共搜索到652条信息,每页显示10条信息,共66页。用时:0小时0分0秒578毫秒
or Tb) crystalline phase was formed at 900 ℃ with the precursor prepar by nitric-citric combustion process. The synthesis process was studied by XRD, TG-DSC and IR spectra. The analysis results show......
纳米Ca0.8Zn0.2TiO3∶Pr3+, Na+荧光粉的合成和红色发光性质 廉世勋1,左成钢1,张华京1,李承志1,尹笃林1 (1.湖南师范大学化学化工学院,化学生物学及中药分析省部共建教育部重点实验室,湖南,长沙,410081) 摘要:采用溶胶-凝胶法在较低温度下合成了Ca0.8Zn0.2TiO3∶Pr3+,Na+纳米荧光粉.金属离子预先分散在溶有柠檬酸的乙二醇溶液中.通过TG-DSC,XRD和SEM对前驱物的分解,晶化和颗粒大小进行了研究.TG-DSC和XRD表明材料的组成随灼烧温度而变化;SEM表明1000 ℃合成材料的粒径在100 nm以下.与高温固相法合成的材料相比,激发光谱主峰发生蓝移,红色发射峰617 nm显著增强. 关键词:Ca0.8Zn0.2TiO3; 溶胶-凝胶法; 纳米荧光粉; 红色发光; 稀土; [全文内容正在添加中] ......
纳米级WO3-CuO复合氧化物粉末的制备徐金龙,张丽英,林涛,吴成义摘 要:用超声喷雾热转换法直接制成纳米级非晶复合氧化物粉末,并采用XRD,TEM和TG-DSC手段研究纳米WO3-CuO复合氧化物粉末的热解与非晶向微晶的转化过程.结果表明用超声喷雾热转换法可以工业化大规模生产纳米级WO3-CuO复合氧化物粉末,粉末平均粒径<50nm,颗粒形状为球形.关键词:超声喷雾转换法;纳米复合粉末;W-Cu合金;......
of specimens in hybrid sol, desiccation of hybrid sol, and calcination of hybrid gel. TG-DSC curve was used to determine appropriate temperature for the conversion of hybrid gel into coating. SEM, ICP...-gel)体系,在单晶硅表面制备含钛的磷灰石蜂窝状多孔涂层,采用热重-差热技术(TG-DSC)确定含钛磷灰石涂层的形成温度,场发射扫描电镜(FE-SEM)观察涂层的形貌结构,电子能谱(EDS)和X射线衍射研究涂层的元素与晶体构成,在模拟体液(SBF)中浸泡样品以考察涂层的化学稳定性与诱导 能力. 1 实验 1.1 样品制备 样品制备过程主要包括: 1) 硅片......
MCM-41固载席夫碱钴配合物在环己烷氧化反应中的应用 单高峰,袁霞,吴剑,罗和安 (湘潭大学 化工学院,湖南 湘潭,411105) 摘要:制备γ-氨丙基三乙氧基硅烷修饰的MCM-41分子筛固载型双水杨醛缩乙二胺合钴(Cosalen)配合物,采用傅里叶变换红外光谱,X线衍射,比表面积测定,热重-差热(TG-DSC),紫外-可见光光谱(UV-Vis),透射电镜等方法对分子筛固载型配合物... into the meso-porous molecular sieve (MCM-41) which was modified by 3-triethoxysilylpropylamine. The prepared Cosalen/MCM-41 was characterized by the technique of FT-IR, XRD, BET-BJH, TG-DSC, UV-Vis......
剂KH550对制备的纳米铜粉进行表面抗氧化处理;然后以纳米铜粉为导电填料,以双酚A型环氧树脂(E51)为载体,加入适量的固化剂和稀释剂,除泡剂,促进剂等制备纳米铜粉导电胶.采用X射线衍射(XRD)和透射电镜(TEM)等对制备铜粉的物相,粒度和形貌等进行表征;对预处理前后的纳米铜粉进行热重与差热(TG-DSC)分析;并研究纳米铜粉添加量对所制备导电胶电阻率和连接强度等性能的影响.结果表明:采用凝胶浇...) were used to characterize the phase composition, particle size and morphology of the copper powders. The copper powders before and after anti-oxidation treatment was conducted by TG-DSC analysis......
410083, China ? Central South University Press and Springer-Verlag Berlin Heidelberg 2012 Abstract: The differences in XRD patterns, elemental compositions, FT-IR spectra and TG-DSC curves of extract... between two humin fractions. TG-DSC analysis shows that thermal decomposition occurs during the heating of testing samples. By contrast, the humin fractions associated with inorganic minerals obtained......
DOI:10.19476/j.ysxb.1004.0609.2019.04.25 采用球磨-低温热处理-浮选法回收废旧锂电池中电极材料的机理 黄红军,黄秋森 (中南大学 资源加工与生物工程学院,长沙 410083) 摘 要:采用球磨-低温热处理两阶段流程可以将阻碍钴酸锂和石墨浮选分离的锂电池电极材料表面有机物膜去除,通过TG-DSC综合热分析,接触角,XPS测试进行机理研究.结果表明...95%以上,其中钴品位为27.32%,远大于矿山矿石品位. 图1 混合物XRD谱 Fig. 1 XRD pattern of the mixture 表1 混合物元素分析结果 Table 1 Elemental analysis results of mixture (mass fraction, %) 1.2 TG-DSC综合热分析......
621010) 摘 要:以锂辉石浮选尾矿为主要原料,黏土矿物为黏结材料,辅以少量羧甲基纤维素钠提高其生坯强度,通过过氧化氢发泡造孔制备出多孔陶瓷材料.通过正交试验探究各因素对试样各方面性能的影响并用SPSS软件对其进行回归分析.最后结合XRF,XRD,SEM,TG-DSC热分析和光学显微镜观察对多孔陶瓷化学组成,物相组成,微观形貌及烧结过程进行分析.结果表明:高岭土较钠基膨润土更适合作为多孔陶...多孔陶瓷材料.通过正交试验探究各因素对试样各方面性能的影响,并用SPSS软件对其进行多元线性回归分析,最后通过XRF,XRD,SEM,TG-DSC热分析及显微镜观察对其主要物理性能进行测试和表征.以期早日实现锂辉石浮选尾矿的高附加值资源化利用. 1 实验 1.1 原料粒度,化学组成和物相组成 本实验所用锂辉石浮选尾矿取自四川甘孜州某选矿厂.原料化学组成和粒度分布分别如表1表......
模板法构筑氧化钼纳米棒阵列的结构与场发射性能研究 陈文1,薛理辉2,麦立强1,祁琰媛2,刘曰利1 (1.武汉理工大学,材料科学与工程学院,湖北,武汉,430070;2.武汉理工大学,材料研究与测试中心,湖北,武汉,430070) 摘要:以聚碳酸酯(PC)膜为模板,结合溶胶凝胶法制备了直径为200nm的非晶态氧化钼纳米棒阵列;390℃热处理1h后转变为晶型良好且高度有序的MoO3·2H2O纳米棒阵列.利用XRD,TG-DSC,SEM和HRTEM测试手段分析产物的形貌与结构,同时发现该阵列具有较好的场发射性能. 关键词:模板; 氧化钼; 纳米棒; 阵列; 场发射性能; [全文内容正在添加中] ......