Preparation of Mg-Li-Sm alloys by electrocodeposition in molten salt YAN Yongde1,ZHANG Milin1,TIAN Yang1,JING Xiaoyan1,HAN Wei1 (1.Key Laboratory of Superlight Materials and Surface Technology... electrolysis condition was a molten salt mixture of LiCl: KCl=50:50 (wt.%), electrolytic temperature: 660 ℃, cathode current density:9.5 A/cm~2 and electrolysis time of 40 min. The current efficiency......
) was investigated in an equimolar mixture of CaCl2-NaCl molten salt at 800 °C for developing a more efficient process for chromium preparation. Cyclic voltammetry and potentiostatic electrolysis were used... the electrolysis process. The results demonstrate that CaCl2-NaCl molten salt is applicable for preparing Cr directly from Cr2O3 and the electrolysis parameters exert great influence on the cathode......
into g-C3 N4 lattice simultaneously by the molten salt method. Alkali metal modification not only promotes the specific surface area, visible light absorption and separation of electron-hole pairs, but tunes...Synthesis of band gap-tunable alkali metal modified graphitic carbon nitride with outstanding photocatalytic H2O2 production ability via molten salt methodXiaoyu Qu,Shaozheng Hu,Jin Bai,Ping Li,Guang......
electrodeposition in LiF-NaF-KF-K2TiF6-KBF4 molten salt LI Jun1, LI Bing2 (1. School of Materials Engineering, Shanghai University of Engineering Science, Shanghai 201600, China; 2. School...(Ⅲ) (c(KBF4)=0.4mol/L) on the platinum electrode in 46.5LiF-11.5NaF-42KF (mole fraction, %) molten salt at 700℃ were investigated by means of the cyclic voltammetry technique. The cathode process......
......
in AlCl 3 -NaCl-KCl molten salt with a mass ratio of 8:1:1 were investigated by SEM and EDS. The binding force was measured by splat-cooling method and bending method. The results indicate...Electrodeposition of aluminum on aluminum surface from molten saltWenmao HUANG, Xiangyu XIA, Bin LIU, Yu LIU, Haowei WANG and Naiheng MA State Key Laboratory of Metal Matrix Composites, Shanghai Jiao......
......
性,发现样品大约在400℃开始分解,表明Ba0.6K0.4BiO3在400℃以上是不稳定的. 关键词:Ba1-xKxBiO3:熔盐法; 超导电性; Ba1-xKxBiO3; molten salt method; superconductivity; [全文内容正在添加中] ......
nanocoating methods. The molten salt method may also be used to produce other metal oxides coating nanostructures as the electrode materials for lithium-ion batteries. Key words: nanometer materials... of (006) and (110) planes, respectively. The overall synthetic procedure and growth mechanism are described in Fig. 1. The molten salt method shows an accelerated reaction rate and controllable particle......
......