共搜索到14582条信息,每页显示10条信息,共1459页。用时:0小时0分0秒265毫秒
......
Vanadium extraction and dephosphorization from V-bearing hot metal with fluxes containing CaOWANG Yan-nan(王艳南)1, 2, SONG Wen-chen(宋文臣)1, 2, LI Hong(李宏)1, 2(1. State Key Laboratory of Advanced...)Abstract:Extracting vanadium and removing phosphorus simultaneously by adding CaO containing materials to V-bearing hot metal were investigated under the condition of simulating the process of vanadium......
point in un-dripped slag. Also, MgO could form the solid solution of FeO-MgO, in which the melting point of solid solution increased with increased amount of MgO [15]. Figure 5 Effect of MgO bearing... compressive strengths in the fluxed-pellets with different category MgO bearing additives. The slag or gangue also has effects on the compressive strength of fluxed-pellets with different category......
and the hardness of the steel after the shortened heat treatments were measured. Finally the possibility to use these processes in industrial production is discussed. 关键词:bainite; bearing steel; dilatometry... treatment of throughhardening bearing grades in the lower bainitic range allows to adjust the mechanical properties of machine components to the later application, similar to those of martensitic......
Equilibrium between Slag and Molten Iron in the Direct Alloying of Steel with Nb2O5-Bearing Slag陈伟庆,周荣章,林宗彩摘 要:<正> Equilibrium between slag and molten iron at 1600℃ was investigated for the direct alloying of steel with Nb2O6-bearing slag. The activity of niobium oxide in the slag was measured. The αNb2O5 is in the range of 10-2-10-4. TheδNb2O5......
Research on Hydration of Steel Slag Cement Activatedwith Waterglass胡曙光摘 要:This paper studied the hydration and strength influence factors of Steel Slag Cement (SSC), such as the quantity of steel slag and slag and the dosage of additive. The results show that: (a) In the process of hydration of SSC,steel slag and slag activate each other; (b) Waterglass......
Dripping and evolution behavior of primary slag bearing TiO2 through the coke packed bed in a blast-furnace hearthYan-xiang Liu1,2,Jian-liang Zhang1,2,Ke-xin Jiao2,Guo-hua Zhang1,Kuo-chih Chou1,21...="ChDivSummary" name="ChDivSummary">To investigate the flow of primary slag bearing TiO2 in the cohesive zone of blast furnaces,experiments were carried out based on the laboratory-scale packed bed......
,呈方解石晶型. 表1钒渣的化学成分 Table 1 Chemical compositions of vanadium slag (mass fraction, %) 采用行星式球磨机(Retsch PM100)对样品进行机械活化;采用高温综合热分析仪(Setsys EVO TG-DTA 1750)进行热重分析;采用电感耦合等离子发射光谱仪(Thermo Fisher ICAP 6000)测定...至最低值0.93 μm;当延长至80 min时,钒渣粒径团聚的体积平均粒径略微增加至5.27 μm. 图2 不同活化时间钒渣的粒度分析 Fig. 2 Particle size analysis for vanadium slag with different activation time 表2 不同活化时间钒渣粒度特征值 Table 2  ......
Pressure leaching of converter vanadium slag with waste titanium dioxideGuo-Quan Zhang,Ting-An Zhang,Ying Zhang,Guo-Zhi Lv,Yan Liu,Zhuo-Lin LiuKey Laboratory of Ecological Utilization of Multi-Metal... vanadium slag with waste titanium dioxide without roasting was studied. Mineralogy analysis indicates that the converter vanadium slag contains mainly three mineral phases:magnetite, titanium magnetite......
钒在FeO-SiO2-MnO渣系与铁液间的分配行为董进明1,2,赵飞3,张延玲3,仇圣桃0,干勇3(1.北京市钢铁研究总院连铸技术国家工程研究中心2.北京市北京蒂本斯工程技术有限公司3.北京科技大学 冶金与生态工程学院,北京 100083)摘 要:在实验室条件下,系统研究了1380℃下,钒在FeO-SiO2-MnO渣系与铁液间的分配行为.结果表明:钒的提取率,钒在渣-金两相的分配比,渣的钒容量随渣中SiO2的质量分数升高而降低.在SiO2的质量分数较低时,以上参数随MnO质量分数的增加而升高.而在SiO2的质量......