Crystal Structures and Thermoelectric Properties of Sm-Filled Skutterudite Compounds SmyFexCo4-xSb12

来源期刊:JOURNAL OF RARE EARTHS2007年第6期

论文作者:Yan Yonggao Liu Taoxiang Xie Wenjie Zhang Qingjie Tang Xinfeng

Key words:skutterudite compound; thermoelectric properties; Sm filling; rare earths;

Abstract: Polycrystalline samples of Sm partially filled skutterudites SmyFexCo4-xSb12 were prepared by melting and Spark Plasma Sintering technique.The results of Rietveld refinement showed that the obtained SmyFexCo4-xSb12 samples possessed filled skutterudite structures.The thermal parameter (B) of Sm is larger than that of Sb, Fe, and Co, indicating that Sm "rattled" in Sb-icosahedron voids.The effects of filling atom Sm on thermoelectric properties of these compounds were investigated.With the increase of Sm filling fraction (y), electrical conductivity decreased, Seebeck coefficient increased and had a maximum value when y was 0.38; thermal conductivity reduced and had a minimum value when y was 0.32.At 750 K, the highest figure of merit of 0.68 was obtained for Sm0.32Fe1.47Co2.53Sb12.

详情信息展示

Crystal Structures and Thermoelectric Properties of Sm-Filled Skutterudite Compounds SmyFexCo4-xSb12

Yan Yonggao1,Liu Taoxiang1,Xie Wenjie1,Zhang Qingjie1,Tang Xinfeng1

(1.State Key Laboratory of Advanced Technology for Materials Synthesis and Processing,Wuhan University of Technology,Wuhan 430070,China)

Abstract:Polycrystalline samples of Sm partially filled skutterudites SmyFexCo4-xSb12 were prepared by melting and Spark Plasma Sintering technique.The results of Rietveld refinement showed that the obtained SmyFexCo4-xSb12 samples possessed filled skutterudite structures.The thermal parameter (B) of Sm is larger than that of Sb, Fe, and Co, indicating that Sm "rattled" in Sb-icosahedron voids.The effects of filling atom Sm on thermoelectric properties of these compounds were investigated.With the increase of Sm filling fraction (y), electrical conductivity decreased, Seebeck coefficient increased and had a maximum value when y was 0.38; thermal conductivity reduced and had a minimum value when y was 0.32.At 750 K, the highest figure of merit of 0.68 was obtained for Sm0.32Fe1.47Co2.53Sb12.

Key words:skutterudite compound; thermoelectric properties; Sm filling; rare earths;

【全文内容正在添加中】

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号