共搜索到43514条信息,每页显示10条信息,共4352页。用时:0小时0分0秒624毫秒
Trans. Nonferrous Met. Soc. China 22(2012) 2416-2420 Influence of electron-beam superposition welding on intermetallic layer of Cu/Ti joint CHEN Guo-qing, ZHANG Bing-gang, LIU Wei, FENG Ji-cai State... and the effect of the intermetallic layer (IMC-layer) on the mechanical properties of the joint was investigated. The IMC-layers are joint weaknesses at the Cu fusion line in centered welding......
强Cu基或Al基复合材料是未来铜材或铝材方面最具潜力的发展方向之一.在本研究中,综述了近几年在CNTs增强Cu基和Al基复合材料研究方面取得的进展,论述CNTs的预处理,CNTs-金属复合粉末的制备,CNTs-金属复合块体材料的制备,界面结合机制以及CNTs的强化机理5个主要方面. 关键词:碳纳米管;Cu基复合材料;Al基复合材料;制备方法;增强机理 中图分类号:TB333  ...的金属离子还原为金属并沉积在基体表面上,形成镀层的化学镀表面修饰方法最为常见.如通过化学镀方法对CNTs表面进行镀Cu[24-25],Ni[26-27],W[28],Mo[29]等金属,得到连续,均匀,光滑,致密的镀层,优化了CNTs与基体的界面结合. 2 CNTs-金属复合粉末的制备 由于CNTs和金属基体之间存在较大的密度差,如多壁碳纳米管的密度(1.8~2.1 g/cm3)仅为铜......
for selective sulfide precipitation of Cu Figure 17 shows the XRD pattern of the precipitate, indicating that CuS was the dominant phase. The SEM image and EDS analysis are shown in Fig. 18...Trans. Nonferrous Met. Soc. China 31(2021) 1103-1112 Separation and recovery of copper in Cu-As-bearing copper electrorefining black slime by oxidation acid leaching and sulfide precipitation Mei......
热分解法制备Cu空心微球及其光热转换性能徐斌,陈程华,张彩霞,鲁聪达,倪忠进摘 要:以甲酸铜-辛胺配合物为前驱体,油胺为表面活性剂,在熔化液态石蜡中通过热分解法单步制备Cu空心微球.利用扫描电子显微镜(SEM),透射电子显微镜(TEM),X射线衍射仪(XRD),导热系数仪,紫外-可见-近红外分光光度计(UV-Vis-NIR)及光热转换测试装置表征Cu球,研究其光热转换性能,分析Cu空心微球的合成机理.结果表明:反应温度为110℃,反应时间为3h,油胺物质的量为0.005mol的条件下,能够获得Cu空心微球,其平均粒径为380nm,壁厚约为70nm.Cu空心微球的形成机理:油胺吸附的Cu纳米晶在界面能最小化的驱动下,沿着前驱体热分解反应,生成的气泡和液态石蜡所形成的气-液界面聚合生长而成.Cu空心微球悬......
文章编号:1004-0609(2010)08-1487-08 Cu含量对铸造Mg-3Zn-xCu-0.6Zr镁合金 时效析出行为的影响 李爱文1,刘江文1,伍翠兰2,罗承萍1,焦东玲1, 朱红梅1 (1. 华南理工大学 材料科学与工程学院,广州510640; 2. 湖南大学 材料科学与工程学院,长沙410082) 摘 要:研究铜含量对铸造Mg-3Zn-xCu-0.6Zr镁... and X-ray diffractometry (XRD). The results show that the primary strengthening precipitate formed in the Cu-containing Mg-3Zn-0.6Zr alloys aged at 180 ℃ is the lath-shaped -MgZn2 with its axis......
Cu及其合金的大气腐蚀研究现状齐东梅1,成若义2,杜小青1,陈宇1,张昭1,张鉴清1,31. 浙江大学化学系2. 海军工程大学3. 中国科学院金属研究所金属腐蚀与防护国家重点实验室摘 要:综述了Cu及其合金的大气腐蚀机理,重点介绍了影响Cu及其合金大气腐蚀的主要因素和几种常见的大气腐蚀研究方法,并对其今后的研究趋势进行了展望.关键词:Cu;铜合金;大气腐蚀;......
Trans. Nonferrous Met. Soc. China 25(2015) 2009-2017 Growth behavior of CVD diamond in microchannels of Cu template Xue-zhang LIU1, Xiong-wei ZHANG2, Zhi-ming YU2 1. School of Materials... deposited in cylindrical microchannels of Cu template by hot-filament chemical vapor deposition. Micro-Raman spectroscopy and scanning electron microscopy (SEM) were used to characterize diamond film......
J. Cent. South Univ. (2019) 26: 3488-3501 DOI: https://doi.org/10.1007/s11771-019-4268-3 Muscovite 40Ar-39Ar age and its geological significance in Zhuxi W(Cu) deposit, northeastern Jiangxi OUYANG... Nature 2019 Abstract: The Zhuxi W(Cu) skarn deposit, the world’s largest tungsten deposit is newly discovered in Jingdezhen city, northeastern Jiangxi province, China. It mainly occurs near the contact......
Cu掺杂LiNi0.6Co0.2Mn0.2O2的电化学性能邱世涛1,2,钟盛文1,2,李婷婷1,2,杨金猛1,2,田丰1,21. 江西理工大学材料科学与工程学院2. 江西理工大学江西省动力电池及其材料重点实验室摘 要:采用共沉淀法制备前驱体,高温固相合成正极材料Li(Ni0.6Co0.2Mn0.2)1-xCuxO2(x=0,0.01,0.015和0.02),通过X射线衍射,SEM和电池测试系统及电化学工作站测试,对其结构,形貌和电化学性能进行表征.结果表明,掺杂少量的Cu,样品均具有α-NaFeO2型结构,没有出现杂相;样品(108)/(110)峰分裂明显,材料有着良好的层状结构;随着Cu掺杂量的增加,c和c/a增大,层间距增大,Li+脱嵌通道增大,改善导电性.Cu掺杂1%和1.5%的I(003)/I......
过程,并分析Mg和Cu的基本作用.结果表明:时效初期,Al-6Zn合金中的Zn原子有较强的团聚倾向,形成了明显的Zn原子簇;而在Al-6Zn-2Mg合金中出现明显的Zn原子簇,Zn-Mg原子簇及少量的Mg原子簇.Mg的作用是通过Mg和Zn原子间强烈的相互作用形成Zn,Mg原子交替排布的短程有序结构.含铜的Al-10Zn- 1.9Mg-1.7Cu合金中,不仅形成了Zn原子簇,Mg原子簇和Zn-Mg原...Cu原子的Al-10Zn-1.9Mg-1.7Cu合金中,Zn原子簇和Zn-Mg原子簇的平均尺寸比不含铜的合金尺寸大,而Zn原子簇和Zn-Mg原子簇的密度比不含铜的合金密度小.Al基体中剩余Zn,Mg原子浓度比Al-10Zn-1.9Mg合金的溶质原子浓度小,说明Cu原子促进了Zn原子和Zn-Mg原子的团簇过程.这与在Al-Zn-Mg合金中添加Cu能促进时效硬化的实验结果吻合[22].从图6(b)中可以......