Influence of adding various rare earths on microstructures and corrosion resistance of chromizing coatings prepared via pack cementation on P110 steel

来源期刊:Journal of Rare Earths2010年第2期

论文作者:林乃明 谢发勤 钟涛 吴向清 田伟

文章页码:301 - 304

摘    要:In order to improve the corrosion resistance and increase the service lifetime of P110 steel during operation,four chromizing coatings were formed onto its surface with/without addition of rare earths via pack cementation process.The surface morphologies and microstructures of the chromizing coatings were observed using scanning electron microscopy(SEM),and the phase constitutions were investigated by X-ray diffraction(XRD).Electrochemical corrosion behavior of the chromizing coatings in simulated oilfield brine at 30 oC was studied by means of open-circuit potential measurements and cyclic potential dynamic polarization tests.The results showed that the coatings were mainly composed of Cr23C6,Cr7C3,and(Cr,Fe)7C3.There were obvious differences in surface morphologies and microstructures of the coatings.The thickness values of the coatings were arranged as follows:CeO2-coating>Y2O3-coating>La2O3-coating>no RE-coating.The corrosion resistance of the coatings was sorted in the following sequence:CeO2-coating<no RE-coating<La2O3-coating<Y2O3-coating.Adding various rare earths could influence the microstructures and corrosion resistance of the chromizing coatings indeed.

详情信息展示

Influence of adding various rare earths on microstructures and corrosion resistance of chromizing coatings prepared via pack cementation on P110 steel

林乃明1,谢发勤1,钟涛1,吴向清1,田伟1,2

1. School of Aeronautics,Northwestern Polytechnical University

摘 要:In order to improve the corrosion resistance and increase the service lifetime of P110 steel during operation,four chromizing coatings were formed onto its surface with/without addition of rare earths via pack cementation process.The surface morphologies and microstructures of the chromizing coatings were observed using scanning electron microscopy(SEM),and the phase constitutions were investigated by X-ray diffraction(XRD).Electrochemical corrosion behavior of the chromizing coatings in simulated oilfield brine at 30 oC was studied by means of open-circuit potential measurements and cyclic potential dynamic polarization tests.The results showed that the coatings were mainly composed of Cr23C6,Cr7C3,and(Cr,Fe)7C3.There were obvious differences in surface morphologies and microstructures of the coatings.The thickness values of the coatings were arranged as follows:CeO2-coating>Y2O3-coating>La2O3-coating>no RE-coating.The corrosion resistance of the coatings was sorted in the following sequence:CeO2-coating<no RE-coating<La2O3-coating<Y2O3-coating.Adding various rare earths could influence the microstructures and corrosion resistance of the chromizing coatings indeed.

关键词:

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号