Surface Modification of Hydroxyapatite by Using γ-aminopropyl Silane
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2001年第3期
论文作者：张胜民
文章页码：37 - 38
摘 要：Surface modification of hydroxyapatite（ HA） powder was performed with r-aminopropyi silane in toluent solvent. The modification effects were characterized by using XPS and FT-IR methods . The results indicated that the P2p electron binding energy of the modified HA decreases 0.4 eV compared to that of HA . Furthermore , a new peak, 998cm-1 absorption appeared in IR differential spectra of modified HA and HA, which is dueto a stretching vibration of structure P-O-Si, meaning that a direct covalent bonding between hydroxyl group on HA surface and the organic silane molecule was realized after modification, and the chemical bonding type was P-O-Si. The formation of the above structure suggested that the more effective interfacial adhesion between the modified HA and polymer matrix could be carried out.
张胜民
摘 要：Surface modification of hydroxyapatite（ HA） powder was performed with r-aminopropyi silane in toluent solvent. The modification effects were characterized by using XPS and FT-IR methods . The results indicated that the P2p electron binding energy of the modified HA decreases 0.4 eV compared to that of HA . Furthermore , a new peak, 998cm-1 absorption appeared in IR differential spectra of modified HA and HA, which is dueto a stretching vibration of structure P-O-Si, meaning that a direct covalent bonding between hydroxyl group on HA surface and the organic silane molecule was realized after modification, and the chemical bonding type was P-O-Si. The formation of the above structure suggested that the more effective interfacial adhesion between the modified HA and polymer matrix could be carried out.
关键词：