Fabrication and Characterization of Porous Mullite Ceramics from Pyrolysis of Alumina Powders Filled Silicone Resin
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2013年第6期
论文作者:MA Qingsong TIAN Hao
文章页码:1082 - 1084
摘 要:Porous mullite ceramics were fabricated from pyrolysis of nanometer alumina powders filled silicone resin. At 1573 K, the mixture of nanometer-Al 2 O 3 and silicone resin can be entirely transformed to mullite in air. The effects of shaping pressure on microstructure and mechanical property were investigated. Increasing shaping pressure leads to decrease in open porosity and average pore size, narrower pore size distribution, and improvement in flexural strength. With a shaping pressure of 43 MPa, nanoporous mullite ceramics with an average pore size of 50 nm can be obtained, showing 33% in open porosity and 42 MPa in flexural strength. The microstructure of porous mullite ceramics consists of dense region and loose region.
MA Qingsong,TIAN Hao
Science and Technology on Advanced Ceramic Fibers &Composites Laboratory,National University of Defense Technology
摘 要:Porous mullite ceramics were fabricated from pyrolysis of nanometer alumina powders filled silicone resin. At 1573 K, the mixture of nanometer-Al 2 O 3 and silicone resin can be entirely transformed to mullite in air. The effects of shaping pressure on microstructure and mechanical property were investigated. Increasing shaping pressure leads to decrease in open porosity and average pore size, narrower pore size distribution, and improvement in flexural strength. With a shaping pressure of 43 MPa, nanoporous mullite ceramics with an average pore size of 50 nm can be obtained, showing 33% in open porosity and 42 MPa in flexural strength. The microstructure of porous mullite ceramics consists of dense region and loose region.
关键词: