共搜索到18627条信息,每页显示10条信息,共1863页。用时:0小时0分0秒374毫秒
; 文献标志码:A Control analysis of main group element for Ti-13Nb-13Zr alloy in VAR process NIU Zhong-jie1, 2, YANG Guan-jun1, ZHAO Yong-qing2, CAO Ji-min2, YANG Hong-jin2 (1. Xi... module and mass transportation control coefficient calculation module, the saturated pressures and volatilization direction of Ti-13Nb-13Zr alloy in VAR process from thermodynamics field were......
Trans. Nonferrous Met. Soc. China 29(2019) 2090-2098 Artificial intelligence model of complicated flow behaviors for Ti-13Nb-13Zr alloy and relevant applications Ze-yan SHI1, 2, Guo-zheng QUAN2, Chao... Ti-13Nb-13Zr alloy was conducted by an improved intelligent algorithm, GA-SVR, the combination of genetic algorithm (GA) and support vector regression (SVR). The GA-SVR model learns from a training dataset......
Friction and Wear Behavior of Modified Layer Prepared on Ti-13Nb-13Zr Alloy by Magnetron Sputtering and Plasma Nitriding田伟红,GUO Yangyang,LI Xuanpeng,TANG Bin,范爱兰Research Institute of Surface Engineering, Taiyuan University of Technology摘 要:Two kinds nitride modified layers were obtained on Ti-13Nb-13 Zr surface to improve the wear property via magnetron......
放电等离子烧结温度对Ti-13Nb-13Zr合金在人工模拟体液中耐腐蚀性能的影响何远怀1,张玉勤1,2,蒋业华1,周荣11. 昆明理工大学材料科学与工程学院2. 云南省钛材应用产品工程技术研究中心摘 要:利用放电等离子烧结技术(spark plasma sintering,SPS)制备Ti-13Nb-13Zr...强.该合金在模拟人工体液中耐腐蚀性能优异的主要原因是合金表面形成稳定,均匀且保护性更强的复合氧化物钝化膜,钝化膜由Ti O2,Nb2O5和Zr O2组成;随烧结温度升高,合金获得较高的致密度和近β型单相组织,耐腐蚀性能提高.关键词:Ti-13Nb-13Zr合金;放电等离子烧结;Hank’s溶液;烧结温度;电化学腐蚀;......
microscopy. The wear resistance of TLM alloy was tested by sliding wear in comparison with as-annealed Ti-6Al-4V and as-aged Ti-13Nb-13Zr. The results show that the specimen cooled from α+β dual phase... Ti-6Al-4V and aged Ti-13Nb-13Zr, whereas the specimen treated at 510 ℃, 6 h, AC exhibits the highest value. So, heat treatment and alloy composition have a great influence on the wear resistance for Ti......
热处理对Ti-13Nb-13Zr合金显微组织的影响 () 摘要: Ti-13Nb-13Zr合金具有低模量,高生物相容性,耐蚀,抗磨等特性.经7次非自耗电弧熔炼制备了Ti-13Nb-13Zr合金的饼坯,化学成分如表1所示. [全文内容正在添加中] ......
Ti-13Nb-13Zr合金力学性能和显微组织的研究 王克光1,付艳艳2,周廉2,于振涛1 (1.西北有色金属研究院生物中心,陕西,西安,710016;2.东北大学材料与冶金学院,辽宁,沈阳,110004) 摘要:研究了Ti-13Nb-13Zr合金在β相区和(α+β)两相区固溶和时效处理后其合金力学性能及组织变化规律. 分析发现在β相区固溶的合金, 水冷时生成针状马氏体α′, 空冷时生成亚稳定β相和少量αp, 在(α+β)两相区固溶生成β转和αP. 在β相区和(α+β)两相区固溶试样经时效后, 晶粒内部主要析出点状和棒状αS. 在750 ℃/1 h固溶(WQ)和低温510 ℃/6 h时效的合金抗拉强度高,塑性较高,弹性模量低, 可以满足人体植入要求. 关键词:Ti-13Nb-13Zr; 力学性能; 显微组织; [全文内容正在添加中] ......
植入物用Ti-13Nb-13Zr合金电化学性能的研究何蕾摘 要:<正>Ti-6Al-4V ELI合金的杨氏模量仅为120136GPa,与Co-Cr基合金及不锈钢相比,更接近于人体骨骼的杨氏模量(1030 GPa),因此被广泛应用于制造人造髋关节及人造牙根.然而,随着对钛合金研究的深入,Ti-Nb-Zr(TNZ)及Ti-Nb-Zr-Ta(TNZT)系等杨氏模量更接近于人体骨骼的医用钛合金被逐渐研制和推广应用.其中,Ti-13Nb-13Zr的杨氏模关键词:......
显微组织对Ti-13Nb-13Zr医用钛合金力学性能的影响 王克光1,付艳艳2,周廉1,于振涛1 (1.西北有色金属研究院,陕西,西安,710016;2.东北大学,辽宁,沈阳,110004) 摘要:研究了Ti-13Nb-13Zr合金在β相区和α+β相区固溶和时效处理后合金的力学性能变化规律.利用光学显微镜,扫描电镜和透射电镜观察和X射线衍射分析,重点分析了不同显微组织对合金强韧性的影响.结果表明:含有一定数量初生α析出相的加工态组织具有较高的强度和断裂韧性.固溶时效处理后,随着显微组织的形貌,晶粒大小和数最的不同,其对强度和断裂韧性的影响也有所不同. 关键词:医用钛合金; Ti-13Nb-13Zr; 断裂韧性; 强度; [全文内容正在添加中] ......
基于TiH2粉末制备Ti-13Nb-13Zr合金的微观组织与结构王静哲1,2,张家敏1,3,2,4,易健宏1,3,2,4,甘国友1,3,2,4,刘意春1,3,2,41. 昆明理工大学2. 云南省新材料制备与加工重点实验室3. 稀贵及有色金属先进材料教育部重点实验室4. 昆明市稀贵及有色金属先进材料重点实验室摘 要:利用TiH2,ZrH2的脱氢特性,结合粉末冶金方法,将TiH2,Nb和ZrH2粉末经混合球磨,压制成形,真空烧制得到Ti-13Nb-13Zr合金,对样品进行金相显微镜,SEM,XRD分析,结果表明:烧结坯体相对密度达到92.2%,合金主要组织为α+β型片状魏氏组织,且在合金形成过程中β稳定元素的Nb发挥作用,使得钛的β相在降温完成后仍稳定存在;α-Ti及α-Zr为六方密排(hcp)结构,β......