Effect of Multiple Alloying Elements on Microstructure and Magnetic Properties of Nanocomposite Nd2Fe14B/α-Fe Magnets

来源期刊:JOURNAL OF RARE EARTHS2003年第3期

论文作者:陈秀云 朱静 马春来 姜忠良 白飞明

Key words:nanocomposite; Nd2Fe14B; melt-spun ribbons; interaction; rare earths;

Abstract: Effect of multiple alloying elements (Ga, Nb, Zr, Hf and Pr) on microstructure and magnetic properties of nanocomposite Nd9-xPrxFe86.5-y-z-m-nGayNbzZrmHfnB4.5 (x=0, 2.25; y, z, m, n=0.5, 1.0) ribbons was investigated by a L16(215) orthogonal experiment. The results show that the addition of multiple alloying elements can effectively reduce the grain size of Nd2Fe14B and α-Fe phases and promote amorphous phase to occur at low wheel speed. No inhomogeneous growth of grains was found in annealed ribbons, but a large amount of additives would results in irregularity of Nd2Fe14B and α-Fe grains. On the other hand, addition of multiple alloying elements has complex effects on magnetic properties due to interactions between alloying elements. When the content of Nb is 0.5%, increasing the content of Pr and Ga and decreasing the content of Zr and Hf can improve the magnetic properties effectively. The optimum magnetic properties were obtained in Nd2.25Pr6.75Fe84.5Ga1.5Nb0.5B4.5 ribbons spun at 15 m*s-1 with Jr=1.053 T, iHc=530.9 kA*m-1,(BH)max=124 kJ*m-3.

详情信息展示

Effect of Multiple Alloying Elements on Microstructure and Magnetic Properties of Nanocomposite Nd2Fe14B/α-Fe Magnets

陈秀云1,朱静1,马春来1,姜忠良1,白飞明1

(1.School of Materials Science & Engineering, Tsinghua University, Beijing 100084, China)

Abstract:Effect of multiple alloying elements (Ga, Nb, Zr, Hf and Pr) on microstructure and magnetic properties of nanocomposite Nd9-xPrxFe86.5-y-z-m-nGayNbzZrmHfnB4.5 (x=0, 2.25; y, z, m, n=0.5, 1.0) ribbons was investigated by a L16(215) orthogonal experiment. The results show that the addition of multiple alloying elements can effectively reduce the grain size of Nd2Fe14B and α-Fe phases and promote amorphous phase to occur at low wheel speed. No inhomogeneous growth of grains was found in annealed ribbons, but a large amount of additives would results in irregularity of Nd2Fe14B and α-Fe grains. On the other hand, addition of multiple alloying elements has complex effects on magnetic properties due to interactions between alloying elements. When the content of Nb is 0.5%, increasing the content of Pr and Ga and decreasing the content of Zr and Hf can improve the magnetic properties effectively. The optimum magnetic properties were obtained in Nd2.25Pr6.75Fe84.5Ga1.5Nb0.5B4.5 ribbons spun at 15 m*s-1 with Jr=1.053 T, iHc=530.9 kA*m-1,(BH)max=124 kJ*m-3.

Key words:nanocomposite; Nd2Fe14B; melt-spun ribbons; interaction; rare earths;

【全文内容正在添加中】

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号