Influence of MgO-type Expansive Agent Hydration Behaviors on Expansive Properties of Concrete
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2011年第2期
论文作者：黄启忠
文章页码：345 - 347
摘 要：The hydration behaviors and expansive properties of MgO-type expansive agent curing at different temperatures and environment were investigated.When the curing temperatures changed from 25℃ to 50℃,the conductivities of MgO samples increased from 40 to 80 μs/cm,and the hydrations of MgO were quickened up obviously.Through SEM observation,the hydration product of MgO cured at 50℃ for 28 day was about 2-3μm in length.The expansion of pastes with 5% of the MgO-type expansive agent was from 0.36% to 1.01% when the curing temperature changed from 25oC to 50℃.When 8% of the MgO-type expansive agent was added,the early shrinkage of concrete was reduced.The expansion ratio increased with the curing temperature,and the expansive cracking of concrete with MgO-type expansive agent might be decreased by blending fly ash.
卢小琳
College of Materials Science and Technology,Nanjing University of Aeronautics & Astronautics
摘 要：The hydration behaviors and expansive properties of MgO-type expansive agent curing at different temperatures and environment were investigated.When the curing temperatures changed from 25℃ to 50℃,the conductivities of MgO samples increased from 40 to 80 μs/cm,and the hydrations of MgO were quickened up obviously.Through SEM observation,the hydration product of MgO cured at 50℃ for 28 day was about 2-3μm in length.The expansion of pastes with 5% of the MgO-type expansive agent was from 0.36% to 1.01% when the curing temperature changed from 25oC to 50℃.When 8% of the MgO-type expansive agent was added,the early shrinkage of concrete was reduced.The expansion ratio increased with the curing temperature,and the expansive cracking of concrete with MgO-type expansive agent might be decreased by blending fly ash.
关键词：