Interfacial Microstructure and Properties of a Vacuum Hot Roll-bonded Titanium-Stainless Steel Clad Plate with a Niobium Interlayer
来源期刊：Acta Metallurgica Sinica2013年第6期
论文作者：Zongan LUO Guanglei WANG Guangming XIE Lipeng WANG Kun ZHAO
文章页码：754 - 760
摘 要：Vacuum hot roll bonding（VHRB）was used to bond pure titanium（Ti）plate to a 304 stainless steel（SS）plate with a niobium（Nb）interlayer,with the aim of producing a high-quality Ti-SS clad plate.The roll-bonding process was performed at diferent temperatures in the range of 850–1000 C,followed by characterization of microstructure and mechanical properties.The study demonstrates that the interfaces are free from cracks and discontinuities,and interdifusion between the stainless steel and the titanium is efectively prevented by inserting a layer of pure Nb foil.No intermetallic reaction layer occurred at the Nb-Ti interface at any of the investigated temperatures.An intermetallic FeNb phase was formed at the Nb-SS interface when bonding was performed at 950 C and above.The presence of the FeNb layer was confirmed by x-ray difraction.The maximum shear strength of396 MPa was obtained when bonding is carried out at 900 C.However,the formation of the FeNb layer at roll bonding temperature greater than 900 C led to decrease in shear strength.Ductile fracture occurred through the Ti-Nb interface for roll-bonded temperatures of up to 900 C.On the other hand,at temperature of 950 C and above,failure occurred through the Nb-SS interface,with brittle fracture characteristics.
Zongan LUO1，Guanglei WANG1，Guangming XIE1，Lipeng WANG2，Kun ZHAO1
1. State Key Laboratory of Rolling and Automation,Northeastern University2. Shougang Jingtang Iron & Steel Co.,Ltd.
摘 要：Vacuum hot roll bonding（VHRB）was used to bond pure titanium（Ti）plate to a 304 stainless steel（SS）plate with a niobium（Nb）interlayer,with the aim of producing a high-quality Ti-SS clad plate.The roll-bonding process was performed at diferent temperatures in the range of 850–1000 C,followed by characterization of microstructure and mechanical properties.The study demonstrates that the interfaces are free from cracks and discontinuities,and interdifusion between the stainless steel and the titanium is efectively prevented by inserting a layer of pure Nb foil.No intermetallic reaction layer occurred at the Nb-Ti interface at any of the investigated temperatures.An intermetallic FeNb phase was formed at the Nb-SS interface when bonding was performed at 950 C and above.The presence of the FeNb layer was confirmed by x-ray difraction.The maximum shear strength of396 MPa was obtained when bonding is carried out at 900 C.However,the formation of the FeNb layer at roll bonding temperature greater than 900 C led to decrease in shear strength.Ductile fracture occurred through the Ti-Nb interface for roll-bonded temperatures of up to 900 C.On the other hand,at temperature of 950 C and above,failure occurred through the Nb-SS interface,with brittle fracture characteristics.
关键词：