size.TG-DSC curves and XRD peaks of different glycine/metal ratio show that smaller particle size can be obtained with a slightly fuel-deficient ratio.XRD results indicate that the as-prepared powders......
, TG-DSC and electrochemical methods. The results show that the CPE modified with 10% La2O3 (mass fraction) has the best practical applicability, which indicates that the thermal and electrochemical......
sintering method. The mass loss of raw materials and the characterization of the outcome were investigated by means of TG-DSC, XRD and optical microscopy. The reaction mechanism was discussed... by digital polarization microscope (AXIOSKOP 40, HAL 100, Czech Republic). 3 Results and discussion 3.1 TG-DSC analysis TG-DSC was used to assess the degree of reaction occurred and stability......
(TG-DSC), X-ray diffractometry (XRD), and scanning electronic microscopy (SEM). The results show that the hydrothermally synthesized precursor is an essential amorphous. The precursor can be easily......
ZrW2O8的合成及高温转变过程 程晓农1,杨娟1,张美芬1,严学华1 (1.江苏大学,材料科学与工程学院,江苏,镇江,212013) 摘要:ZrW2O8是具有负热膨胀各向同性的化合物材料.本文使用ZrOCl2*8H2O,H2WO4,浓氨水为原料采用化学沉淀法制备ZrW2O8粉末.通过高温XRD,常温XRD,TG-DSC等分析手段对产物结构进行表征,结果表明采用化学沉淀法在1150~1200℃短时间内(1h)可以生成单一ZrW2O8粉末.采用SEM技术分析了该粉末的形貌和尺寸.并对前驱体的高温转变过程进行了初步探讨. 关键词:ZrW2O8; 沉淀法; 高温转变; [全文内容正在添加中] ......
超声沉淀-热分解二步法制备棒状Co3O4纳米粒子 沈国柱1,徐政1 (1.同济大学材料科学与工程学院,上海,200092) 摘要:以CoCl2·6H2O和H2C2O4·2H2O为原料,运用超声沉淀法制备前驱体CoC2O4·2H2O,然后在300℃下煅烧前驱体制得棒状Co3O4纳米粒子.结合TG-DSC热分析,X射线衍射仪和透射电子显微镜等表征手段研究了最终产物的结构和形貌.结果显示产物为棒状立方相Co3O4,其直径大约为100nm,长度范围为0.4-2.0μm,并讨论了棒状Co3O4粒子的形成机理. 关键词:Co3O4; 纳米粒子; 超声; 制备; [全文内容正在添加中] ......
LaCrO3掺Li+的热膨胀行为研究 薛志伟1,史守华1,王峰1,成宇1,孙良成1,李德辉1 (1.包头稀土研究院,内蒙古,包头,014030) 摘要:以La2O3,Cr2O3和Li2CO3为原料,用固相法合成的LaCr(1.05-x)LixO3(x=0.05,0.1)作为样品,通过测量其热膨胀系数及TG-DSC等分析手段研究了Li及含量的大小对材料热膨胀系数的影响.结果表明,Li的添加能显著改变材料的热膨胀性能,可以达到7×10-6K-1~8×10-6K-1左右.但过多Li的添加反而不能达到改善材料热膨胀系数的目的. 关键词:铬酸镧; 热膨胀系数; 掺杂; [全文内容正在添加中] ......
广丰蒙脱土的有机改性,结构表征及应用研究 方荣生1,秦英月1,王传虎1,葛金龙1 (1.蚌埠学院化学与材料实验室,安徽,蚌埠,233030) 摘要:以十六烷基三甲基溴化铵对广丰蒙脱土进行有机改性,以红外光谱,XRD,TG-DSC等手段对其结构进行了表征,研究发现有机改性后蒙脱土晶层间距达到2.250nm.将制备的有机蒙脱土添加于环氧树脂中,在含量为5%时环氧树脂的冲击强度和断裂强度明显提高,而添加3%可使环氧树脂热变形温度提高6.1℃. 关键词:蒙脱土; 有机改性; 结构表征; [全文内容正在添加中] ......
硫酸锰固相分解制备高纯Mn3O4 高家利1,文衍宣1,粟海锋1,黎铉海1,童张法1 (1.广西大学化学化工学院,广西南宁,530004) 摘要:用TG-DSC结合XRD分析研究了硫酸锰的热分解过程.实验考察了温度,时间和冷却方式等因素对硫酸锰分解产物总锰含量的影响.实验结果表明.通过控制固相分解的工艺条件,可制备高纯Mn3O4.在较佳条件下制备的Mn3O4产物为γ-Mn4O4,总锰含量71.8%,含硫0.0O5%,硫酸锰分解接近完全. 关键词:硫酸锰; 四氧化三锰; 固相分解; [全文内容正在添加中] ......
醇钛合成Ti-PILCs焙烧性能研究 庹必阳1,张一敏1 (1.武汉科技大学,湖北,武汉,430081) 摘要:以醇钛柱撑精制钠基膨润土获得的蒙脱石纳米复合材料(Ti-PILCs)(d001=3.59 nm)为原料进行焙烧研究;运用XRD,FT-IR和TG-DSC分析等对焙烧的Ti-PILCs进行分析检测表明:焙烧后比表面积由S60℃=409.1m2/g下降到S300℃=397.8m2/g,S500℃=374.3m2/g;焙烧后的Ti-PILCs存在大量的中孔,热稳定性超过900℃,领先国内水平. 关键词:Ti-PILCs; 焙烧; 热稳定性; 比表面积; 复合材料; [全文内容正在添加中] ......