Effect of hydrogenation on the microstructure of Ti-5.6Al-4.8Sn-2.0Zr alloy
来源期刊:Rare Metals2009年第4期
论文作者:LI Miaoquan and LIN Yingying School of Materials Science and Engineering, Northwestern Polytechnical University, Xi’an , China
文章页码:343 - 345
摘 要:The hydride phase in the Ti-5.6Al-4.8Sn-2.0Zr alloy after hydrogenation was investigated through TEM and XRD analysis. The experimental results show that the phase transition temperature of the hydrogenated Ti-5.6Al-4.8Sn-2.0Zr alloy is decreased approximately by 150-200oC. XRD analysis verifies that the hydrogenation treatment accelerates the phase transition process from α phase to β phase of the Ti-5.6Al-4.8Sn-2.0Zr alloy, so as to decrease the phase transition temperature of the alloy. Meanwhile, TiH2 hydride (δ phase) with strip structure appears in α phase and β phase.
LI Miaoquan and LIN Yingying School of Materials Science and Engineering, Northwestern Polytechnical University, Xi’an 710072, China
摘 要:The hydride phase in the Ti-5.6Al-4.8Sn-2.0Zr alloy after hydrogenation was investigated through TEM and XRD analysis. The experimental results show that the phase transition temperature of the hydrogenated Ti-5.6Al-4.8Sn-2.0Zr alloy is decreased approximately by 150-200oC. XRD analysis verifies that the hydrogenation treatment accelerates the phase transition process from α phase to β phase of the Ti-5.6Al-4.8Sn-2.0Zr alloy, so as to decrease the phase transition temperature of the alloy. Meanwhile, TiH2 hydride (δ phase) with strip structure appears in α phase and β phase.
关键词: