共搜索到7709条信息,每页显示10条信息,共771页。用时:0小时0分0秒687毫秒
Trans. Nonferrous Met. Soc. China 30(2020) 2311-2325 Relationship between amounts of low-melting-point eutectics and hot tearing susceptibility of ternary Al-Cu-Mg alloys during solidification Jia... and the hot tearing susceptibility of ternary Al-Cu-Mg alloys during solidification was performed. By controlling the concentrations of major alloying elements (Cu, Mg), the amounts of LMP eutectics......
Trans. Nonferrous Met. Soc. China 24(2014) s53-s58 Effect of Mg composition on sintering behaviors and mechanical properties of Al-Cu-Mg alloy Min Chul OH, Byungmin AHN Department of Energy Systems.... Key words: powder metallurgy; Al-Cu-Mg alloy; spinel structure; liquid phase sintering 1 Introduction Aluminum alloy is one of the most common lightweight alloys used in various engineering structures......
文章编号:1004-0609(2011)07-1504-09 Ag对Al-Cu-Mg合金Ω相析出行为的影响 蔡金伶, 易丹青, 王宏伟, 王 斌 (中南大学 材料科学与工程学院,长沙,410083) 摘 要:用硬度测试,差热分析(DSC)以及透射电镜(TEM)研究Al-Cu-Mg-(Ag)合金时效过程中组织和性能的演变;根据不同升温速率的DSC曲线,采用Kissinger法计算Ω相和θ′相的激活能,探讨Ag对Al-Cu-Mg合金Ω相和θ′相析出行为的影响.结果表明:Al-Cu-Mg合金经185 ℃时效后,时效硬化曲线呈双阶段硬化特征,生成少量Ω相;添加Ag后,合金的时效硬化能力显著提高,经170,185和200 ℃时效时,对应的峰值时效时间分别为10,5和2 h,峰值硬度随着时效温度的升高而下降;Ag能促进Ω相析出,使θ′相的激活能提高,从而抑制θ′相的 ......
文章编号:1004-0609(2016)-08-1607-08 Al-Cu-Mg合金蠕变成形热处理工艺 周泽鹏1,张 劲2, 3,邓运来1, 3,张新明1, 3 (1. 中南大学 材料科学与工程,长沙 410083; 2. 中南大学 轻合金研究院,长沙 410083; 3. 中南大学 高性能复杂制造国家重点实验室,长沙 410083) 摘 要:采用扫描电镜,透射电镜,常温拉伸,断裂韧性,疲劳裂纹扩展速率等测试方法对比研究蠕变时间,自然时效及人工时效对Al-Cu-Mg合金蠕变成形后的力学性能,疲劳裂纹扩展性能和显微组织的影响.结果表明:不同蠕变成形时间对合金的常温力学性能影响较小,抗拉强度和屈服强度的波动幅度均在4%以内;相比于人工时效状态,合金在自然时效状态下综合性能更好;试样经413 ℃,12 h蠕变成形后,再进行T4时效处理得到最佳的综合性能,通过该实验条件......
......
inhibitor [J]. Corrosion Science, 2010, 52(2): 602-611. [35] WANG S C, STARINK M J. Precipitates and intermetallic phases in precipitation hardening Al-Cu-Mg-(Li) based alloys [J]. International...Trans. Nonferrous Met. Soc. China 23(2013) 3215-3227 Corrosion behavior of 2024 Al-Cu-Mg alloy of various tempers K. S. GHOSH, Md. HILAL, Sagnik BOSE Department of Metallurgical and Materials......
, Starink M J. Precipitates and intermetallic phases in precipitation hardening Al-Cu-Mg-(Li) based alloys[J]. International Materials Reviews, 2005, 50(4): 193-215. [2] 王祝堂, 田荣璋. 铝合金及其加工手册[M]. 3版. 长沙: 中南...主要强化机制为析出强化,主要的强化相有θ系列相和S相;T3处理工艺的主要强化机制为加工硬化和析出强化,主要强化相为GPI区;T8工艺的主要强化机制为析出强化,细晶强化和部分的加工硬化,主要强化相种类取决于预变形形变量. 关键词:Al-Cu-Mg合金;析出相;时效;背散射电子衍射;电子显微学技术 中图分类号:TG146.2  ......
DOI:10.19476/j.ysxb.1004.0609.2017.10.06 蛇形轧制对Al-Cu-Mg合金板材强韧性能及微观组织的影响 胥福顺1, 2,张 劲3, 4,邓运来1, 4,张新明1, 4 (1. 中南大学 材料科学与工程学院,长沙 410083; 2. 云南冶金集团服份有限公司,昆明 650502; 3. 中南大学 轻合金研究院,长沙 410083; 4. 中南大学 高性能复杂制造国家重点实验室,长沙 410083) 摘 要:基于实验室自制蛇形轧制装置,采用室温拉伸,Kahn撕裂,电子背散射衍射(EBSD)等测试方法对比研究蛇形轧制非对称工艺参数对Al-Cu-Mg合金轧制板材的室温强度,断裂韧性和显微组织的影响.结果表明:合理的蛇形轧制工艺在能够使Al-Cu-Mg合金板材保持强度性能的同时,显著提升其断裂韧性.当偏移量相同时,蛇形轧制板材的强度性......
文章编号:1004-0609(2013)07-1812-07 Mg含量对Al-Cu-Mg-Ag合金组织与力学性能的影响 宋艳芳1,潘清林1,2,丰 雷1,王 迎1,李 晨1 (1. 中南大学 材料科学与工程学院,长沙 410083; 2. 中南大学 有色金属材料科学与工程教育部重点实验室,长沙 410083) 摘 要:采用维氏硬度,室温拉伸性能测试,金相显微分析技术,透射电子显微分析等手段,研究Mg含量对Al-Cu-Mg-Ag耐热铝合金的组织和性能的影响.结果表明:随着Mg含量的增加,合金的时效响应速率加快,峰时效时间提前,且峰值硬度先增大后减小,在Cu/Mg摩尔比接近6时峰值硬度达到极大值;合金的抗拉强度和屈服强度先上升后下降,塑性则先降低后提高,但总体保持在较高水平;Mg含量(质量分数)为0.4%和0.8%时,合金的主要强化相为Ω相和少......
DOI: 10.11817/j.ysxb.1004.0609.2021-40080 激光选区熔化成形含锆Al-Cu-Mg合金的显微组织与力学性能 王凯冬,刘允中,程 文,刘小辉,周志光 (华南理工大学 国家金属材料近净成形工程技术研究中心,广州 510640) 摘 要:采用激光选区熔化(Selective laser melting,SLM)技术制备含锆Al-Cu-Mg合金,通过SEM,EBSD,TEM,拉伸实验等方法研究沉积态和热处理态试样的显微组织与力学性能.结果表明:当激光能量密度为370 J/mm3时,试样的致密度最高.原位生成Al3Zr使试样的平均晶粒尺寸细化为1.28 μm,消除了SLM成形Al-Cu-Mg合金中的热裂纹.尺寸为50~300 nm的Al3Zr亚稳态相(L12-Al3Zr)分布于基体,L12-Al3Zr可充当α(Al)非均匀形核的有效衬底......