Strength Improvement in ZK60 Magnesium Alloy Induced by Pre-deformation and Heat Treatment
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2016年第2期
论文作者：陈先华 LIU Lizi PAN Fusheng
文章页码：393 - 398
摘 要：The influence of pre-deformation and heat treatment on mechanicalproperties of as-extruded ZK60 alloy was investigated.The experimentalresults indicated that the solid solution,pre-cold rolling and artificialaging treatments remarkably improved the mechanicalstrength of alloys compared with the asextruded condition.Especially,pre-cold rolling in 5% reduction combined with artificialaging at 150 ℃ for 20 h was determined as the optimum heat treatment condition,which resulted in a yield strength of 333 MPa with an increment of 87 MPa and ultimate tensile strength of 373 MPa.High density of nanoscale precipitates in α-Mg matrix observed in this sample was beneficialto enhancing the strength.The as-extruded sample showed a typicalbrittle fracture while the solution treated sample exhibited ductile-fragile failure characterized by cleavage fractures,river patterns,and tear ridges.And the sample after pre-cold rolling combined with aging presented more equiaxialdimples with a great amount of cracked particles in them.The above-mentioned observations were analyzed in terms of microstructure and possible strengthening mechanism in the extruded ZK60 alloy.
陈先华1,2，LIU Lizi1，PAN Fusheng1,2,3
1. College of Materials Science and Engineering,Chongqing University2. National Engineering Research Center for Magnesium Alloys,Chongqing University3. Chongqing Academy of Science and Technology
摘 要：The influence of pre-deformation and heat treatment on mechanicalproperties of as-extruded ZK60 alloy was investigated.The experimentalresults indicated that the solid solution,pre-cold rolling and artificialaging treatments remarkably improved the mechanicalstrength of alloys compared with the asextruded condition.Especially,pre-cold rolling in 5% reduction combined with artificialaging at 150 ℃ for 20 h was determined as the optimum heat treatment condition,which resulted in a yield strength of 333 MPa with an increment of 87 MPa and ultimate tensile strength of 373 MPa.High density of nanoscale precipitates in α-Mg matrix observed in this sample was beneficialto enhancing the strength.The as-extruded sample showed a typicalbrittle fracture while the solution treated sample exhibited ductile-fragile failure characterized by cleavage fractures,river patterns,and tear ridges.And the sample after pre-cold rolling combined with aging presented more equiaxialdimples with a great amount of cracked particles in them.The above-mentioned observations were analyzed in terms of microstructure and possible strengthening mechanism in the extruded ZK60 alloy.