Electrodeposition of magnesium-yttrium alloys by molten salt electrolysis
来源期刊：JOURNAL OF RARE EARTHS2010年第S1期
论文作者：杨少华 杨凤丽 廖春发 李明周 王旭
文章页码：385 - 388
摘 要：Electrodeposition of magnesium-yttrium alloys from molten salts was studied by electrochemical techniques.LiF-YF3 was electrolyte system with magnesium oxide and Yttrium oxide as raw materials.It was proved that Mg2+ and Y3+was deposited more prior than other ions during cyclic voltammetry and potential step measurement at 1050 °C.Voltammograms showed Mg2+ could be deposited at-0.5 V,and Y3+ could be deposited at-0.7 V on tungsten electrode compared with platinum electrode.The sedimentation of Mg2+ was more positive about 230 mV than that of other ions in electrolyte.The electrolytic codeposition of yttrium and magnesium was 0.58 V on condition that the weight ratio of Y2O3/MgO was 4:1.Chronopotentiogram indicated that the process of electrodeposition of magnesium-yttrium alloys on tungsten electrode was controlled by diffusion of ions from electrolyte to electrode interface.It was feasible to prepare Magnesium-Yttrium alloys by controlling content of ions in molten salt electrolyte.
杨少华，杨凤丽，廖春发，李明周，王旭
School of Materials and Chemistry,Jiangxi University of Science and Technology
摘 要：Electrodeposition of magnesium-yttrium alloys from molten salts was studied by electrochemical techniques.LiF-YF3 was electrolyte system with magnesium oxide and Yttrium oxide as raw materials.It was proved that Mg2+ and Y3+was deposited more prior than other ions during cyclic voltammetry and potential step measurement at 1050 °C.Voltammograms showed Mg2+ could be deposited at-0.5 V,and Y3+ could be deposited at-0.7 V on tungsten electrode compared with platinum electrode.The sedimentation of Mg2+ was more positive about 230 mV than that of other ions in electrolyte.The electrolytic codeposition of yttrium and magnesium was 0.58 V on condition that the weight ratio of Y2O3/MgO was 4:1.Chronopotentiogram indicated that the process of electrodeposition of magnesium-yttrium alloys on tungsten electrode was controlled by diffusion of ions from electrolyte to electrode interface.It was feasible to prepare Magnesium-Yttrium alloys by controlling content of ions in molten salt electrolyte.
关键词：