MoSi2-SiC-Si-B Anti-oxidation Coating on Carbon/Carbon Composites by Fused Slurry
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2009年第S1期
论文作者：来忠红
文章页码：29 - 31
摘 要：A simple and low cost method was used to fabricate a MoSi2-SiC-Si-B anti-oxidation coating on Carbon/Carbon composites.The microstructures and crystalline structures of the as-obtained coating were characterized by optical microscopy,X-ray diffractometry and scanning electron microscopy with energy dispersive spectroscopy.The results indicate that the coating with 200-250 μm in thickness has two-layer structures,which composed of SiC bonding-layer and MoSi2-Si main-layer containing boron and SiC particles.The MoSi2-SiC-Si-B coating has excellent oxidation resistance at temperature range of 1200-1400 ℃ and the maximum cumulative weight loss per unit area is only 0.01 g/cm2 for 20-hours of isothermal cyclic oxidation.
来忠红
School of Materials Science & Engineering,Harbin Institute of Technology
摘 要：A simple and low cost method was used to fabricate a MoSi2-SiC-Si-B anti-oxidation coating on Carbon/Carbon composites.The microstructures and crystalline structures of the as-obtained coating were characterized by optical microscopy,X-ray diffractometry and scanning electron microscopy with energy dispersive spectroscopy.The results indicate that the coating with 200-250 μm in thickness has two-layer structures,which composed of SiC bonding-layer and MoSi2-Si main-layer containing boron and SiC particles.The MoSi2-SiC-Si-B coating has excellent oxidation resistance at temperature range of 1200-1400 ℃ and the maximum cumulative weight loss per unit area is only 0.01 g/cm2 for 20-hours of isothermal cyclic oxidation.
关键词：