共搜索到4436条信息，每页显示10条信息，共444页。用时：0小时0分0秒578毫秒
brazing of Si3N4 ceramic, it is important to find a suitable filler alloy to improve the properties of the joints. In this investigation, a Cu-Zn-Ti alloy was used as the filler alloy for the active... Article ID: 1003-6326(2005)03-0497-07 Effect of bonding parameters on microstructure and properties of Si3N4/Si3N4 joint brazed by Cu-Zn-Ti filler alloy ZHANG Jie(张 杰)1......
Detailing interfacial reaction layer products between cubic boron nitride and Cu-Sn-Ti active filler metalYonggang Fan,Junxiang Fan,Cong WangSchool of Metallurgy, Northeastern University摘 要:active filler metal at 1223 K.Current findings demonstrate that adequate wettability and satisfactory bonding have been achieved via chemical reactions between Ti and N,B.More importantly,we......
; 文献标识码: A Microstructure and properties of BCu80Ni5SnTi active filler metal for brazing cubic boron nitride WANG Yi1, 2, YIN Shi-qiang1, LU Guang-lin3, LI Shi-quan1, QIU Xiao-ming1 (1... boron nitride (c-BN) and 45 steel was prepared. The microstructures of BCu80Ni5SnTi active filler metal and mechanical properties of the joints of c-BN and 45 steel brazed with BCu80Ni5SnTi filler metal......
Brazing temperature-dependent interfacial reaction layer features between CBN and Cu-Sn-Ti active filler metalYonggang Fan1,Junxiang Fan1,Cong Wang1,21. School of Metallurgy, Northeastern University2... are prepared by active brazing sintering at 1123 K,1173 K, 1223 K and 1273 K, respectively. The effects of brazing temperature on the wettability, interfacial characteristics, and elemental distribution......
strength of the joints. Active filler nano Ai, Si powder can greatly improve the properties of the joints treated at high temperature. The improvement is over 700%. Key words: preceramic; silicone resin; pyrolysis temperature; inert filler; active filler; joining CLC number: TB323 Document code: A 1 INTRODUCTION......
Active metal brazing of SiO2–BN ceramic and Ti plate with Ag–Cu–Ti+BN composite fillerZ.W.Yang1,C.L.Wang1,Y.Wang1,L.X.Zhang2,D.P.Wang1,J.C.Feng21. Tianjin Key Lab of Advanced Joining Technology... ceramic and Ti plate were joined by active brazing in vacuum with Ag–Cu–Ti+BN composite filler.The effect of BN content,brazing temperature and time on the microstructure and mechanical properties......
......
and shear strengths of HEA/HEA and HEA/6061-Al joints were determined after direct active soldering (DAS) in air with Sn3.5Ag4Ti active filler at 250 °C for 60 s. The results showed that the diffusion... filler; Al0.3CrFe1.5MnNi0.5; direct active soldering 1 Introduction As various application fields such as energy, aerospace, transportation, and manufacturing advance, they present new demands......
were successfully produced using the latter filler alloy under the brazing condition of(1170-1230)℃for 10 min. The results showed that the active element V strongly diffused to the surface of Cf/SiBCN...Joining of Cf/SiBCN composite with CuPd-V filler alloyWen-Wen Li1,Bo Chen1,La-Mei Cao2,Wei Liu2,Hua-Ping Xiong1,Yao-Yong Cheng11. Welding and Plastic Forming Division, Beijing Institute......
formed by adding AI203 particulates into Ag-Cu-Ti active filler metal. The results showed that the material parameters (the Ti content, Al2O3 particulate volume fraction) of the composite filler materials...Effects of Al2O3-Particulate-Contained Composite Filler Materials on the Shear Strength Alumina JointsJianguo YANG, Hongyuan FANG and Xin WANNational Key Laboratory of Advanced Welding Production......