Influence of Sb2O3 doping on the properties of KBT-NBT-BT lead-free piezoelectric ceramics
来源期刊：Rare Metals2011年第1期
论文作者：HUANG Xinyou,GAO Chunhua,WEI Minxian,CHEN Zhigang,and CUI Yongzhen School of Materials Science and Engineering,Jiangsu University,Zhenjiang ,China
文章页码：72 - 75
摘 要：0.144（K0.5Bi0.5）TiO3-0.85（Na0.5Bi0.5）TiO3-0.006BaTiO3（KBT-NBT-BT） lead-free piezoelectric ceramics were prepared using a conventional solid state method.The influence of Sb2O3 doping on the crystal phase,surface microstructure and properties of the KBT-NBT-BT lead-free piezoelectric ceramics were investigated using X-ray diffraction（XRD）,scanning electron microscope（SEM） and other analytical methods.The results show that all compositions are of pure perovskite structure solid states.Sb2O3 doping does not influence the microstructure of KBT-NBT-BT lead-free piezoelectric ceramics obviously in the Sb2O3 doping range of 0.1-0.5 wt.%.Sb2O3 functions as a donor when doped small amount,while functions as a acceptor when doped large amount.The piezoelectric strain constant（d33） increases first and then decreases;the dielectric constant（ε3T3/ε0） and the dielectric loss（tanδ） decrease continuously when the amount of Sb2O3 dopant increases.When the doping amount of Sb2O3 is 0.1 wt.%,the KBT-NBT-BT piezoelectric ceramics with good comprehensive properties are obtained,whose d33,ε3T3/ε0 and tanδ are 147 pC/N,1510 and 4.2%,respectively.
HUANG Xinyou,GAO Chunhua,WEI Minxian,CHEN Zhigang,and CUI Yongzhen School of Materials Science and Engineering,Jiangsu University,Zhenjiang 212013,China
摘 要：0.144（K0.5Bi0.5）TiO3-0.85（Na0.5Bi0.5）TiO3-0.006BaTiO3（KBT-NBT-BT） lead-free piezoelectric ceramics were prepared using a conventional solid state method.The influence of Sb2O3 doping on the crystal phase,surface microstructure and properties of the KBT-NBT-BT lead-free piezoelectric ceramics were investigated using X-ray diffraction（XRD）,scanning electron microscope（SEM） and other analytical methods.The results show that all compositions are of pure perovskite structure solid states.Sb2O3 doping does not influence the microstructure of KBT-NBT-BT lead-free piezoelectric ceramics obviously in the Sb2O3 doping range of 0.1-0.5 wt.%.Sb2O3 functions as a donor when doped small amount,while functions as a acceptor when doped large amount.The piezoelectric strain constant（d33） increases first and then decreases;the dielectric constant（ε3T3/ε0） and the dielectric loss（tanδ） decrease continuously when the amount of Sb2O3 dopant increases.When the doping amount of Sb2O3 is 0.1 wt.%,the KBT-NBT-BT piezoelectric ceramics with good comprehensive properties are obtained,whose d33,ε3T3/ε0 and tanδ are 147 pC/N,1510 and 4.2%,respectively.
关键词：