Microstructure and properties of as-cast Cu-Cr-Zr alloys with lanthanum addition
来源期刊：Journal of Rare Earths2018年第4期
论文作者：Jilin Li Lili Chang Shengli Li Xinde Zhu Zhongxin An
文章页码：424 - 429
摘 要：Cu-0.45 Cr-0.2 Zr-xLa（x = 0-0.48） alloys were prepared by vacuum casting. The effects of La addition and orientation on the microstructure and properties of the as-cast alloy were investigated by an optical microscope, a scanning electron microscope with an energy dispersive X-ray spectrometer, a tensile testing machine and an electrical conductivity tester. The result shows that the addition of La significantly refines the columnar grainsize and decreases the secondary dendrite arm spacing. Trace addition of La improves the room temperature ultimate tensile strength,elongation and electrical conductivity mainly by purifying during melting and casting. The ultimate tensile strength, elongation and electrical conductivity significantly decrease with the increase of La content due to formation of coarse particles and oxides, which severely harm the performance of the Cu-0.45 Cr-0.2 Zr-xLa alloys. The Cu-0.45 Cr-0.2 Zr-0.13 La alloy possesses a good combination of room temperature ultimate tensile strength, elongation and electrical conductivity. In addition, room temperature ultimate tensile strength and electrical conductivity along transverse direction of the ingot are higher than that along longitudinal direction,which is mainly ascribed to different distribution of grain boundary and grain orientation.
Jilin Li1,2，Lili Chang1，Shengli Li1，Xinde Zhu1，Zhongxin An1
1. Department of Material Science and Engineering,Shandong University2. Zhengzhou Yutong Bus Co.Ltd.
摘 要：Cu-0.45 Cr-0.2 Zr-xLa（x = 0-0.48） alloys were prepared by vacuum casting. The effects of La addition and orientation on the microstructure and properties of the as-cast alloy were investigated by an optical microscope, a scanning electron microscope with an energy dispersive X-ray spectrometer, a tensile testing machine and an electrical conductivity tester. The result shows that the addition of La significantly refines the columnar grainsize and decreases the secondary dendrite arm spacing. Trace addition of La improves the room temperature ultimate tensile strength,elongation and electrical conductivity mainly by purifying during melting and casting. The ultimate tensile strength, elongation and electrical conductivity significantly decrease with the increase of La content due to formation of coarse particles and oxides, which severely harm the performance of the Cu-0.45 Cr-0.2 Zr-xLa alloys. The Cu-0.45 Cr-0.2 Zr-0.13 La alloy possesses a good combination of room temperature ultimate tensile strength, elongation and electrical conductivity. In addition, room temperature ultimate tensile strength and electrical conductivity along transverse direction of the ingot are higher than that along longitudinal direction,which is mainly ascribed to different distribution of grain boundary and grain orientation.
关键词：