共搜索到652条信息,每页显示10条信息,共66页。用时:0小时0分0秒390毫秒
of tetraethylorthosilicate (TEOS) on the surface of the Fe particles. The samples were characterized by XRD, TEM, SAED, TG-DSC and VSM. The results indicate that a thin film of silica is coated on the surface of Fe... of SiO2-coated iron nanoparticles (c) In order to confirm the difference of anti-oxidation capability of the coated and uncoated samples, the TG-DSC curves were measured. Fig.4 shows that the mass change......
晶态层状N,N-二乙酸亚氨基亚甲基膦酸-磷酸氢锆的制备及插层研究 牛丽明1,陈静蓉1,傅相锴1,杨新斌1,饶小平1 (1.西南师范大学,化学化工学院,重庆应用化学市级重点实验室,重庆,400715) 摘要:采用氢氟酸络合法合成了结晶度高的N,N二乙酸亚氨基亚甲基膦酸-磷酸氢锆(α-ZPPMIDA)层状晶体,层间距为1.477m.研究了正丁胺对α-ZPPMIDA的插层反应,用IR,XRD,TG-DSC热分析和元素分析对该插层复合物进行了表征.结果表明正丁胺在主体底物中呈双分子层,层间距增大了0.847nm. 关键词:N,N-二乙酸亚氨基亚甲基膦酸-磷酸氢锆; 正丁胺; 插层; 双分子层; [全文内容正在添加中] ......
化学共沉淀法制备Ca_2Co_2O_5粉体 林元华1,兰金叻1,赵淑金2,李国晶2,梅骜1 (1.清华大学,新型陶瓷与精细工艺国家重点实验室,北京,100084;2.佳木斯大学,黑龙江,佳木斯,154007) 摘要:以硝酸钴和硝酸钙为原料,氢氧化钠为沉淀剂,利用化学共沉淀法制备Ca_2Co_2O_5粉体.采用TG-DSC,XRD,SEM和激光粒度分析仪(LPSA)等测试方法对粉体热分解过程,样品的物相,形貌和粒度分布进行表征.结果表明:在pH=13.2时制备的共沉淀粉,在750 ℃煅烧2 h后可获得单相层状的Ca_2Co_2O_5粉体,颗粒尺寸分布均匀,粒度在几百个纳米范围内. 关键词:共沉淀法; NaOH; Ca_2Co_2O_5粉体; coprecipitation methods; sodium hydroxide; Ca_2Co_2O_5 powders; [全文内容......
characterized by various characterization techniques such as TG-DSC,XRD and TPR.The results of TG-DSC indicated that the Ce1-xNixO2 precursor generated a stable phase after the heat-treatment......
八水碳酸镨的热分解及其动力学分析邓庚凤,谢耀,李志午,邓超群,汪晨阳,曾青云江西理工大学冶金与化学工程学院摘 要:采用碳酸氢钠和氯化镨制备八水碳酸镨颗粒后,运用TG-DSC技术,在不同程序升温下,研究八水碳酸镨(Pr2(CO3)3·8H2O)的热分解过程.分别采用Ozawa-Flynm-Wall法,Kissinger法,Crane法和Coats-Redfem法确定其热分解动力学参数.TG-DSC表明,八水碳酸镨热分解过程为3个阶段,第一阶段为脱水反应,第二阶段碳酸镨分解为Pr2CO5,第三阶段为Pr2CO5分解为Pr6O11.运用Coats-Redfem积分法得出第二阶段反应的反应机理受二维扩散机理控制,第三阶段反应的反应机理受成核和生长机理控制.在确定了八水碳酸镨热分解反应机理函数的前提下,实验计算......
characterized by various characterization techniques such as TG-DSC,XRD and TPR.The results of TG-DSC indicated that the Ce1-xNixO2 precursor generated a stable phase after the heat-treatment......
种典型锌精矿氧压酸浸渣的粒度分布,化学组成,形貌特征和表面元素化学价态以及分子键结构等矿物学特性.采用热分析仪(TG-DSC)和毒性浸出程序(TCLP)分别考察锌氧压酸浸渣的着火性能和短期环境活性等安全属性.研究结果表明:氧压酸浸渣1多呈球块状,平均粒径为22 μm,主要物相为单质硫,闪锌矿,黄铁矿,石膏和石英等,其中单质硫质量分数最高,达52%;氧压酸浸渣2外形不规则,平均粒径为86 μm,主要... of ZLRs were investigated by thermal analysis(TG-DSC) and toxic leaching procedure(TCLP), respectively. The results show that No.1 ZLR is spherical in shape, with an average particle size of 22 μm......
验.利用XRD,SEM和TG-DSC等手段,研究净浆试样水化产物种类,微观形貌及质量损失率;基于室内实验研究成果,开展新型充填胶凝材料工业化应用研究.研究结果表明:当复合激发剂掺量为15%,石膏和熟料质量比为1:4,充填体3 d抗压强度最大为1.05 MPa;当复合激发剂掺量为20%,石膏和熟料质量比为3:2,充填体28 d抗压强度最大为8.61 MPa.石膏促使浆体中钙矾石(缩写为AFt)的生成... of cementitious materials with different gypsum-clinker mass ratios were carried out. XRD, SEM and TG-DSC were used to study the types, micro-morphology and mass loss rate of hydration products. Based......
溶胶-凝胶燃烧合成制备NiO纳米颗粒的研究 于美1,刘建华1,李松梅1 (1.北京航空航天大学,材料科学与工程学院,北京,100083) 摘要:研究了以硝酸镍和柠檬酸为原料溶胶-凝胶自燃烧法制备氧化镍纳米颗粒的最佳工艺条件及配比.用热重分析(TG-DSC),扫描电镜(SEM)和X射线衍射(XRD)对反应物,反应过程,产物氧化镍等进行了表征.研究了溶胶-凝胶pH值,原料配比对产物的影响并对反应机理进行了初步探讨.通过调整柠檬酸与硝酸镍的配比来避免镍的出现.本方法设备简单,操作方便易行. 关键词:溶胶-凝胶自燃烧; 氧化镍纳米颗粒; 原料配比; [全文内容正在添加中] ......
钛交联蒙脱石纳米复合材料的合成与物理性能 张一敏1,强敏1,项茹1 (1.武汉科技大学化工与资源环境学院,武汉,430081) 摘要:以经过精制的湖北钠基蒙脱石为基质材料,以钛酸正丁酯为钛源,制备了钛交联蒙脱石纳米复合材料(Ti-PILCs);并利用XRD,TG-DSC,FT-IR,N2吸附脱附等分析手段对材料进行了结构性能表征.结果表明:Ti-PILCs的层间距从钠基蒙脱石的1.28nm最高可增加至3.74nm;Ti-PILCs的热失重比精土大,且在970℃之前具有较好的热稳定性;比表面积从精土的31.6m2/g增大到Ti-PILCs的S60℃=415.1m2/g;Ti-PILCs以中孔孔径为主;同时还具有Ti-O键和Ti-O-Si键的红外振动峰. 关键词:钠基蒙脱石; 钛交联; 合成; 表征; [全文内容正在添加中] ......