Electrochemical Intercalation of Sodium into Silicon Thin Film
来源期刊:材料科学与工程学报2008年第1期
论文作者:Gyu-Bong Cho Dong-Yeon Kim Jou-Hyeon Ahn Ho-Suk Ryu Ki-Won Kim Won-Cheol Shin Hyo-Jun Ahn Jong-Seon Kim
关键词:Sodium intercalation; Na battery; Si thin film electrode; DC magnetron sputtering;
摘 要:In order to investigate the possibility of Si thin film as an anode for Na battery, we studied the electrochemical intercalation of sodium into the Si film. Amorphous Si thin film electrode was prepared using DC magnetron sputtering. Sodium ion could intercalate into Si thin film upto Na0.52Si, i.e. 530mAh · g-1-Si. The first discharge capacity was 80mAh.·g-1-Si, which meant reversible amount of sodium intercalation. The discharge capacity slightly decreased to70mAh · g-1-Si after 10 cycles.
Gyu-Bong Cho1,Dong-Yeon Kim1,Jou-Hyeon Ahn2,Ho-Suk Ryu1,Ki-Won Kim1,Won-Cheol Shin3,Hyo-Jun Ahn1,Jong-Seon Kim1
(1.I-cube center nano advanced materials Engineering, Gyeongsang National University Jinju, 660-701, Korea;
2.Department of Chemical & Biological Engineering, Gyeongsang National University, Jinja, 660-701, Korea;
3.INOSTEK lnc, Gyeonggi Technopark, 1271-11 Sal-dong, Sangnok-gu, Ansan-si, Gyeonggi-do 426-901, Korea)
摘要:In order to investigate the possibility of Si thin film as an anode for Na battery, we studied the electrochemical intercalation of sodium into the Si film. Amorphous Si thin film electrode was prepared using DC magnetron sputtering. Sodium ion could intercalate into Si thin film upto Na0.52Si, i.e. 530mAh · g-1-Si. The first discharge capacity was 80mAh.·g-1-Si, which meant reversible amount of sodium intercalation. The discharge capacity slightly decreased to70mAh · g-1-Si after 10 cycles.
关键词:Sodium intercalation; Na battery; Si thin film electrode; DC magnetron sputtering;