作用 潘青林1,张传福1,尹志民1 (1.中南大学材料科学与工程系,湖南,长沙,410083) 摘要:研究了微量Sc和Zr复合合金化对Al-Mg合金显微组织与拉伸性能的影响.结果表明:Sc和Zr复合微合金化可显著提高Al-Mg合金的强度.Al-Mg-Sc-Zr合金凝固过程中形成的初生Al3(Sc, Zr)复合粒子具有极强的晶粒细化作用,次生Al3(Sc, Zr)质点与Al-Mg-Sc合金中次生Al3Sc质点相比析出密度大大增加,分布更加均匀弥散,抑制再结晶的能力更为强烈.Sc和Zr复合微合金化大大促进了微量Sc在Al-Mg合金中的强化作用.由于Zr的价格比Sc便宜很多,采用Sc和Zr复合微合金化可减少铝合金中Sc的加入量,从而降低合金的成本. 关键词:Al-Mg-Sc-Zr合金; Al3(Sc,Zr); Al3Sc; 显微组织......