Effects of Fe2O3 Nanoparticles on Water Permeability and Strength Assessments of High Strength Self-Compacting Concrete

来源期刊:JOURNAL OF MATERIALS SCIENCE TECHNOLOG2012年第1期

论文作者:Ali Khoshakhlagh Ali Nazari Gholamreza Khalaj

文章页码:73 - 82

摘    要:In this work,compressive,flexural and split tensile strength together with coefficient of water absorption of high performance self-compacting concrete containing different amount of Fe2O3 nanoparticles have been investigated.The strength and the water permeability of the specimens have been improved by adding Fe2O3 nanoparticles in the cement paste up to 4.0 wt%.Fe2O3 nanoparticle as a foreign nucleation site could accelerate C-S-H gel formation as a result of increased crystalline Ca(OH)2 amount especially at the early age of hydration and hence increase the strength of the specimens.In addition,Fe2O3 nanoparticles are able to act as nanofillers and recover the pore structure of the specimens by decreasing harmful pores to improve the water permeability.Several empirical relations have been presented to predict the flexural and the split tensile strength of the specimens by means of the corresponding compressive strength at a certain age of curing.Accelerated peak appearance in conduction calorimetry tests,more weight loss in thermogravimetric analysis and more rapid appearance of peaks related to hydrated products in X-ray diffraction results indicate that Fe2O3 nanoparticles up to 4 wt% could improve the mechanical and the physical properties of the specimens.

详情信息展示

Effects of Fe2O3 Nanoparticles on Water Permeability and Strength Assessments of High Strength Self-Compacting Concrete

Ali Khoshakhlagh1,Ali Nazari2,Gholamreza Khalaj1

1. Department of Materials Engineering,Science and Research Branch,Islamic Azad University2. Department of Materials Engineering,Saveh Branch,Islamic Azad University

摘 要:In this work,compressive,flexural and split tensile strength together with coefficient of water absorption of high performance self-compacting concrete containing different amount of Fe2O3 nanoparticles have been investigated.The strength and the water permeability of the specimens have been improved by adding Fe2O3 nanoparticles in the cement paste up to 4.0 wt%.Fe2O3 nanoparticle as a foreign nucleation site could accelerate C-S-H gel formation as a result of increased crystalline Ca(OH)2 amount especially at the early age of hydration and hence increase the strength of the specimens.In addition,Fe2O3 nanoparticles are able to act as nanofillers and recover the pore structure of the specimens by decreasing harmful pores to improve the water permeability.Several empirical relations have been presented to predict the flexural and the split tensile strength of the specimens by means of the corresponding compressive strength at a certain age of curing.Accelerated peak appearance in conduction calorimetry tests,more weight loss in thermogravimetric analysis and more rapid appearance of peaks related to hydrated products in X-ray diffraction results indicate that Fe2O3 nanoparticles up to 4 wt% could improve the mechanical and the physical properties of the specimens.

关键词:

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号