Effect of magnesium addition on inclusions in H13 die steel
来源期刊：International Journal of Minerals Metallurgy and Materials2014年第11期
论文作者：Zheng Wu Jing Li Cheng-bin Shi Liang-liang Wang
文章页码：1062 - 1067
摘 要：The effect of magnesium addition on the number, morphology, composition, size, and density of inclusions in H13 die steel was studied. The results show that the total oxygen content in the steel can be significantly decreased to 0.0008wt%. Al2O3 and Mn S inclusions are changed into nearly spherical Mg O·Al2O3 spinel and spherical Mg O·Mg S inclusions, respectively. The number of inclusions larger than 1 μm decreases and the number of inclusions smaller than 1 μm increases with increasing magnesium content. V（N,C） precipitates around Mg O·Al2O3 and Mg O·Mg S inclusions during solidification of liquid steel. The densities of Mg O·Al2O3 spinel inclusions are lower than that of alumina inclusions. With increasing magnesium content in the Mg-containing inclusions, the density of inclusions decreases, leading to the improvement of inclusion removal efficiency.
Zheng Wu，Jing Li，Cheng-bin Shi，Liang-liang Wang
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
摘 要：The effect of magnesium addition on the number, morphology, composition, size, and density of inclusions in H13 die steel was studied. The results show that the total oxygen content in the steel can be significantly decreased to 0.0008wt%. Al2O3 and Mn S inclusions are changed into nearly spherical Mg O·Al2O3 spinel and spherical Mg O·Mg S inclusions, respectively. The number of inclusions larger than 1 μm decreases and the number of inclusions smaller than 1 μm increases with increasing magnesium content. V（N,C） precipitates around Mg O·Al2O3 and Mg O·Mg S inclusions during solidification of liquid steel. The densities of Mg O·Al2O3 spinel inclusions are lower than that of alumina inclusions. With increasing magnesium content in the Mg-containing inclusions, the density of inclusions decreases, leading to the improvement of inclusion removal efficiency.
关键词：