Resistivity and Susceptibility of Y-Ba-Cu and Bi-Sr-Ca-Cu Oxides
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG1990年第3期
论文作者：王永忠 朱乃平 严雪芹 郝慧青 乔桂文
文章页码：215 - 218
摘 要：<正> The resistivity and magnetic susceptibility ofthe quenched samples for the Y-Ba-Cu oxideswere measured at room temperature.Themeasurement for the temperature dependence of theamorphous Bi-Sr-Ca-Cu oxides with differentheat treatment temperature was made.Theresistivity and the parameters C in the formulax=X0+C/（T-0）of the quenched samples forY-Ba-Cu oxides decreased with lowering quenchtemperature,and their susceptibility did not varymonotonously with quench temperature.The tem-perature dependence of the amorphousBi-Sr-Ca-Cu oxides gradually deviates fromCurie-Weiss law with increasing heat treatmenttemperature.The local magnetic moments forY-Ba-Cu and amorphous Bi-Sr-Ca-Cu oxidesgradually decrease with decreasing quench tempera-ture or increasing heat treatment temperature.
王永忠，朱乃平，严雪芹，郝慧青，乔桂文
摘 要：<正> The resistivity and magnetic susceptibility ofthe quenched samples for the Y-Ba-Cu oxideswere measured at room temperature.Themeasurement for the temperature dependence of theamorphous Bi-Sr-Ca-Cu oxides with differentheat treatment temperature was made.Theresistivity and the parameters C in the formulax=X0+C/（T-0）of the quenched samples forY-Ba-Cu oxides decreased with lowering quenchtemperature,and their susceptibility did not varymonotonously with quench temperature.The tem-perature dependence of the amorphousBi-Sr-Ca-Cu oxides gradually deviates fromCurie-Weiss law with increasing heat treatmenttemperature.The local magnetic moments forY-Ba-Cu and amorphous Bi-Sr-Ca-Cu oxidesgradually decrease with decreasing quench tempera-ture or increasing heat treatment temperature.
关键词：