Segregation behaviors of Sc and unique primary Al3Sc in Al-Sc alloys prepared by molten salt electrolysis
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2019年第7期
论文作者：Xuan Liu Jilai Xue Zhichao Guo Cheng Zhang
文章页码：1422 - 1431
摘 要：This work mainly deals with the segregating behaviors of Sc and the growth of unique primary Al3Sc in AlSc alloys prepared by molten salt electrolysis. The alloys contain 0.23–1.38 wt%Sc where Sc segregation is observed. It is found that a high current density and long electrolysis time are in favor of high Sc content, and so do the high temperature and the addition level of Sc2O3. Sc content at the edge of Al based alloy（average Sc content: 0.75 wt%） can be as high as 1.09 wt%, while it is merely 0.24 wt% at the central area. The cooling rates have a strong impact on the morphology and particle size of primary Al3Sc,but a weak influence on Sc segregation. The cusped cubic and dendritic primary Al3Sc can precipitate in the prepared Al-Sc alloys. In a slightly hypereutectic Al-0.67 wt%Sc alloy, a large and cusped dendrite grows from the edge into the center. The primary and secondary dendritic arms can be as long as 600 and 250 μm, respectively. The Sc segregating behaviors in Al-Sc alloys is due to the mechanism controlled by the limited diffusion rate of Sc in liquid Al. This can involve the establishment of a near spherical discharge interface between liquid Al and the electrolyte. The Sc rich layer near Al-molten salt interface may provide the potential primary nuclei and sufficient Sc atoms for the growth of large dendritic primary Al3Sc.
Xuan Liu，Jilai Xue，Zhichao Guo，Cheng Zhang
School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing
摘 要：This work mainly deals with the segregating behaviors of Sc and the growth of unique primary Al3Sc in AlSc alloys prepared by molten salt electrolysis. The alloys contain 0.23–1.38 wt%Sc where Sc segregation is observed. It is found that a high current density and long electrolysis time are in favor of high Sc content, and so do the high temperature and the addition level of Sc2O3. Sc content at the edge of Al based alloy（average Sc content: 0.75 wt%） can be as high as 1.09 wt%, while it is merely 0.24 wt% at the central area. The cooling rates have a strong impact on the morphology and particle size of primary Al3Sc,but a weak influence on Sc segregation. The cusped cubic and dendritic primary Al3Sc can precipitate in the prepared Al-Sc alloys. In a slightly hypereutectic Al-0.67 wt%Sc alloy, a large and cusped dendrite grows from the edge into the center. The primary and secondary dendritic arms can be as long as 600 and 250 μm, respectively. The Sc segregating behaviors in Al-Sc alloys is due to the mechanism controlled by the limited diffusion rate of Sc in liquid Al. This can involve the establishment of a near spherical discharge interface between liquid Al and the electrolyte. The Sc rich layer near Al-molten salt interface may provide the potential primary nuclei and sufficient Sc atoms for the growth of large dendritic primary Al3Sc.
关键词：