Deposition rate of hafnium crystal bar by iodide process
来源期刊：Rare Metals2014年第2期
论文作者：Li-Sen Tian Yan-Xi Yin Zhi-Fang Hu Hong-Lin Jiang Zhong-Qi Li Li-Jun Wang
文章页码：161 - 165
摘 要：Single variable and deposition weight methods were adopted in the experiment. The hafnium crystal bar was fabricated by the iodide process. Influence of hafnium filament temperature(K value), temperature controlling method, types of feed, and the loading methods on the deposition rate were studied. The results show that the K value, temperature control method, types of feed, and the loading methods have obvious effects on the deposition rate of the hafnium crystal bar. The deposition rate increases with the K value rising in the range of certain temperature;the salt bath controlling temperature method could effectively obtain the better deposition rate; the greater the contact areas of the feeds are, the faster the deposition rate is.So, the optimal iodide deposition techniques of preparing hafnium crystal bar are as follows: hafnium turnings as feed,molybdenum feed retainer charging, salt bath temperature controlling under the higher K value.
Li-Sen Tian，Yan-Xi Yin，Zhi-Fang Hu，Hong-Lin Jiang，Zhong-Qi Li，Li-Jun Wang
Division of Rare Metals Materials & Metallurgy,General Research Institute for Nonferrous Metals
摘 要：Single variable and deposition weight methods were adopted in the experiment. The hafnium crystal bar was fabricated by the iodide process. Influence of hafnium filament temperature(K value), temperature controlling method, types of feed, and the loading methods on the deposition rate were studied. The results show that the K value, temperature control method, types of feed, and the loading methods have obvious effects on the deposition rate of the hafnium crystal bar. The deposition rate increases with the K value rising in the range of certain temperature;the salt bath controlling temperature method could effectively obtain the better deposition rate; the greater the contact areas of the feeds are, the faster the deposition rate is.So, the optimal iodide deposition techniques of preparing hafnium crystal bar are as follows: hafnium turnings as feed,molybdenum feed retainer charging, salt bath temperature controlling under the higher K value.
关键词：