共搜索到807条信息,每页显示10条信息,共81页。用时:0小时0分0秒531毫秒
低温固相反应法制备NiFe2O4纳米粉体 王海波1,王丽1,田庚方1,李发伸1 (1.兰州大学教育部磁学与磁性材料重点实验室,甘肃兰州,730000) 摘要:采用低温固相反应法制备了NiFe2O4铁氧体纳米粉体.用X射线衍射,振动样品磁强计及穆斯堡尔谱仪对样品进行了分析与观测.结果表明,该方法可以方便地得到纯度较高,粒径在9~35 nm之间,粒度分布均匀的尖晶石结构的NiFe2O4粉体.随着焙烧温度的提高相结构趋于完整,晶粒尺寸增大.随着晶粒尺寸的增大,样品饱和磁化强度随之增大,向块体逼近;平均超精细场也随之增大,穆谱数据还显示了样品的超顺磁转变尺寸为9 nm左右. 关键词:低温固相反应法; 镍铁氧体纳米颗粒; 微结构; 磁性能; [全文内容正在添加中] ......
. Key words: powder metallurgy; Al-Cu-Mg alloy; spinel structure; liquid phase sintering 1 Introduction Aluminum alloy is one of the most common lightweight alloys used in various engineering structures... the oxide on the metal-oxide interface, transforming to MgAl2O4 spinel structure [8-14]. MgAl2O4 spinel structure (3.59 g/cm3) exhibits lower density than the aluminum oxide Al2O3 (3.9 g/cm3......
Ag含量对NiFe2O4基金属陶瓷惰性阳极性能的影响 张晓明1,席锦会2,刘宜汉1,姚广春1 (1.东北大学,材料与冶金学院,辽宁,沈阳,110004;2.中国矿业大学,材料科学与工程学院,江苏,徐州,221008) 摘要:为了提高NiFe2O4陶瓷阳极材料的力学性能和抗热震性,向原料中加入金属Ag,采用粉末冶金法制备了Ag/NiFe2O4金属陶瓷惰性阳极.研究了Ag含量对材料微观结构,抗弯强度以及抗热震性的影响.研究结果表明随着Ag含量的增加,惰性阳极材料的晶粒尺寸逐渐减小,说明Ag能够有效抑制陶瓷基体晶粒的长大.而且随着Ag含量的增加,材料的结构越来越致密,说明Ag在一定程度上能够促进烧结.对材料的力学性能和抗热震性测试结果发现,Ag能提高材料的强度,随着Ag含量的增加,材料的抗弯强度逐渐增大,抗热震性在银含量为10%处达到最大值. 关键词:金属陶瓷; 惰性阳极; 抗弯强度......
NiFe2O4尖晶石烧结过程阳极试样力学性能的影响 张磊1,姚广春2,焦万丽1 (1.山东理工大学,材料工程与科学学院,山东,淄博,255049;2.东北大学材料与冶金学院,辽宁,沈阳,110004) 摘要:以NiO和Fe2O3为主要原料,研究了其在合成镍铁尖晶石反应烧结过程中的热力学及合成的镍铁尖晶石粉料烧结过程的动力学条件,利用球模型推导的扩散机制的烧结方程测算出不同合成温度烧结试样的烧结机制.同时对在不同烧结温度下合成的尖晶石粉料经二次烧结制备的阳极试样的抗折强度进行了测量.结果表明,NiO和Fe2O3固相反应的热力学条件具备,不同烧结温度烧结的NiFe2O4尖晶石粉料初期烧结由体积扩散和界面扩散共同控制,且当合成尖晶石温度为900℃时,惰性阳极试样气孔率达到一个最小值,此时强度值最大. 关键词:镍铁尖晶石; 固相反应; 热力学; 动力学; 力学性能; [全文内容正在添......
......
High-rate capability of spinel LiNi0.05Mn1.95O4 cathode for Li-ion batteries prepared via coprecipitated precursor SUN Bin(孙 斌)1, 2, SHEN Guo-pei(申国培)2, HU Yan-long(胡燕龙)2 1. College... September 2007 Abstract: Spinel LiNi0.05Mn1.95O4 cathode material for lithium ion batteries was synthesized by solid-state reaction from coprecipitated Ni-Mn hydroxide precursors and characterized by X-ray......
Electrochemical performance of Al2O3 pre-coated spinel LiMn2O4Hong-Ming Zhou1,2,Yu-Hua Zhu1,Jian Li1,2,Wen-Jiao Sun1,Zhong-Zhong Liu11. School of Materials Science and Engineering, Central South University摘 要:Al2O3-coated spinel LiMn2O4 cathode materials, presintered LiMn2O4(P-LMO), and calcined LiMn2O4(C-LMO) were synthesized by chemical deposition......
NiFe2O4基惰性阳极的润湿性及气泡析出行为王斌1,杜金晶1,刘宜汉2,姚广春21. 西安建筑科技大学冶金工程学院2. 东北大学材料与冶金学院摘 要:利用座滴法和双室透明电解槽对NiFe2O4基惰性阳极的润湿性和气泡析出行为进行研究.结果表明,电解质对NiFe2O4基惰性阳极的润湿性要优于碳素阳极.在低电流密度情况下电解,阳极气泡的析出是一个动态过程,它先在阳极表面形核,以球形方式长大,小气泡在长大过程逐渐汇聚偏移,然后逸出.惰性阳极上析出的气泡尺寸比碳素阳极小,在阳极上的逗留时间也更短.大电流密度情况下,气泡的生成速度加快,尺寸降低,很难准确测量气泡的直径.关键词:NiFe2O4基惰性阳极;润湿性;气泡;......
Cyclic voltammetry studies on 4 V and 5 V plateaus of non-stoichiometric spinel Li1+xMn2-yO4 BAI Ying(白 莹)1, 2, WU Chuan(吴 川)1, 2, WU Feng(吴 锋)1, 2, WANG Guo-qing(王国庆)1, 2 1. School of Chemical... reaction. By X-ray diffraction analysis, Li2MnO3 was detected as a second phase with increasing the Li/Mn ratio; and the role of Li2MnO3 in Li1+xMn2-yO4 spinel was discussed. A slow scanning cyclic......
烧结工艺对NiFe2O4陶瓷纯度和相对密度的影响林启权1,黄伟1,董文正1,朱远志2,姜滔11. 湘潭大学机械工程学院2. 武汉科技大学材料与冶金学院摘 要:采用粉末冶金固相烧结法合成了NiFe2O4陶瓷,研究了烧结温度和保温时间对其纯度和相对密度的影响.结果表明:随着烧结温度的升高和保温时间的延长,NiFe2O4的纯度增大;在1 100℃保温2h即可合成纯度较高的NiFe2O4陶瓷;提高烧结温度和延长保温时间均有利于NiFe2O4陶瓷的致密化;在1 200℃保温2h是制备NiFe2O4陶瓷的较佳工艺.关键词:NiFe2O4陶瓷;烧结温度;保温时间;纯度;相对密度;......