Preparation and Characterization of La Doped Ferrite Using Marine Manganese Nodules as Raw Materials
来源期刊:Journal of Rare Earths2007年第S1期
论文作者:张平萍 韩沉花 程继鹏 陈雪刚
文章页码:477 - 480
摘 要:A kind of La doped ferrite was prepared with marine manganese nodules derived from East Pacific sea-bottom as raw material, NaOH as fluxing reagent, La(NO3)3 as doping agent, by calcination at 1000 ℃ for 5 h. XRD analysis showed that the ferrite products were of a spinel structure, and that its molecular formula could be expressed as MnFe2-xRxO4. SEM images proved that these ferrites showed octahedral and cubic aspects. It was found that there is some relationship between the La doping amount and the magnetic property of the ferrite. When the La doping amount was 0.03, the susceptibility of the ferrite was maximal. The as-prepared La doped ferrite is a kind of soft magnetic material that is easy to be magnetized with rather weak coercive force.
张平萍1,韩沉花1,程继鹏2,陈雪刚1
1. Department of Earth Science, Zhejiang University2. Department of Materials Science and Engineering, Zhejiang University
摘 要:A kind of La doped ferrite was prepared with marine manganese nodules derived from East Pacific sea-bottom as raw material, NaOH as fluxing reagent, La(NO3)3 as doping agent, by calcination at 1000 ℃ for 5 h. XRD analysis showed that the ferrite products were of a spinel structure, and that its molecular formula could be expressed as MnFe2-xRxO4. SEM images proved that these ferrites showed octahedral and cubic aspects. It was found that there is some relationship between the La doping amount and the magnetic property of the ferrite. When the La doping amount was 0.03, the susceptibility of the ferrite was maximal. The as-prepared La doped ferrite is a kind of soft magnetic material that is easy to be magnetized with rather weak coercive force.
关键词: