Mineralogical and sink-float studies of Jajarm low-grade bauxite
来源期刊：International Journal of Minerals Metallurgy and Materials2010年第3期
论文作者：Mohammad Zarbayani Esmaeil Jorjani Mirsaleh Mirmohammadi Mohammad Noaparast
文章页码：251 - 256
摘 要：Jajarm’s bauxite deposits are mainly diasporic,and they have a low mass ratio of Al2O3/SiO2. It is necessary to increase the run-of-mine mass ratio before feeding the material to the Bayer process. Chemical analysis indicated that the low-grade bauxite sample from Jajarm contained 43.9wt% Al2O3 and 13.35wt% SiO2, resulting in a mass ratio of 3.29. According to mineralogical studies, the presence of aluminosilicate minerals such as kaolinite, illite, and quartz was the main reason for the decrease of the mass ratio. Microscopic observations revealed that, with the size reduction from -1000+710 to -38 μm, the liberation degree of diaspore increased from 10% to 60%, and that of aluminosilicates increased from 20% to 85%. Heavy liquids with the densities of 2.8, 3.0, 3.2, and 3.4 g/cm3 were used to evaluate the heavy media separation in three sizes, i.e., -3350+710, -710+212, and -212+125 μm. Laboratory studies confirm that the density of 3.2 g/cm3 can produce the concentrates （in sunk fractions） with recoveries of 89.09%, 91.24%, and 84.68% with the Al2O3/SiO2 mass ratios of 5.03, 5.16, and 5.15 for the ?3350+710, ?710+212, and ?212+125 μm sizes, respectively.
Mohammad Zarbayani1，Esmaeil Jorjani1，Mirsaleh Mirmohammadi2，Mohammad Noaparast2
1. Science and Research Branch,Islamic Azad University2. School of Mining Engineering,University of Tehran
摘 要：Jajarm’s bauxite deposits are mainly diasporic,and they have a low mass ratio of Al2O3/SiO2. It is necessary to increase the run-of-mine mass ratio before feeding the material to the Bayer process. Chemical analysis indicated that the low-grade bauxite sample from Jajarm contained 43.9wt% Al2O3 and 13.35wt% SiO2, resulting in a mass ratio of 3.29. According to mineralogical studies, the presence of aluminosilicate minerals such as kaolinite, illite, and quartz was the main reason for the decrease of the mass ratio. Microscopic observations revealed that, with the size reduction from -1000+710 to -38 μm, the liberation degree of diaspore increased from 10% to 60%, and that of aluminosilicates increased from 20% to 85%. Heavy liquids with the densities of 2.8, 3.0, 3.2, and 3.4 g/cm3 were used to evaluate the heavy media separation in three sizes, i.e., -3350+710, -710+212, and -212+125 μm. Laboratory studies confirm that the density of 3.2 g/cm3 can produce the concentrates （in sunk fractions） with recoveries of 89.09%, 91.24%, and 84.68% with the Al2O3/SiO2 mass ratios of 5.03, 5.16, and 5.15 for the ?3350+710, ?710+212, and ?212+125 μm sizes, respectively.