Effect of Alloying Additions on the Oxidation of High Speed Steels under Dry and Wet Conditions

来源期刊:中国腐蚀与防护学报2009年第4期

论文作者:M.J.MONTEIRO F.C. RIZZO S.R.J.SAUNDERS

关键词:steam oxidation; adhesion; kinetics; high speed steels;

摘    要:An investigation has been carried out into the effects of chromium and vanadium content on the oxidation rate and on the adhesion of oxide scales grown on three different chemical compositions of high speed steels under dry and wet conditions. The oxidation tests were carried out in a thermobalance at 650 ℃ for up to 14.4 ks. The mass gain of the specimens increased with increasing contents of water vapour. Alloy composition had no effect on the oxidation rate in dry conditions. The "adhesion" of the oxide scale was determined using indentation with a Rockwell C diamond and the pull adhesion test to determine the interfacial toughness and the tensile strength of the oxide metal bond, respectively. Generally, the results of the investigation indicated that oxide adhesion was lowest for the specimens exposed to dry conditions, and that with increasing water vapour content, the scale was more adherent. Indentation test results showed that an increase in the Ⅴ concentration was deleterious to oxidc adhesion in both the dry and wet environments, whereas an increase in the Cr-content had little effect on adhesion.

详情信息展示

Effect of Alloying Additions on the Oxidation of High Speed Steels under Dry and Wet Conditions

()

摘要:An investigation has been carried out into the effects of chromium and vanadium content on the oxidation rate and on the adhesion of oxide scales grown on three different chemical compositions of high speed steels under dry and wet conditions. The oxidation tests were carried out in a thermobalance at 650 ℃ for up to 14.4 ks. The mass gain of the specimens increased with increasing contents of water vapour. Alloy composition had no effect on the oxidation rate in dry conditions. The "adhesion" of the oxide scale was determined using indentation with a Rockwell C diamond and the pull adhesion test to determine the interfacial toughness and the tensile strength of the oxide metal bond, respectively. Generally, the results of the investigation indicated that oxide adhesion was lowest for the specimens exposed to dry conditions, and that with increasing water vapour content, the scale was more adherent. Indentation test results showed that an increase in the Ⅴ concentration was deleterious to oxidc adhesion in both the dry and wet environments, whereas an increase in the Cr-content had little effect on adhesion.

关键词:steam oxidation; adhesion; kinetics; high speed steels;

【全文内容正在添加中】

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号