Bulk Al/SiC nanocomposite prepared by ball milling and hot pressing method GU Wan-li(谷万里) School of Mechanical Engineering, Shandong University of Technology, Zibo 255049, China Received 10...-sized SiC particle. The bulk Al/SiC nanocomposite can be fabricated by hot pressing the nano-sized Al/SiC powders at temperature about 723 K under pressure of 100 MPa. Key words: nanocomposite......
J. Cent. South Univ. (2012) 19: 55-62 DOI: 10.1007/s11771-012-0972-y Simulation of pressure effects on hot isostatic pressing of stainless steel powder LIU Guo-cheng(刘国承), SHI Yu-sheng(史玉升), WEI Qing... University Press and Springer-Verlag Berlin Heidelberg 2012 Abstract: To investigate the effects of pressure on the hot isostatic pressing (HIP) process of a stainless steel powder, density distribution......
Synthesis of high-purity Ti2AlN ceramic by hot pressing YAN Ming(严 明)1, CHEN Yan-lin(陈艳林)1, MEI Bing-chu(梅炳初)2, ZHU Jiao-qun(朱教群)2 1. College of Chemistry and Environmental Engineering, Hubei...; Abstract: High-purity Ti2AlN ceramic was prepared at 1300 ℃ by hot pressing(HP) of Ti/Al/TiN powders in stoichiometric proportion. The sintered product was characterized using X-ray......
......
Synthesis of Ti2AlC by hot pressing and its mechanical and electrical properties WANG Ping(王 苹)1, 2, MEI Bing-chu(梅炳初)2, HONG Xiao-lin(洪小林)2, ZHOU Wei-bing(周卫兵)2 1. School of Science, Wuhan...; Abstract: Ti2AlC bulk material was synthesized by hot pressing of mixture powders of TiC, Ti, Al and active carbon. The phase compositions of resultant product at different......
Synthesis of Al2O3/TiCN-0.2%Y2O3 Composite by Hot Pressing李喜坤,邱关明,丘泰,赵海涛,白华,孙旭东摘 要:Al2O3/TiCN composites were synthesized by hot pressing.The influences... of Al2O3/TiCN composite increased with temperature when hot pressing temperature is below 1650 ℃.The mechanical properties reached their maximums when the composites were sintered at 1650 ℃ for 30 min under hot......
......
......
Fabrication of Ni3Al by hot pressing from element powdersMENG Jie, JIA Chengchang, and HE Qing School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China摘 要:Ni3Al intermetallic was synthesized by hot pressing from element powders of nickel, aluminum, and boron. The influences of parameters......
">In the present study, pure magnesium was in situ coated with pre-alloyed Al–Cu–Mg alloy through hot pressing. The produced samples were characterized by means of hardness, wear properties and microstructure characterization. A ball-on-disk test was used to determine the dry sliding wear characteristics of the compacts. The results showed that the hot pressing technique has been successfully applied......